Study on Inclusion Induced Fatigue Crack Initiation and Propagation in UltraHigh Strength Steel for Aerospace Application
FAN Hongmei1,ZENG Yanping1,WANG Xishu2,CUI Zhengqiang1,XIE Xishan1
1. High Temperature Materials Research Laboratories, University of Science and Technology Beijing, Beijing 100083, China;2. Department of Engineering Mechanics, Tsinghua University, Beijing 100084, China
Abstract:The microbehavior of inclusion inducing crack initiation and propagation in ultrahigh strength steel MA250 for aerospace application under low cyclic fatigue loading was studied by means of SEM original position observation. The characteristics of low cyclic fatigue crack initiation and propagation were obtained. The method for accurately measuring fatigue crack growth rate in MA250 is discussed.
范红妹;曾燕屏;王习术;崔正强;谢锡善. 航空用超高强度钢中夹杂物导致疲劳裂纹萌生与扩展的微观行为[J]. 钢铁, 2007, 42(7): 72-0.
FAN Hongmei;ZENG Yanping;WANG Xishu;CUI Zhengqiang;XIE Xishan. Study on Inclusion Induced Fatigue Crack Initiation and Propagation in UltraHigh Strength Steel for Aerospace Application. Iron and Steel, 2007, 42(7): 72-0.