重轨钢超声波探伤不合原因分析
吉玉
武钢研究院工艺所
Analy of ultrasonic defect inside Heavy Rail Steel
摘要 针对重轨钢出现超声波探伤不合格的情况，通过金相制样，大样电解等手段，利用扫描电镜配合能谱仪分别对钢轨点状报警和连续报警试样进行了研究。结果表明，钢中大型夹杂物是造成重轨钢探伤不合的主要原因，点状报警主要由单个大颗粒夹杂物引起，而连续报警主要由细长条或链状夹杂物引起。对大颗粒夹杂物的来源进行了分析，在工艺采取了相应的改进措施后，重轨的探伤合格率明显提高
Abstract ：Considering that many heavy rail pass the ultrasonic defect test, the samples causeing sport alarm and continuous alarm were researched by SEM and EDX. The results showed that the defects in heavy rail steel were mainly caused by large inclusions, spot alarms were caused by single large inclusion and continuous alarms were caused by slender or line inclusion. The sources of large inclusion were analyzed and relevant improvement measures were taken, the percent qualified by ultrasonic defect detection have been greatly increased.
收稿日期: 2010-03-16
出版日期: 2011-03-15
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment
2011, Vol. 46 