Abstract:The technology of hot metal dephosphorization pretreatment and less-slag steelmaking process was optimized step by step in Shougang Jingtang. The dephosphorization rate could reach 70% through the optimization of scrap size,bottom tuyer number and arrangement in De-P converter. The steady temperature and P content in semi-steel after the pretreatment in De-P converter can provide a good condition for the less-slag steelmaking and automatic steelmaking to achieve double hit ratios by steelmaking end. By the measurements,such as keeping slag operation,less-slag steelmaking and slag splashing technology,the automatic end-point aim can reach 90% and the lining life was more than 7 000. All the materials containing Fe,such as steel containing slag, precipitator dust,scales and so on,were all recycled in steelmaking plant. Through the dephosphorization pretreatment and less-slag steelmaking process,the quality of steel improved,the total content of S,P,N can reach less than 0.009 5% in ultra-low P and S steel grades.
收稿日期: 2015-10-10
出版日期: 2016-04-26
引用本文:
赵长亮,孙彦辉,袁天祥,闫占辉,罗 磊. 转炉预脱磷与“全三脱”铁水少渣冶炼技术[J]. 钢铁, 2016, 51(5): 28-36.
ZHAO Chang-liang,,SUN Yan-hui,YUAN Tian-xiang,YAN Zhan-hui,LUO Lei. Dephosphorization pretreatment in LD converter and less-slag steelmaking process. Iron and Steel, 2016, 51(5): 28-36.