Abstract：In order to develop thick steel plate which is more than 150 mm thickness， the process which consists of the application of Q345B continuous casting slab with surface scarfing， vacuum welding and heat in chamber furnace， and the rolling by heavy steel plate mill was used to produce cladding heavy steel plate 200 mm in thickness. The bonding degree and mechanical properties were tested by flaw detection， tensile， shear and cold bending tests. Microstructure and the tensile fracture of heavy steel plate were analyzed by means of optical microscope and scanning electron microscope. Results show that the heavy steel plate produced by current process has good bonding properties and can satisfy the GB/T 7734—2004Ⅰdemand of flaw detection. Both the structure at bonding site and matrix structure are ferrite plus pearlite. The reduction on cross section in thickness direction reaches more than 35%.
收稿日期: 2015-04-21
出版日期: 2015-10-29
引用本文:
李文斌，原思宇，李广龙，费 静. Q345B特厚复合钢板开发[J]. 钢铁, 2015, 50(11): 88-92.
LI Wen-bin，YUAN Si-yu，LI Guang-long，FEI Jing. Research on the bonding properties of Q345B cladding heavy steel plate. Iron and Steel, 2015, 50(11): 88-92.
Zang Y,Cao J N,Hu X Z,The analyzed for the processing way toproduct heavy plate by ingot / /2009 CSM Annual Meeting Proceedings,2009’3: 141( 臧悦,曹建宁,胡小卓.采用钢锭生产特厚板工艺方案的探讨/ /第七届中国钢铁年会论文集,2009’3: 141)
[1]
Zang Y,Cao J N,Hu X Z,The analyzed for the processing way toproduct heavy plate by ingot / /2009 CSM Annual Meeting Proceedings,2009’3: 141( 臧悦,曹建宁,胡小卓.采用钢锭生产特厚板工艺方案的探讨/ /第七届中国钢铁年会论文集,2009’3: 141)
[2]
Wang G L, Luo Z A, Xie G M et al. Experiment Research on Impact of Total Rolling Reduction Ratio on the Properties of Vacuum Rolling-Bonding Ultra-Thick steel plate [J]. Advanced Materials Research, 2011, 299: 962-965.
[2]
Wang G L, Luo Z A, Xie G M et al. Experiment Research on Impact of Total Rolling Reduction Ratio on the Properties of Vacuum Rolling-Bonding Ultra-Thick steel plate [J]. Advanced Materials Research, 2011, 299: 962-965.
[3]
Nishida S, Matsuoka T, Wada T. Technology and Products of JFE Steel’s Three Plate Mills [J]. JFE Technological Report, 2005, 5(3): 1-8.[4］ Wang D W,The new progress of the production technology for ultra-heavy plate,China Steel Focus,2009’5: 56( 王定武.特厚钢板制造技术的新进展.冶金管理.2009’5:56)
[3]
Nishida S, Matsuoka T, Wada T. Technology and Products of JFE Steel’s Three Plate Mills [J]. JFE Technological Report, 2005, 5(3): 1-8.[4］ Wang D W,The new progress of the production technology for ultra-heavy plate,China Steel Focus,2009’5: 56( 王定武.特厚钢板制造技术的新进展.冶金管理.2009’5:56)
2015, Vol. 50 