摘要研究了S含量对高速车轮钢性能和夹杂物的影响。借助扫描电镜（SEM）对车轮钢中MnS，Al2O3等夹杂物进行了观察和统计分析，结果表明：随着S质量分数的增加（0.002%~0.014%），车轮钢的强度基本保持同一水平但冲击韧性先增加后降低，在S质量分数为0.011%时韧性最优。其原因在于S含量的增加可以有效地促进塑性较好的MnS对硬性的Al2O3相的包裹，从而改善钢的韧性；但S含量过度增加则导致MnS量过多，反而对韧性不利。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	余音宏
	潘涛
	尹建成
	苏航
	马跃

关键词 ：高速车轮钢, S含量, 夹杂物, 统计分析

Abstract：Effect of different contents of sulfur on the properties and inclusions in the high speed wheel steels was investigated. Inclusions (MnS, Al2O3) in the high speed wheel steels were observed by scanning electron microscopy (SEM) and statistically analyzed. The results show that, the impact toughness of the wheel steels increases with the ascending of sulfurs (0.002%-0.014%) at the beginning and gets the maximum at 0.011% then descends, while the strength remain almost the same level. The reason is that the increasing of the sulfur contents can effectively promote the covering ablity of MnS to Al2O3, which is good to the toughness of steels. However, too large content of sulfur is harm to the toughness of the wheel steels, for the excessive amount of MnS is got in this case.

Key words： high speed wheel steels sulfur contents inclusions statistical analysis

收稿日期: 2012-12-28 出版日期: 2013-10-14

PACS:

TG142.1

引用本文:

余音宏潘涛尹建成苏航马跃. S含量对高速车轮钢性能和夹杂物的影响[J]. 钢铁, 2013, 48(10): 57-62. YU Yin-hong,,PAN Tao,YIN Jian-cheng,SU Hang,MA Yue. Effect of Sulfur Contents on Properties and Inclusions in High Speed Wheel Steels. Iron and Steel, 2013, 48(10): 57-62.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/ 或 http://www.chinamet.cn/Jweb_gt/CN/Y2013/V48/I10/57

[1]	Lyne C M, Kasak A. Effect of Sulfur on the Fatigue Behavior of Bearing Steel[J]. Trans ASM, 1968; 61:10-13.
[1]	Lyne C M, Kasak A. Effect of Sulfur on the Fatigue Behavior of Bearing Steel[J]. Trans ASM, 1968; 61:10-13.
[2]	邓枝生. 硫对GCr15 轴承钢K (1c) 的影响[J].金属学报, 1976; 12: 187-190.
[2]	邓枝生. 硫对GCr15 轴承钢K (1c) 的影响[J].金属学报, 1976; 12: 187-190.
[3]	张维平. 硫化物对GCr15 轴承钢疲劳寿命的影响[J].四川师范大学学报(自然科学版), 2005; 28: 619-622.
[3]	张维平. 硫化物对GCr15 轴承钢疲劳寿命的影响[J].四川师范大学学报(自然科学版), 2005; 28: 619-622.
[4]	马跃, 潘涛, 江波, 崔银会, 苏航, 彭云. 硫含量对高速车轮钢断裂韧性影响的研究[J].金属学报, 2011; 47: 978-983.
[4]	马跃, 潘涛, 江波, 崔银会, 苏航, 彭云. 硫含量对高速车轮钢断裂韧性影响的研究[J].金属学报, 2011; 47: 978-983.
[5]	Birkle A J, Wei R P, Pellissier G E. Analysis of plane-strain fracture in a series of 0.45c-ni-cr-mo steels with different sulfur contents[J].Trans ASM, 1966, 59: 981-990.
[5]	Birkle A J, Wei R P, Pellissier G E. Analysis of plane-strain fracture in a series of 0.45c-ni-cr-mo steels with different sulfur contents[J].Trans ASM, 1966, 59: 981-990.
[6]	Raghupathy V P, Srinivasan V, Krishnan H, Chandrasekharaiah M N. The effect of sulphide inclusions on fracture toughness and fatigue crack growth in 12 wt% Cr steels[J]. J Mater Sci, 1982, 17: 2112-2126.
[6]	Raghupathy V P, Srinivasan V, Krishnan H, Chandrasekharaiah M N. The effect of sulphide inclusions on fracture toughness and fatigue crack growth in 12 wt% Cr steels[J]. J Mater Sci, 1982, 17: 2112-2126.
[7]	杨成威, 吕迺冰, 卓晓军, 王新华, 王万军. MnS 在Ti-Al复合脱氧氧化物上的析出研究[J].钢铁，2010; 45(11): 32-36
[7]	杨成威, 吕迺冰, 卓晓军, 王新华, 王万军. MnS 在Ti-Al复合脱氧氧化物上的析出研究[J].钢铁，2010; 45(11): 32-36
[8]	Oikawa K, Ohtani H, Ishida K, Nishizawa T. The Control of the Morphology of MnS Inclusions in Steel during Solidification[J].ISIJ international,1995; 35(4)：402-408.
[8]	Oikawa K, Ohtani H, Ishida K, Nishizawa T. The Control of the Morphology of MnS Inclusions in Steel during Solidification[J].ISIJ international,1995; 35(4)：402-408.
[9]	Masamitsu W, Takashi S, Shozo M. Effect of S content on the MnS precipitation in steel with oxide nuclei[J].ISIJ International, 1996; 36(8): 1014-1021.
[9]	Masamitsu W, Takashi S, Shozo M. Effect of S content on the MnS precipitation in steel with oxide nuclei[J].ISIJ International, 1996; 36(8): 1014-1021.
[10]	Li J, Guo F, Li Z, Wang J L, Yan M G. Influence of sizes of inclusions and voids on fracture toughness of Ultra-High strength steel aerMet100[J]. J Iron Steel Research, Inter, 2007, 14: 254-258.
[10]	Li J, Guo F, Li Z, Wang J L, Yan M G. Influence of sizes of inclusions and voids on fracture toughness of Ultra-High strength steel aerMet100[J]. J Iron Steel Research, Inter, 2007, 14: 254-258.
[11]	Garrison Jr W M, Wojcieszynski A L. A discussion of the effect of inclusion volume fraction on the toughness of steel[J]. Materials Science and Engineering: A, 2007, 464: 321-329.
[11]	Garrison Jr W M, Wojcieszynski A L. A discussion of the effect of inclusion volume fraction on the toughness of steel[J]. Materials Science and Engineering: A, 2007, 464: 321-329.