Effect of deoxidation technology on cleanliness of low carbon aluminum killed steel
MA Huan-xun1,WANG Xin-hua1,HUANG Fu-xiang1,JI Chen-xi2,PAN Hong-wei2
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Strip Technology Department, Shougang Research Institute of Technology, Beijing 100043, China
Abstract:Two different deoxidation methods for low carbon aluminum killed (LCAK) steel produced by KR-BOF-RH-CC process were compared: a part of aluminum were added when tapping, followed by deoxidation with carbon in RH process, and then fully deoxidated by aluminum (methodⅠ); full deoxidation by aluminum when tapping, followed by pure cycling and alloying in RH degasser (method Ⅱ). Apart from total oxygen content measurement and analysis of top slag modification, the morphology, composition, and size of non-metallic inclusions during RH refining process and surface layer of continuously-cast slabs and hot rolled coils were analyzed with Automatic Feature Analysis (AFA) equipped on ASPEX PSEM Explorer. The results show that method Ⅱ is superior to method Ⅰin refining slag modification. Furthermore, the inclusions larger than 20 μm are well removed during RH process and method Ⅱ is also more advantageous than method Ⅰin controlling the size of inclusions in the slab and on hot rolled plate surface, as well as number density and total oxygen content.
收稿日期: 2015-02-13
出版日期: 2016-01-06
引用本文:
马焕珣,王新华,黄福祥,季晨曦,潘宏伟. 脱氧工艺对低碳铝镇静钢洁净度的影响[J]. 钢铁, 2016, 51(1): 19-24.
MA Huan-xun,WANG Xin-hua,HUANG Fu-xiang,JI Chen-xi,PAN Hong-wei. Effect of deoxidation technology on cleanliness of low carbon aluminum killed steel. Iron and Steel, 2016, 51(1): 19-24.
H.Kajioka. .Ladle Refining-Challenges to Mass Production Systems of Various Grade and High Quality Steels[M]. Metallurgical Industry Press, Beijing, 2002.
[3]
H.Kajioka. .Ladle Refining-Challenges to Mass Production Systems of Various Grade and High Quality Steels[M]. Metallurgical Industry Press, Beijing, 2002.
[4]
ZHANG Li-feng.Indirect Methods of Detecting and Evaluating Inclusions in Steel-A Review[J].Journal of Iron and Steel Research International, 2006, 13(4):1-8
[4]
ZHANG Li-feng.Indirect Methods of Detecting and Evaluating Inclusions in Steel-A Review[J].Journal of Iron and Steel Research International, 2006, 13(4):1-8
Lifeng ZHANG and Brian G.THOMASState of the Art in Evaluation and Control of Steel Cleanliness[J].ISIJ International, 2003, 43(3):271-291
[6]
Lifeng ZHANG and Brian G.THOMASState of the Art in Evaluation and Control of Steel Cleanliness[J].ISIJ International, 2003, 43(3):271-291
[7]
Wen Yang, Xinhua Wang, Lifeng Zhang, et al.Cleanliness of Low Carbon Aluminum-Killed Steels during Secondary Refining Processes[J].Steel Research, 2013, 84(5):473-489
[7]
Wen Yang, Xinhua Wang, Lifeng Zhang, et al.Cleanliness of Low Carbon Aluminum-Killed Steels during Secondary Refining Processes[J].Steel Research, 2013, 84(5):473-489
[8]
陈家祥.炼钢常用图表数据手册[M]. 北京. 冶金工业出版社, 2010. 219.
[8]
陈家祥.炼钢常用图表数据手册[M]. 北京. 冶金工业出版社, 2010. 219.
[9]
KK.Lee, J.M.Park, J.Y.Chung, et al..The Secondary Refining Technologies for Improving the Cleanliness of Ultra-Low Carbon Steel at Kwangyang Works[C].Paris, France, 1995:503-509.
[9]
KK.Lee, J.M.Park, J.Y.Chung, et al..The Secondary Refining Technologies for Improving the Cleanliness of Ultra-Low Carbon Steel at Kwangyang Works[C].Paris, France, 1995:503-509.
[10]
X.M.Yang,CB.Shi,M.Zhang,G.M.Chai and F. Wang. A Thermodynamic Model of Sulfur Distribution Ratio between CaO–SiO2–MgO–FeO–MnO–Al2O3 Slags and Molten Steel during LF Refining Process Based on the Ion and Molecule Coexistence Theory[J].Metallurgical and Materials Transactions B, 2011, 42(6):1150-1180
[10]
X.M.Yang,CB.Shi,M.Zhang,G.M.Chai and F. Wang. A Thermodynamic Model of Sulfur Distribution Ratio between CaO–SiO2–MgO–FeO–MnO–Al2O3 Slags and Molten Steel during LF Refining Process Based on the Ion and Molecule Coexistence Theory[J].Metallurgical and Materials Transactions B, 2011, 42(6):1150-1180
[11]
Zhiyin DENG, Miaoyong ZHU.Deoxidation Mechanism of Al-Killed Steel during Industrial Refining Process[J].ISIJ international, 2014, 54(7):1498-1506
[11]
Zhiyin DENG, Miaoyong ZHU.Deoxidation Mechanism of Al-Killed Steel during Industrial Refining Process[J].ISIJ international, 2014, 54(7):1498-1506
Miki Y, Shimada Y, Thomas B G, et al.Model of Inclusion Removal During RH Degassing of Steel[J].Iron and Steelmaker, 1997, 24(8):31-38
[15]
Miki Y, Shimada Y, Thomas B G, et al.Model of Inclusion Removal During RH Degassing of Steel[J].Iron and Steelmaker, 1997, 24(8):31-38
[16]
BOMMARAJU R, JACKSON T, LUCA S J, SKOCZYLAS G, CLARK B, Design.Development and Application of Mold Powder to Reduce Slivers, Steelmaking Conference [C]. Toronto, Ontario, Canada, 1992: 21-27.
[16]
BOMMARAJU R, JACKSON T, LUCA S J, SKOCZYLAS G, CLARK B, Design.Development and Application of Mold Powder to Reduce Slivers, Steelmaking Conference [C]. Toronto, Ontario, Canada, 1992: 21-27.
[17]
HASEGAWA M, MARUHASHI S, KAMIDATE Y, et al.Improvement of Surface Quality of Slab and Tundish Nozzle Blockage of Continuous Casting of Stainless Steel Containing Titanium, Steelmaking Conference[C]. Atlanta, Ga, USA, 1983: 247-260.
[17]
HASEGAWA M, MARUHASHI S, KAMIDATE Y, et al.Improvement of Surface Quality of Slab and Tundish Nozzle Blockage of Continuous Casting of Stainless Steel Containing Titanium, Steelmaking Conference[C]. Atlanta, Ga, USA, 1983: 247-260.
[18]
Xiao-xuan Deng, Lin-ping Li, Xin—hua Wang, et al.Subsurface Macro-inclusions and Solidified Hook Character in Aluminum-killed Deep-drawing Steel Slabs[J].International Journal of Minerals, Metallurgy and Materials, 2014, 21(6):531-543
[18]
Xiao-xuan Deng, Lin-ping Li, Xin—hua Wang, et al.Subsurface Macro-inclusions and Solidified Hook Character in Aluminum-killed Deep-drawing Steel Slabs[J].International Journal of Minerals, Metallurgy and Materials, 2014, 21(6):531-543