Contrast on non-metallic inclusions control in wire rods for saw wire
WANG Kun-peng1，JIANG Min1，ZHAO Hao-qian2，WANG Xin-hua1，WANG Ying2
1. School of Metallurgical and Ecological Engineering， University of Science and Technology Beijing， Beijing 100083， China 2. Technology Center， Xingtai Iron and Steel Co.， Ltd.， Xingtai 054027， Hebei， China
Abstract：Inclusions in wire rods for saw wire produced in Kobe steel and a steel works of China were investigated by means of automatic analysis technology using Aspex Explorer. Inclusion size， number density， composition and morphology were studied systematically. The results show that the inclusions of wire rods from Kobe steel are in a low amount and the size is less than 5 μm on cross section. There are two type inclusions in Kobe wire rods， namely， the SiO2 rich SiO2-MnO-Al2O3-(R2O，R=Na、K) type and the low melting point CaO-SiO2-Al2O3-MnO-(MgO) type， both of them are elongated during rolling and are nearly harmless. Inclusions of wire rods from China are also classified into two types： SiO2-MnO-Al2O3 and CaO-SiO2-Al2O3-MnO-(MgO). The inclusions in wire rods from China are not only in lager amount but also in worse deformability. The inclusions more than 5μm in size were observed on cross section of wire rods from China. Chemical analysis shows[w([Al]s)]is 0.000 4%-0.000 6% and [w(T[O])]is 0.001 2%-0.001 3% in Kobe wire rod while[w([Al]s)]is 0.000 4%-0.000 6% and[w(T[O])]is 0.001 2%-0.001 3% in domestic ones.
王昆鹏，姜 敏，赵昊乾，王新华，王 郢. 切割丝用盘条非金属夹杂物对比分析[J]. 钢铁, 2016, 51(1): 33-38.
WANG Kun-peng，JIANG Min，ZHAO Hao-qian，WANG Xin-hua，WANG Ying. Contrast on non-metallic inclusions control in wire rods for saw wire. Iron and Steel, 2016, 51(1): 33-38.
Maede S，Soejima，Saito T et al.Shape control of inclusions in wire rods for high tensile tire cord by refining with synthetic slag[C].Steelmaking Conference Proceedings, 1989, 77:379-385
[1]
Maede S，Soejima，Saito T et al.Shape control of inclusions in wire rods for high tensile tire cord by refining with synthetic slag[C].Steelmaking Conference Proceedings, 1989, 77:379-385
[2]
Kang Y B，Lee H G.Inclusions chemistry for MnSi deoxidized steels: thermodynamic predictions and experimental confirmations[J].ISIJ Int, 2004, 44(6):1006-1015
[2]
Kang Y B，Lee H G.Inclusions chemistry for MnSi deoxidized steels: thermodynamic predictions and experimental confirmations[J].ISIJ Int, 2004, 44(6):1006-1015
[3]
Karihara K.Production technology of wire rod for high tensile strength steel cord[J].Kobelco technology review, 1989, 77:379-385
[3]
Karihara K.Production technology of wire rod for high tensile strength steel cord[J].Kobelco technology review, 1989, 77:379-385
Chen S H，Jiang M，He X F et al.Top slag refining for inclusion composition transform control in tire cord steel[J].International Journal of Minerals, Metallurgy and Materials, 2012, 19(6):490-498
[6]
Chen S H，Jiang M，He X F et al.Top slag refining for inclusion composition transform control in tire cord steel[J].International Journal of Minerals, Metallurgy and Materials, 2012, 19(6):490-498
2016, Vol. 51 