Effect and Mechanism of Heat Treatment on Mechanical Property of AM355 Steel
SUN Yong-qing1, LIANG Jian-xiong1, YANG Zhi-yong1, LIU Zhen-bao1, LI Wen-hui1, ZHANG Li-na2
1. Special Steel Institute, Central Iron and Steel Research Institute, Beijing 100081, China 2. Technical Centre, Fushun Special Steel Co., Ltd., Fushun 113001, Liaoning, China
Abstract：Different heat treatment process on AM355 steel bars were searched, which were produced by VIM+ESR technique and forged into φ80mm. Mechanical properties were tested after different quench temperatures, followed by same deep cold and different temperature. The results show that, with a contrast of traditional heat treatment （1 070 ℃×1 h AC＋（－70 ℃）×8 h＋200 ℃×2 h AC）, new heat treatment process (1 000 ℃×1 h AC＋（－70 ℃）×8 h＋450 ℃×2 h AC＋200 ℃×2 h AC) can lead a rise of about 100 MPa in strength and 5HRC in hardness. Details of mechanical property are: [Rm＝]1 630 MPa, [Re＝]1 380 MPa, [A＝]16%, [Z＝]59%, impact energy 51 J, 50HRC. Sorts and precipitations of carbides in this AM355 bar were carried out by SEM and TEM, and strengthening mechanism were also searched. In conclusion, the quenching temperature has main effect on grain size, carbides, remained austenite, etc., and the exist of M23C6 carbide can lead a high strength.
孙永庆， 梁剑雄， 杨志勇， 刘振宝， 李文辉， 张丽娜. 热处理工艺对AM355不锈钢力学性能的影响及机理[J]. 钢铁, 2014, 49(9): 77-80.
SUN Yong-qing, LIANG Jian-xiong, YANG Zhi-yong, LIU Zhen-bao, LI Wen-hui, ZHANG Li-na. Effect and Mechanism of Heat Treatment on Mechanical Property of AM355 Steel. Iron and Steel, 2014, 49(9): 77-80.
2014, Vol. 49 