Abstract:In order to achieve the industrial application of high strength steel rebars,Nb-V microalloyed 600 MPa grade steel rebars were set as studied object,effect of heating temperature on grain growth was studied by confocal laser scanning high-temperature microscope,and plant trial was conducted. The result shows that increasing heating temperature leads to increasing austenite grains.When the heating temperature changes from 1 180 ℃ to 1 270 ℃ and the soaking time is 60 min,the average austenite grain size improves from 58.7 μm to 85.1 μm. When the heating temperature is improved to 1 270 ℃,the average austenite grain size increases to 77.8 μm. In plant trial,with the heating temperature increases from 1 200 ℃ to 1 270 ℃,the proportion of pearlite and the size of the pearlite colony increases,the tensile fracture morphology changes from ductile fracture to quasi-cleavage brittle fracture. While heating at 1 200-1 250 ℃ can produce a steel rebars with a yield strength of 640-659 MPa,a tensile strength of 823-846 MPa,a yield ratio of 1.28-1.30,a elongation rate of 16.6%-19.2%,a maximum force elongation of 10.6%-13.0%.
周云, 杨晓伟, 陈焕德, 张宇. 加热温度对600 MPa级高强钢筋组织及性能的影响[J]. 钢铁, 2020, 55(1): 101-107.
ZHOU Yun, YANG Xiao-wei, CHEN Huan-de, ZHANG Yu. Effect of heating temperature on microstructure and properties of 600 MPa grade high strength steel rebars. Iron and Steel, 2020, 55(1): 101-107.
[1] 杨才福. 高强度建筑钢筋的最新技术进展[J]. 钢铁,2010,45(11):1.(YANG Cai-fu. Recent developments of high strength rebars for building[J]. Iron and Steel,2010,45(11):1.) [2] 林双平,苗明明,张岩,等. 建筑用高强抗震钢筋 [J]. 金属热处理,2012,37(7):103.(LIN Shuang-ping,MIAO Ming-ming,ZHANG Yan,et al. High-strength seismic reinforcement steel bar for building[J]. Heat Treatment of Metals,2012,37(7):103.) [3] 李成军. 600 MPa级钒氮微合金化热轧高性能钢筋的研制[J]. 天津冶金,2012(2):8.(LI Cheng-jun. Development of 600 MPa grade vanadium nitrogen microalloyed hot rolled high performance steel bar[J]. Tianjin Metallurgy,2012(2):8.) [4] 大卫·米尔本,李钰. 钒微合金化在生产高强度抗震钢筋方面的冶金优势[J]. 钢铁钒钛,2012,33(2):1.(Milbourn David,LI Yu. Metallurgical benefits of vanadium microalloying in producing high strength seismic grade rebar[J]. Iron Steel Vanadium Titanium,2012,33(2):1.) [5] 陈伟,施哲,陈红,等. 控冷温度对钒铌微合金高强钢筋组织和性能的影响[J]. 材料热处理学报,2013,34(10):55.(CHEN Wei,SHI Zhe,CHEN Hong,et al. Effects of controlled cooling temperature on microstructure and performance of V-Nb microalloyed high-strength rebars[J]. Transactions of Materials and Heat Treatment,2013,34(10):55.) [6] Masayuki K,Masataka T,Kiyotaka M. Effect of niobium on the formation of microstructure and grain boundary in Fe-Nb and Fe-C-Nb alloys[J]. ISIJ International,2006,46(12):1871. [7] Manohar P A,Dunne D P,Chandra T,et al. Grain growth predictions in microalloyed steels[J]. ISIJ International,1996,36(2):194. [8] DUAN Lin-na,WANG Ji-man,LIU Qing-you,et al. Austenite grain growth behavior of X80 pipeline steel in heating process[J]. Journal of Iron and Steel Research,International,2010,17(3):62. [9] 赵英利,时捷,曹文全,等. 加热温度对含Nb中碳钢奥氏体晶粒长大的影响[J]. 材料热处理学报,2010,31(4):67.(ZHAO Ying-li,SHI Jie,CAO Wen-quan,et al. Effect of heating temperature on austenite grain growth of a medium-carbon Nb steel[J]. Transactions of Materials and Heat Treatment,2010,31(4):67.) [10] 钟云龙,刘国权,刘胜新,等. 新型油井管钢33Mn2V的奥氏体晶粒长大规律[J]. 金属学报,2003,39(7):699.(ZHONG Yun-long,LIU Guo-quan,LIU Sheng-xin,et al. Austenite grain growth behavior of steel 33Mn2V designed for oil-well tubes[J]. Acta Metallurgica Sinica,2003,39(7):699.) [11] CHEN J H,CAO R. Micromechanism of Cleavage Fracture of Metals[M]. Beijing:China Science Publish,2018. [12] 徐永波,刘民治. 珠光体组织的形变、裂纹形核与扩展微观过程的动态研究[J]. 金属学报,1982(1):58.(XU Yong-bo,LIU Min-zhi. Dynamic study on deformation,crack nucleation and extended microscopic process of pearlite structure[J]. Acta Metallurgica Sinica,1982(1):58.) [13] 周煌,刘铖霖,曹建春,等. 高强抗震钢筋原位拉伸的微观组织变形机理[J]. 钢铁研究学报,2018,30(10):822.(ZHOU Huang,LIU Cheng-lin,CAO Jian-chun,et al. Microstructure deformation mechanism of SEM in-situ tension in high-strength anti-seismic rebars[J]. Journal of Iron and Steel Research,2018,30(10):822.) [14] Sun J,Boyd J D. Through-thickness cleavage fracture stress of a Ti-V-N plate steel[J]. Journal of Materials Engineering and Performance,2001,10(3):337. [15] 梁宇,余凌锋,梁益龙. 珠光体钢微观组织与拉伸性能关系[J]. 材料热处理学报,2013,34(7):73.(LIANG Yu,YU Ling-feng,LIANG Yi-long. Relationship between microstructure and tensile properties of a pearlitic steel[J]. Transactions of Materials and Heat Treatment,2013,34(7):73.) [16] 段桂花,张平,李金许,等. 铁素体和珠光体含量影响变形过程的原位研究[J]. 北京科技大学学报,2014,36(8):1032.(DUAN Gui-hua,ZHANG Ping,LI Jin-xu. et al. In situ studies on the effect of ferrite and pearlite contents on the deformation process[J]. Journal of University of Science and Technology Beijing,2014,36(8):1032.) [17] Yang W J,Lee B S,Oh Y J,et al. Microstructural parameters governing cleavage fracture behaviors in the ductile-brittle transition region in reactor pressure vessel steels[J]. Materials Science and Engineering A,2004,379(1/2):17. [18] Smith E. The nucleation and growth of cleavage microcracks in mild steel[C]//Proceedings of Conference on Physical Basis of Yield and Fracture. London:Institute of Physics and Physical Society,1996:36. [19] Korda A A,Mutoh Y,Miyashita Y,et al. Effects of pearlite morphology and specimen thickness on fatigue crack growth resistance in ferritic-pearlitic steels[J]. Materials Science and Engineering A,2006,428(1/2):262.