1.School of Physical Science and Technology, Yunnan University, Kunming 650091, Yunnan, China;2.National Engineering Research Center of Advanced Steel Technology, Beijing 100081, China;3.Jiangyin Xingcheng Special Steel Co., Ltd., Jiangyin 214429, Jiangsu, China;4.The Chinese Society for Metals, Beijing 100711, China
Abstract:The highcycle fatigue fracture behavior of 60Si2CrVA spring steels produced by two different metallurgical processes were studied by using rotating bar twopoint bending fatigue machine. The experimental results indicate that the characteristics of the inclusions in these two steels were different, which was the main reason for the significant difference of their fatigue properties, although their oxygen content was almost equal. Compared with X8 steel produced by the metallurgical process of EAF+LF+VD+CC, the number and size of inclusions in X6 steel produced by the metallurgical process of LD+LF+RH+CC was decreased obviously, especially the number of Al2O3riched hard inclusions was reduced, therefore the latter had not only higher fatigue strength, but also higher fatigue life stability.
郝立群;惠卫军;项金钟;惠荣;翁宇庆;. 两种不同冶金工艺生产的60Si2CrVA弹簧钢的高周疲劳性能[J]. 钢铁, 2009, 44(2): 64-0.
HAO Liqun;HUI Weijun;XIANG Jinzhong;HUI Rong;WENG Yuqing;. HighCycle Fatigue Properties of 60Si2CrVA Spring Steels Produced by Two Different Metallurgical Processes. Iron and Steel, 2009, 44(2): 64-0.