Study of Controlling Nitrogen Content of NBearing Stainless Steel During AOD Process
LI Xuefeng1,2,LI Zhengbang2
1. Quallity Department, Taiyuan Iron and Steel (Group)Co., Taiyuan 030003, Shanxi, China; 2. Institute of Metallurgical Technology, Center Iron and Steel Research Institute, Beijing 100081, China
Abstract：The solution of nitrogen in molten stainless steel was studied thermodynamically and kinetically. The results showed that the solubility of nitrogen is increased with decreasing temperature and increasing Cr, Mn, Mo content. The theory and practice of nitrogen alloying model by blowing nitrogen into AOD were studied, and it was indicated that nitrogen content is changed with the changing of carbon content and temperature of molten，oxygen and argon gas flowing rate. The process is suitable to produce Nbearing stainless steel which nitrogen content value below 90% and to assure the accuracy of nitrogen content control, the nitrogen content should be below 80% of solubility under normal pressure.
李学锋;李正邦. AOD炉冶炼含氮不锈钢氮成分控制的研究[J]. 钢铁, 2007, 42(7): 18-0.
LI Xuefeng;LI Zhengbang. Study of Controlling Nitrogen Content of NBearing Stainless Steel During AOD Process. Iron and Steel, 2007, 42(7): 18-0.
2007, Vol. 42 