低碳高硫易切削钢的切削性能研究
王宏斌1,2,林腾昌1,段飞虎1,张志强2,王勇2
1. 北京科技大学冶金与生态工程学院, 北京 100083 2. 宣化钢铁集团有限责任公司, 河北 张家口 075100
Cutting Performance of Free Cutting Steel With Low Carbon and High Sulfur
WANG Hong-bin1,2,LIN Teng-chang1,DUAN Fei-hu1,ZHANG Zhi-qiang2,WANG Yong2
1. Department of Metallurgy Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Xuanhua Iron and Steel Group Co., Ltd., Zhangjiakou 075100, Hebei, China
摘要 对宣钢生产的X1215低碳高硫易切削钢进行了切削试验,运用扫描电镜研究了钢中的夹杂物形态。切削试验表明,该钢的易切削性能优于45钢,切削比Kr达到1.48。分析表明,该钢中全氧的质量分数为120×10-6 时,钢中大量存在的条形硫化锰及纺锤形硫化锰-氧化物的复合夹杂是钢材切削性能优良的主要原因。
Abstract :Cutting experiment was made for X1215 free cutting steel produced by Xuangang. The inclusions were analyzed by SEM. It shows that the free cutting performance of X1215 is better than steel 45, and cutting ratio Kr reaches 1.48. When w(TO) is 120×10-6 , there is a large number of sulfide and spindle manganese sulfide-oxide complex inclusions in steel, which is the main reason of excellent cutting performance.
收稿日期: 2010-12-27
出版日期: 2011-11-17
引用本文:
王宏斌,,林腾昌,段飞虎,张志强,王勇. 低碳高硫易切削钢的切削性能研究[J]. 钢铁, 2011, 46(11): 82-85.
WANG Hong-bin1,2,LIN Teng-chang1,DUAN Fei-hu1,ZHANG Zhi-qiang2,WANG Yong2. Cutting Performance of Free Cutting Steel With Low Carbon and High Sulfur. Iron and Steel, 2011, 46(11): 82-85.
链接本文:
http://www.chinamet.cn/Jweb_gt/CN/ 或 http://www.chinamet.cn/Jweb_gt/CN/Y2011/V46/I11/82
[1]
Jun Zhao, Hai-bin Zuo, Chao Ling, Wen-tao Guo, Jing-song Wang, Qing-guo Xue. Microstructure evolution of coke under CO2 and H2 O atmospheres [J]. 钢铁研究学报(英文版), 2020, 27(7): 743-754.
[2]
Sheng-li Wu, Xiao-bo Zhai, Li-xin Su, Xu-dong Ma. Ore-blending optimization for Canadian iron concentrate during iron ore sintering based on high-temperature characteristics of fines and nuclei [J]. 钢铁研究学报(英文版), 2020, 27(7): 755-769.
[3]
Feng Zhang, De-qing Zhu, Jian Pan, Zheng-qi Guo, Meng-jie Xu. Improving roasting performance and consolidation of pellets made of ultrafine and super high grade magnetite concentrates by modifying basicity [J]. 钢铁研究学报(英文版), 2020, 27(7): 770-781.
[4]
Da‑peng Li, Hua‑zhang Wu, Hai‑feng Wang, Hong Li. Growth of solidified shell in bloom continuous casting mold of hypo-peritectic steel based on a FeS tracer method [J]. 钢铁研究学报(英文版), 2020, 27(7): 782-787.
[5]
Jie Yang, Deng‑fu Chen, Miao‑yong Zhu. Crystallization and heat transfer of CaO–SiO2 -based slag for high-Mn–high-Al steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 788-795.
[6]
Ping‑guo Jiang, Jin‑sheng Liu, Yi‑yu Xiao, Xiao‑heng Tan, Wen‑jie Liu. Recovery of iron from copper slag via modified roasting in CO–CO2 mixed gas and magnetic separation [J]. 钢铁研究学报(英文版), 2020, 27(7): 796-806.
[7]
Hai Wang, Dong Liu, Jian‑guo Wang, Hai‑ping Wang, Yang Hu, Hao‑dong Rao. Characterization of hot deformation behavior of 30Si2MnCrMoVE low-alloying ultra-high-strength steel by constitutive equations and processing maps [J]. 钢铁研究学报(英文版), 2020, 27(7): 807-819.
[8]
Chen Dong, Zheng‑dong Liu, Zheng‑zong Chen, Zhen Liu, Jia‑zhuang Zheng, Xi‑tao Wang. Hot deformation behavior of a heat-resistant alloy without γ′-phase [J]. 钢铁研究学报(英文版), 2020, 27(7): 820-833.
[9]
Jia‑jia Qiu, Min Zhang, Gu‑hui Gao, Zhun‑li Tan, Bing‑zhe Bai. Research and modeling on correlation among microstructure, yield strength and process of bainite/martensite steel [J]. 钢铁研究学报(英文版), 2020, 27(7): 834-841.
[10]
Xiao‑hui Chen, Bo Chen, Xu Cheng, Guo‑chao Li, Zheng Huang. Microstructure and properties of hybrid additive manufacturing 316L component by directed energy deposition and laser remelting [J]. 钢铁研究学报(英文版), 2020, 27(7): 842-848.
[11]
Huan Lin, Mao‑sheng Yang, Bai‑po Shu. Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition [J]. 钢铁研究学报(英文版), 2020, 27(7): 849-866.
[12]
Rui‑wu Li, Zheng Zhang, Jian‑wei Li, Ke‑xin Ma, Yuan‑yuan Guo, Yan‑wen Zhou, Fa‑yu Wu. Surface modification of 316L stainless steel by diamond-like carbon films [J]. 钢铁研究学报(英文版), 2020, 27(7): 867-874.
[13]
He‑ping Li, Sheng‑li Wu, Zhi‑bin Hong, Heng Zhou, Ming‑yin Kou. Development and application of coke oven gas spraying on sinter bed [J]. 钢铁研究学报(英文版), 2020, 27(6): 617-623.
[14]
Xin Jiang, Huai‑yu Zhang, Hai‑yan Zheng, Qiang‑jian Gao, Feng‑man Shen. Three-segment control theory of MgO/Al2 O3 ratio based on viscosity experiments and phase diagram analyses at 1500 °C [J]. 钢铁研究学报(英文版), 2020, 27(6): 624-630.
[15]
Qing‑song Zhang, Yi Min, Jiu‑jian Xu, Cheng‑jun Liu. Formation and evolution behavior of inclusions in Al-killed resulfurized free-cutting steel with magnesium treatment [J]. 钢铁研究学报(英文版), 2020, 27(6): 631-642.