(1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Pangang Group Research Institute Co., Ltd., Chengdu 611731, Sichuan, China)
Abstract:Problems of SRP steelmaking process which is difficult to be adopted in most old steel mills except for newly built steelworks were introduced. Meanwhile,the reason why the popular process MURC is not suitable for semi-steel steelmaking processes was introduced in detail. Based on the 200 t steelmaking converter of Pansteel Group Xichang Steel and Vanadium Co.,Ltd.,for the?recycling?of hot slag in the process of semi-steel steelmaking in converter,a new technique that “the slag of the first heat was all reserved,and the slag of the next heat was poured mostly” was put forward on the basis of the theoretical analysis of dephosphorization. The new technique has achieved significant results in the semi-steel steelmaking. The dephosphorization efficiency is significantly improved,the average flux consumption of converter decreases to 47.64 kg/t,and the average lime consumption is 13.95 kg/t. The new technology has a good effect on reducing steel material consumption and improving converter life-time.
收稿日期: 2016-12-05
出版日期: 2017-07-10
引用本文:
梁新腾,孙彦辉,曾建华,陈 均,陈 路. 攀钢半钢转炉少渣炼钢新工艺开发和应用[J]. 钢铁, 2017, 52(7): 47-51.
LIANG Xin-teng,,SUN Yan-hui,ZENG Jian-hua,CHEN Jun,CHEN Lu. Theoretical?research?and application of less slag steelmaking of semi-steel in BOF of Pansteel. Iron and Steel, 2017, 52(7): 47-51.
Y.Ogawa.Development of the Continuous Dephosphorization and Decarbonization Process Using BOF [J]. Tetsu-to-Hagane, 2001, 87(1): 21-28.
[2]
K. Yoshida, I. Yamazaki, Y. Tozaki, et al. Development of Effective Refining Process Consisting of Hot Metal Pretreatment and Decarburization in Two Top and Bottom Blown Converters [J]. Sumitomo Metals, 1993, 45(3): 2-7.
[5]
王新华等.氧气转炉“留渣+双渣”炼钢工艺技术研究 [J]. 中国冶金,2013(04).
[3]
秦登平.首秦610MPa 级水电用钢低磷钢低成本冶炼关键技术研究[D].北京科技大学,2013.
[6]
S.Basu.Studies on Dephosphorisation During Steelmaking [D]. Doctoral dissertation, Royal Institute of Technology, 2007.
[4]
Y.Ogawa.Development of the Continuous Dephosphorization and Decarbonization Process Using BOF [J]. Tetsu-to-Hagane, 2001, 87(1): 21-28.
[5]
王新华等.氧气转炉“留渣+双渣”炼钢工艺技术研究 [J]. 中国冶金,2013(04).
[6]
S.Basu.Studies on Dephosphorisation During Steelmaking [D]. Doctoral dissertation, Royal Institute of Technology, 2007.
[7]
Turkdogan E T. Activities of Constituents of Iron and Steelmaking Slags[J],ISIJ, 1953,175(3):398-401.
[7]
Turkdogan E T. Activities of Constituents of Iron and Steelmaking Slags[J],ISIJ, 1953,175(3):398-401.
[8]
R.G.Ward:An Introduction to the Physical Chemistry of Iron&Steel Making p.122,Edward Arnold 1962.
[8]
R.G.Ward:An Introduction to the Physical Chemistry of Iron&Steel Making p.122,Edward Arnold 1962.