Slag Forming Route and Dephosphorization of BOF Dephosphorizing Pretreatment and Direct SteelMaking
WANG Xuebin1，FENG Mingxia1，ZOU Zongshu1，ZHAO Guoguang2，LIU Zhengxiang2
1.School of Materials and Metallurgy， Northeastern University， Shenyang 110004， Liaoning, China； 2Shanghai Meishan Group Corporation， Nanjing 210039， Jiangsu, China
Abstract：Based on practical data，the routes of slag formation during BOF dephosphorizing pretreatment and direct steelmaking process were studied. From thermodynamics and kinetics viewpoints，the routes of slag formation in two phases of the dephosphorizing pretreatment and direct steelmaking process are discussed in detail. The route of slag formation is different for hot metals with different phosphorus content. For the dephosphorizing pretreatment and direct steelmaking process，high iron oxide route should be used in dephosphorization phase to improve the kinetic conditions，and high calcium oxide route shoule be used in decarbonization phase to improve the thermodynamic conditions.
王学斌;冯明霞;邹宗树;赵国光;刘正祥. 复吹转炉预直炼法成渣路线分析[J]. 钢铁, 2009, 44(1): 23-0.
WANG Xuebin;FENG Mingxia;ZOU Zongshu;ZHAO Guoguang;LIU Zhengxiang. Slag Forming Route and Dephosphorization of BOF Dephosphorizing Pretreatment and Direct SteelMaking. Iron and Steel, 2009, 44(1): 23-0.
2009, Vol. 44 