板坯SP调宽用新型侧压模块的研究
宁宇 焦四海 孙业中 周成 谢建新
北京科技大学 宝山钢铁股份公司研究院 北京科技大学 北京科技大学
The research on the new Sizing Press anvil
Ning Yu JIAO Sihai Yezhong Sun Zhou Cheng Zhou Xie Jianxin Xie
摘要 本文针对热轧厂SP侧压调宽后出现板形不良而造成热轧成材率下降的问题,提出采用新型双斜面侧压模块以改善SP侧压后的板坯形状、降低板坯的尾部翘曲。有限元数值模拟与实验的研究结果表明:采用新型双斜面模块调宽后,板坯中部的“狗骨”峰值有较大程度的降低,其 “狗骨”的最大高度值小于目前热轧厂普遍使用的单斜面模块,而宽度方向上中心部位的厚度大于单斜面模块;同时,双斜面模块的调宽效率高于单斜面模块;相同变形条件下,经单斜面模块侧压后的板坯尾部翘曲程度大,双斜面模块能够明显减小SP侧压后的板坯尾部翘曲,采用双斜面模块可以改善板坯SP侧压后的板形。
Abstract :To improve the profile of the slab after SP and increase the production efficiency, a new SP tow-step anvil is put forward in this paper. The experimental and FEM results show that, compared with the old anvil, the peak of the “dog bone” reduces and the thick of the middle slab increases after SP when applying the new tow-step anvil. Meanwhile, the slab width adjustment efficiency of the tow-step anvil increases. Under the same deformation conditions, the slab warp after SP reduces obviously.
收稿日期: 2008-11-17
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres [J]. 钢铁研究学报(英文版), 2020, 27(7): 743-754.
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei [J]. 钢铁研究学报(英文版), 2020, 27(7): 755-769.
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity [J]. 钢铁研究学报(英文版), 2020, 27(7): 770-781.
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method [J]. 钢铁研究学报(英文版), 2020, 27(7): 782-787.
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 788-795.
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation [J]. 钢铁研究学报(英文版), 2020, 27(7): 796-806.
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps [J]. 钢铁研究学报(英文版), 2020, 27(7): 807-819.
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase [J]. 钢铁研究学报(英文版), 2020, 27(7): 820-833.
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 834-841.
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting [J]. 钢铁研究学报(英文版), 2020, 27(7): 842-848.
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition [J]. 钢铁研究学报(英文版), 2020, 27(7): 849-866.
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films [J]. 钢铁研究学报(英文版), 2020, 27(7): 867-874.
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed [J]. 钢铁研究学报(英文版), 2020, 27(6): 617-623.
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C [J]. 钢铁研究学报(英文版), 2020, 27(6): 624-630.
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment [J]. 钢铁研究学报(英文版), 2020, 27(6): 631-642.