新型锰系空冷超高强精轧螺纹钢筋的研制
李文韬,李正操,张寒,白秉哲
1. 清华大学材料科学与工程系 2.
Development of AirCooled Super Strength Finish Rolled Rebar
LI Wentao,LI Zhengcao,ZHANG Han,BAI Bingzhe
摘要 对新型锰系空冷超高强精轧螺纹钢筋进行了实验室研究和工业生产试制。在提高性能同时降低合金成本和简化工艺的原则下,在新型锰系空冷贝氏体钢的基础上采用钒微合金化,开发了超高强精轧螺纹钢筋(PBR)。此外,利用TEM研究了PBR钢筋中钒的析出物的形貌、尺寸及分布。开发的PBR超高强钢筋,不含昂贵合金元素,淬透性好,强度高,屈强比低,全面满足PSB 1080级别要求,20mm钢筋抗拉强度达到1600~1610MPa,屈服强度1400~1420MPa,伸长率8.5%,均匀伸长率5.0%;32mm钢筋抗拉强度达到1450~1500MPa,屈服强度1140~1200MPa,伸长率9.0%,均匀伸长率5.0%。
Abstract : Super strength finish rolled rebar based on aircooled was studied in laboratory and industrial production was carried out. Vanadium microalloyed was developed on the base of manganese series bainitic steels in order to improve performance, reduce costs and simplify technology. Besides, morphology, size and distribution of vanadium precipitates were studied by use of TEM. The aircooled bainite steel developed without expensive alloy elements shows high strength and low yield ratio, which fully meets the standard of PSB 1080.20mm rebar has mechanical properties as follows: Rm 16001610MPa; ReL 14001420MPa; A 8.5%; Agt 5.0%.32mm rebar: Rm 14501500MPa; ReL 11401200MPa; A 9.0%; Agt 5.0%.
收稿日期: 2010-06-12
出版日期: 2011-05-15
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres [J]. 钢铁研究学报(英文版), 2020, 27(7): 743-754.
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei [J]. 钢铁研究学报(英文版), 2020, 27(7): 755-769.
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity [J]. 钢铁研究学报(英文版), 2020, 27(7): 770-781.
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method [J]. 钢铁研究学报(英文版), 2020, 27(7): 782-787.
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 788-795.
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation [J]. 钢铁研究学报(英文版), 2020, 27(7): 796-806.
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps [J]. 钢铁研究学报(英文版), 2020, 27(7): 807-819.
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase [J]. 钢铁研究学报(英文版), 2020, 27(7): 820-833.
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 834-841.
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting [J]. 钢铁研究学报(英文版), 2020, 27(7): 842-848.
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition [J]. 钢铁研究学报(英文版), 2020, 27(7): 849-866.
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films [J]. 钢铁研究学报(英文版), 2020, 27(7): 867-874.
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed [J]. 钢铁研究学报(英文版), 2020, 27(6): 617-623.
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C [J]. 钢铁研究学报(英文版), 2020, 27(6): 624-630.
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment [J]. 钢铁研究学报(英文版), 2020, 27(6): 631-642.