(1. Iron and Steel Research Institute, Ansteel Group Corporation, Anshan 114009, Liaoning, China 2. Ansteel Group Corporation, Anshan 114021, Liaoning, China 3. Ironmaking Plant, Angang Co., Ltd., Anshan 114021,Liaoning, China 4. Liaoyang Wanli Mining Co., Ltd., Liaoyang 114000, Liaoning, China)
Abstract:Wanli was characterized by high contents of sulfur, magnesium and a low content of silicon. The concentrate had a particle size distribution suitable for the pelletizing process. Apart from magnetite, the concentrate contained pyrrhotite and MgCO3 which accounted for its high S and Mg contents. Most Fe(1-x)S and MgCO3 particles were found to be liberated and presented between the coarse magnetite particles. The effect of adding Wanli concentrate on the balling and roasting performance of Jinhe concentrate was examined. Increasing preheating and roasting temperature was found to have considerably improved the roasting performance of pellets from blends containing high proportions of Wanli concentrate. The pellets containing 70% Wanli concentrate achieved a compression strength of 2 200 N and[w(FeO)]smaller than 1%, which are generally required for pellet production. Metallurgical tests were also carried out on the pellets from the plant basket trials, and the reduction swelling index (RSI) was lower than 12%. In addition, the low-temperature reduction disintegration index (RDI) and reducibility index (RI) were improved.
收稿日期: 2017-07-07
出版日期: 2018-05-11
引用本文:
周明顺,王义栋,赵东明,王俊山,李建军,金增武. 高硫铁精矿配比对球团工艺参数及性能的影响[J]. , 2018, 53(5): 11-17.
ZHOU Ming-shun,WANG Yi-dong,ZHAO Dong-ming,WANG Jun-shan,LI Jian-jun,JIN Zeng-wu. Effects of adding high-sulfur magnetite concentrate on pelletizing parameters and performance. Iron and Steel, 2018, 53(5): 11-17.
Gao Q J, Shen F M, Wei G, et al.Effects of MgO containing additive on low-temperature metallurgical properties of oxidized pellet[J].Journal of Iron and Steel Research, International, 013, 20( 7) : 25-28.
[2]
Gao Q J, Shen F M, Wei G, et al.Effects of MgO containing additive on low-temperature metallurgical properties of oxidized pellet[J].Journal of Iron and Steel Research, International, 013, 20( 7) : 25-28.
[3]
Kemppainen A, Mattila O, Heikkinen E P, et al. Effect of H2 -H2O on the reduction of olivine pellets in CO-CO2 gas[J].ISIJ International, 2012, 52( 11) : 1973-1978.
[3]
Kemppainen A, Mattila O, Heikkinen E P, et al. Effect of H2 -H2O on the reduction of olivine pellets in CO-CO2 gas[J].ISIJ International, 2012, 52( 11) : 1973-1978.
[4]
Khaki J, Kashiwaya Y, Ishii K. High temperature behaviour of selffluxed pellets during heating up reduction [J],Ironmaking and Steelmaking, 1994, 21(1): 56-63.
[4]
Khaki J, Kashiwaya Y, Ishii K. High temperature behaviour of selffluxed pellets during heating up reduction [J],Ironmaking and Steelmaking, 1994, 21(1): 56-63.