GCr15 Bearing Steel Production at Shijiazhuang Iron and Steel Company
CAO Liguo1 ,2,LI Shiqi1,CHEN Ze1
1. Shool of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083, China;2. Shijiazhuang Iron and Steel Co., Ltd., Shijiazhuang 050031, Hebei, China
Abstract:The GCr15 bearing steel is produced by 60 t BOFLFVDCC route at Shijiazhuang Iron and Steel Company. The key points of the practice are:close oxygen content control on BOF by catching carbon practice, control of the slag carry over during BOF tapping, using CaOSiO2Al2O3 slag with high basicity(R≥3.5) for LF refining,removal ot deoxidization products by effective argon blowing,with further removal during VD process under a vacuum less than 67 Pa and for 1020 minutes and a weak stirring for more than 4 minutes at the end of VD process,protective casting to prevent reoxidation. The average oxygen content of the final products was 9.5×10-6,with the lowest of 7×10-6. The production of GCr15 bearing steel at Shijiazhuang steel is on the domestic top level with such efficient, low cost route.
曹立国;李士琦;陈泽. 石钢GCr15轴承钢实践[J]. 钢铁, 2008, 43(6): 38-0.
CAO Liguo;LI Shiqi;CHEN Ze. GCr15 Bearing Steel Production at Shijiazhuang Iron and Steel Company. Iron and Steel, 2008, 43(6): 38-0.