Al2O3夹杂物在钢-渣界面处的运动特性及去除率

摘要
图/表
参考文献
相关文章 (6)

全文: PDF (0 KB) HTML (0 KB)
输出: BibTeX | EndNote (RIS)

摘要通过理论计算和分析，研究了夹杂物颗粒在钢-渣界面处夹杂物去除层内的运动特性及去除率。结果表明：在夹杂物去除层内，Al2O3夹杂物颗粒的布朗扩散上浮临界尺寸为1.33μm，直径小于临界尺寸的夹杂物颗粒很难上浮去除；布朗碰撞的优势区域主要是直径为2.5μm以下的夹杂物颗粒之间以及直径为2.5～5μm夹杂物颗粒与0.5μm以下的微小颗粒之间的碰撞；直径为20～150μm的夹杂物颗粒在钢-渣界面去除层中9min内很容易完全上浮去除，而直径小于10μm的夹杂物颗粒去除率很低且升高缓慢，是提高钢液洁净度的主要控制对象。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	郭洛方
	李宏*
	王耀
	李永卿

关键词 ：夹杂物去除层，布朗扩散，布朗碰撞，Stokes碰撞，夹杂物去除率

Abstract：The kinetic characteristics and removal rate of Al2O3 particles in the inclusion removing layer, which was close to the interface between steel and slag, were investigated by theoretical calculation and analysis. The results show that: the Brownian diffusion floating critical diameter (BDFCD) of Al2O3 inclusion particle is 1.33μm, and the inclusion particle whose diameter is less than BDFCD is very difficult to be removed by floating; the Brownian collision dominant region is the area in which inclusion particles with diameter less than 2.5μm collide with each other and the inclusion particles with diameter of 2.5-5μm collide with small ones with diameter less than 0.5μm; the inclusion particles with diameter of 20-150μm can easily be completely removed by floating in the inclusion removal layer, but the removal rate of inclusion particles with diameter less than 10μm is very small and rise slowly, so these small inclusion particles are the main control objects to improve steel cleanliness.

收稿日期: 2011-06-30 出版日期: 2012-04-25

PACS:

TF 7

引用本文:

郭洛方，李宏，王耀，李永卿. Al2O3夹杂物在钢-渣界面处的运动特性及去除率[J]. 钢铁, 2012, 47(4): 23-27. GUO Luo-fang,LI Hong,WANG Yao，LI Yong-qing. Floating Critical Diameter and Removal Ratio of Al2O3 Particles in Interface Between Steel and Slag. Iron and Steel, 2012, 47(4): 23-27.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/ 或 http://www.chinamet.cn/Jweb_gt/CN/Y2012/V47/I4/23

[1]	舒志浩,程树森,赵晶晶,等. 钢液中夹杂物的碰撞长大及去除[J]. 北京科技大学学报.31（1）, 2009. 118-120. (Shu Z H,Cheng S S,et al.Inclusion cogulation and removal rate in molten steel[J],Jourmal of University of Science and Technology Beijing.31（1）,2009,118-120.)
[1]	舒志浩,程树森,赵晶晶,等. 钢液中夹杂物的碰撞长大及去除[J]. 北京科技大学学报.31（1）, 2009. 118-120. (Shu Z H,Cheng S S,et al.Inclusion cogulation and removal rate in molten steel[J],Jourmal of University of Science and Technology Beijing.31（1）,2009,118-120.)
[2]	张炯明,邓凤琴,王文科,王新华等. 连铸中间包钢水夹杂物浓度的数值模拟[J]. 北京科技大学学报. 2004, 26(3): 247-250. (Zhang J M,Deng F Q,Wang W K,et al,numerical Simulation of Dimensionless Inclusion Concentration in T-shape Tundishes[J],26（3）,2004,247-250.)
[2]	张炯明,邓凤琴,王文科,王新华等. 连铸中间包钢水夹杂物浓度的数值模拟[J]. 北京科技大学学报. 2004, 26(3): 247-250. (Zhang J M,Deng F Q,Wang W K,et al,numerical Simulation of Dimensionless Inclusion Concentration in T-shape Tundishes[J],26（3）,2004,247-250.)
[3]	P. Gardin, J.F. Domgin, M. Simonnet and J. Lehmann. Modeling of inclusion evolution in a steel ladle[J]. Revue de Métallurgie, 2008, Vol.2, 84.
[3]	P. Gardin, J.F. Domgin, M. Simonnet and J. Lehmann. Modeling of inclusion evolution in a steel ladle[J]. Revue de Métallurgie, 2008, Vol.2, 84.
[4]	Wang Jun, Zhu Miaoyong, Zhou Haibing and Wang Ying. Fluid flow and interfacial phenomenon of slag and metal in continuous casting tundish with argon blowing[J]. Journal of Iron and Steel Research, International, 2007, 15(4): 26-31.
[4]	Wang Jun, Zhu Miaoyong, Zhou Haibing and Wang Ying. Fluid flow and interfacial phenomenon of slag and metal in continuous casting tundish with argon blowing[J]. Journal of Iron and Steel Research, International, 2007, 15(4): 26-31.
[5]	王新华. 钢铁冶金—炼钢学[M]. 北京: 高等教育出版社, 2007.
[5]	王新华. 钢铁冶金—炼钢学[M]. 北京: 高等教育出版社, 2007.
[6]	沈颐身, 李保卫, 吴懋林. 冶金传输原理基础[M]. 北京: 冶金工业出版社, 2006.
[6]	沈颐身, 李保卫, 吴懋林. 冶金传输原理基础[M]. 北京: 冶金工业出版社, 2006.
[7]	汪志诚. 热力学-统计物理[第二版][M]. 北京: 高等教育出版社, 1992.
[7]	汪志诚. 热力学-统计物理[第二版][M]. 北京: 高等教育出版社, 1992.
[8]	S.Taniguchi and A.Kikuchi, Mechanisms of Collision and Coagulation Between Fine Particles in Fluid[J].ISIJ, 1992，78(4):527-535.
[8]	S.Taniguchi and A.Kikuchi, Mechanisms of Collision and Coagulation Between Fine Particles in Fluid[J].ISIJ, 1992，78(4):527-535.
[9]	U. Lindborg, K.Torssell, A collision model for the growth and separation of deoxidation products[J]. Transactions of the metallurgical society of AIME, 1968, (242):94-102.
[9]	U. Lindborg, K.Torssell, A collision model for the growth and separation of deoxidation products[J]. Transactions of the metallurgical society of AIME, 1968, (242):94-102.
[10]	Zhang Lifeng, Shoji Taniguchi and Kaike Cai. Fluid flow and inclusion removal in continuous casting tundish[J]. Metallurgical and Materials Transactions B, 2000, Vol.31B: 253-266.
[10]	Zhang Lifeng, Shoji Taniguchi and Kaike Cai. Fluid flow and inclusion removal in continuous casting tundish[J]. Metallurgical and Materials Transactions B, 2000, Vol.31B: 253-266.
[11]	George Kaptay. Classification of Interfacial Force, Acting on Solid Particles in Technologies of Advanced Metallic Materials[J]. International Conference “Advanced Metallic Materials” 5-7 November, 2003.
[11]	George Kaptay. Classification of Interfacial Force, Acting on Solid Particles in Technologies of Advanced Metallic Materials[J]. International Conference “Advanced Metallic Materials” 5-7 November, 2003.
[12]	Lifeng Zhang, Brian G. Thomas. Alumina Inclusion Behavior During Steel Deoxidation[J]. 7th European Electric Steelmaking Conference, Venice, Italy, Association Italiana di Metallurgical, Milano, Italy, May 26-29, 2002, 277-286.
[12]	Lifeng Zhang, Brian G. Thomas. Alumina Inclusion Behavior During Steel Deoxidation[J]. 7th European Electric Steelmaking Conference, Venice, Italy, Association Italiana di Metallurgical, Milano, Italy, May 26-29, 2002, 277-286.
[13]	黄希祜, 钢铁冶金原理[第3版][M]. 北京: 冶金工业出版社, 2000.
[13]	黄希祜, 钢铁冶金原理[第3版][M]. 北京: 冶金工业出版社, 2000.
[14]	K. Nakanishi, J. Szekely. Deoxidation Kinetics in a Turbulent Flow Field[J]. Trans. ISIJ, 1975, Vol. 15, 522-530.
[14]	K. Nakanishi, J. Szekely. Deoxidation Kinetics in a Turbulent Flow Field[J]. Trans. ISIJ, 1975, Vol. 15, 522-530.