1. Institute of Structure Materials, Steel Research Technology Group Corporation of China, Beijing 100081, China;2. Department of Science and Technology Information, Steel Research Technology Group Corporation of China, Beijing 100081, China
Abstract：Ｔhe effect of solution temperature between 7001050 ℃ on the grain size, austenite fraction and mechanical properties of Custom 465 aged at 510 ℃ was researched. Fracture surface of notch impact specimens were analyzed with SEM. The results show that the best solution temperature range is from 900 ℃ to 950 ℃. The austenite in the steel after aging is mainly reverted austenite.
陈嘉砚;刘江;杨卓越;宋维顺;张永权. 固溶温度对Custom 465钢组织与性能的影响[J]. 钢铁, 2008, 43(1): 73-0.
CHEN Jiayan;LIU Jiang;YANG Zhuoyue;SONG Weishun;ZHANG Yongquan. Effects of Solution Temperature on Structure and Behavior of Custom 465. Iron and Steel, 2008, 43(1): 73-0.
2008, Vol. 43 