Abstract：In order to study the law of solid phase decarburization reaction?of 2 mm Fe-C alloy sheets， the Fe-C alloy sheets were decarburized by introducing oxidizing gas of Ar-H2-H2O into the horizontal furnace for producing low carbon steel sheets. The Fe-C alloy sheets which initial carbon contents were 4.15% and 3.2%， were placed in heating atmosphere. Various heating temperature and decarburization time were investigated. The results showed that the diffusion of carbon to the reaction interface is the rate controlling step of the decarburizing process， and both higher decarburization temperature and longer decarburization time are beneficial to the decarburization process. The Fe-C alloy sheets which have different initial carbon content have the same decarburization rate in the early stage of the reaction. The Fe-C alloy sheet is so thick that the final carbon content can not meet the requirement， thus， a segmented heating decarburization process is proposed to serve this issue. This process has a positive influence on decarburization， and it is found that sheets with 0.28% C（mass percent） can be produced from sheets with initial 4.15% C（mass percent） and with the thickness of 2.0 mm through segmented heating decarburization process within 70 min， and sheets with 0.23% C（mass percent） can be produced from sheets with initial 4.15% C（mass percent） and with the thickness of 2.0 mm through segmented heating decarburization process within 50 min.
收稿日期: 2015-09-21
出版日期: 2016-07-11
引用本文:
程 荣，艾立群，洪陆阔，李 强，李亚强. 2 mm铁碳合金薄带固态脱碳试验[J]. 钢铁, 2016, 51(7): 28-33.
CHENG Rong，AI Li-qun，HONG Lu-kuo，LI Qiang，LI Ya-qiang. Experiment of solid state decarburization process of 2 mm Fe-C alloy sheet. Iron and Steel, 2016, 51(7): 28-33.
J.M.Song, T.S.Lui, L.H.Chen. A study on inhomogeneous distribution of temper graphite particles in strip-cast Fe-C-Si alloys [J].Metallurgical and Materials Transactions A, 2002, 33A(4):1263-1273
[2]
J.M.Song, T.S.Lui, L.H.Chen. A study on inhomogeneous distribution of temper graphite particles in strip-cast Fe-C-Si alloys [J].Metallurgical and Materials Transactions A, 2002, 33A(4):1263-1273
[3]
J.Y.Parka, K.T.Choib, J. A. Szpunara, K.H.Ohc, H.Y.Rac..Effect of Mn negative segregation through the thickness direction on graphitization characteristics of strip-cast white cast iron[J].Scripta Materialia, 2002, 46(3):199-203
[3]
J.Y.Parka, K.T.Choib, J. A. Szpunara, K.H.Ohc, H.Y.Rac..Effect of Mn negative segregation through the thickness direction on graphitization characteristics of strip-cast white cast iron[J].Scripta Materialia, 2002, 46(3):199-203
[4]
Y.W.Chao, T.S.Lui and F.T.Shiao.Characteristics of rapidly solidified cast iron produced by strip casting process. [J].AFS Trans ., . 1994,, 102(1):199-204
[4]
Y.W.Chao, T.S.Lui and F.T.Shiao.Characteristics of rapidly solidified cast iron produced by strip casting process. [J].AFS Trans ., . 1994,, 102(1):199-204
[5]
R.Mahapatra1, W.Blejde1, G.Gillen2, P.Campbell1 and R.Wechsler1..The Status of Twin-roll Strip Casting Technology –Castrip Process.[J].SCANMET II – 2nd International Conference on Process Development in Iron and Steelmaking.Lule?,, 2004, Sweden( June 6-9.):161-172
[5]
R.Mahapatra1, W.Blejde1, G.Gillen2, P.Campbell1 and R.Wechsler1..The Status of Twin-roll Strip Casting Technology –Castrip Process.[J].SCANMET II – 2nd International Conference on Process Development in Iron and Steelmaking.Lule?,, 2004, Sweden( June 6-9.):161-172
Ji-OoPARK, Tran van LONG and Yasushi SASAKI.Feasibility of Solid-state Steelmaking from Cast Iron Decarburization of Rapidly Solidified Cast Iron[J].ISIJ International, 2012, 52(1):26-34
[8]
Ji-OoPARK, Tran van LONG and Yasushi SASAKI.Feasibility of Solid-state Steelmaking from Cast Iron Decarburization of Rapidly Solidified Cast Iron[J].ISIJ International, 2012, 52(1):26-34
2016, Vol. 51 