Inclusion Removal in Steel Continuous Casting Tundish
YUE Qiang,ZOU Zongshu,CHEN Zhou
School of Materials and Metallurgy, Northeastern University, Sheyang 110004, Liaoning, China
摘要 引入湍流涡旋的Kolmogoroff尺度作为区分钢液中夹杂物粒径大小的标准。对中间包内不同粒径夹杂物的上浮规律进行了理论分析,为中间包内夹杂物去除的实验研究提供了理论依据。采用不同的模拟介质对中间包内夹杂物的去除做了研究,验证了理论分析的正确性。
关键词 :
中间包 ,
非金属夹杂物 ,
湍流 ,
涡旋尺度
Abstract :Kolmogoroff eddy scale was introduced to determine inclusions size in molten steel. A theoretical basis for water modeling of inclusion removal in tundish was used to study nonmetallic inclusion removal in tundish. The water modeling was performed by using two types of plastic particles as inclusions. The results show that the theoretical analysis is acceptable.
Key words :
tundish
nonmetallic inclusion
turbulent flow
eddy scale
收稿日期: 1900-01-01
[1]
侯新梅, 刘云松, 王恩会. 钢包内衬用耐火材料对钢中非金属夹杂物的影响 [J]. 钢铁, 2020, 55(6): 15-24.
[2]
牛凯军, 杨文, 张立峰, 储焰平, 张洪起, 郭子强. 帘线钢凝固过程夹杂物生成热力学及工业实践 [J]. 钢铁, 2020, 55(6): 61-67.
[3]
朱坦华, 周秋月, 任英, 段豪剑, 张立峰. 二次氧化过程IF钢中间包中夹杂物演变行为 [J]. 钢铁, 2020, 55(3): 35-39.
[4]
王伟 朱立光. 双流T-型中间包的流场模拟及其控流结构优化 [J]. , 2020, 45(2): 0-0.
[5]
储焰平, 谌智勇, 刘南, 张立峰. 高速重轨钢中尖晶石夹杂物的形成及控制 [J]. 钢铁, 2020, 55(1): 38-46.
[6]
张硕1,唐海燕1,刘锦文1,肖红1,2,姚海英2,张家泉1. 六流H型通道感应加热中间包的结构优化 [J]. 钢铁研究学报, 2019, 31(9): 787-794.
[7]
潘晓倩,杨健,职建军,王睿之,范正洁,徐龙云. 超低碳汽车外板BH钢炼钢过程中夹杂物的演变 [J]. 钢铁, 2019, 54(8): 48-57.
[8]
秦绪锋,程常桂,李阳,张春明,金焱,武光君. 上水口环形吹氩对中间包内渣眼形成的影响 [J]. 钢铁, 2019, 54(8): 107-115.
[9]
李牧明,于会香,潘明,白皓. 精炼渣对高锰钢中非金属夹杂物的影响 [J]. 钢铁, 2019, 54(6): 37-42.
[10]
李少翔 铁占鹏 寇玉山 陈培莉 唐海燕 张家泉. 三流大方坯连铸中间包流场优化数值模拟研究 [J]. , 2019, 44(5): 0-0.
[11]
张庆松, 闵 义, 许海生, 许久健, 刘承军. 硅镇静钢镁处理后夹杂物的生成及演变行为 [J]. 钢铁, 2019, 54(4): 37-42.
[12]
陈玉辉 刘吉刚. 中间包优化对板坯连铸钢水洁净度的影响分析 [J]. , 2019, 44(3): 0-0.
[13]
王林珠, 李军旗, 杨树峰, 陈朝轶, 金会心. 高铝钢中钙处理对非金属夹杂物特征的影响 [J]. 钢铁, 2019, 54(11): 27-32.
[14]
张国成1,2,罗果萍1,邬虎林2,白晓光2. 包钢烧结合理利用巴西高硅混合粉实验 [J]. 钢铁研究学报, 2019, 31(10): 875-881.
[15]
张晓萌,李少翔,唐海燕,铁占鹏,兰鹏,张家泉. 非对称中间包稳态浇铸与换包操作的冶金效果 [J]. , 2019, 31(1): 15-23.