Research progress on ultra-long-life fatigue properties of steel and its influencing factors
ZHANG Zhi-jun1,2,HE Bo-lin1,2,LI Li1,2
1. School of Mechanical and Electrical Engineering, East China Jiaotong University, Nanchang 330013,Jiangxi,China 2. Key Laboratory for Conveyance and Equipment of Ministry of Education, East China Jiaotong University, Nanchang 330013,Jiangxi,China
Abstract:In the modern industry, many steel structures are required to bear the fatigue load more than 108 cycles, so the research of ultra-long-life fatigue properties of steel has become a hot-spot in the research of the fatigue field. The research status and progress on fatigue properties of steel in ultra-long-life regime and its influencing factors are reviewed in this paper, which mainly introduced the S-N curves, the mechanism of crack initiation and propagation, and several impact factors of ultra-long-life fatigue of steel. Besides, several points which need further research on ultra-long-life fatigue of steel are put forward to provide a reference for the current research.
张志军,何柏林,李 力,. 钢的超高周疲劳性能及其影响因素研究进展[J]. 钢铁, 2016, 51(10): 62-68.
ZHANG Zhi-jun,,HE Bo-lin,,LI Li,. Research progress on ultra-long-life fatigue properties of steel and its influencing factors. Iron and Steel, 2016, 51(10): 62-68.
Natio T, Ueda H, Kikuchi M. Observation of Fatigue Fracture Surface of Carburized Steel[J]. Journal of the Society of Materials Science, Japan. 1983, 32(361): 1162-1166.
[1]
Natio T, Ueda H, Kikuchi M. Observation of Fatigue Fracture Surface of Carburized Steel[J]. Journal of the Society of Materials Science, Japan. 1983, 32(361): 1162-1166.
Wei K, He B L. Failure Mechanism of Very High Cycle Fatigue for High Strength Steels[J]. Key Engineering Materials, 2015, 664:275-281.
[4]
Wei K, He B L. Failure Mechanism of Very High Cycle Fatigue for High Strength Steels[J]. Key Engineering Materials, 2015, 664:275-281.
[5]
W. J. Hui, C. Zhou, Y. J. Zhang, et al. Very high cycle fatigue properties of high-strength spring steel 60SiCrV7[J]. Fatigue & Fracture of Engineering Materials & Structures, 2016,00:1-11.
[5]
W. J. Hui, C. Zhou, Y. J. Zhang, et al. Very high cycle fatigue properties of high-strength spring steel 60SiCrV7[J]. Fatigue & Fracture of Engineering Materials & Structures, 2016,00:1-11.
[6]
Shiozawa K, Lu L, Ishihara S. S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon chromium bearing steel [J]. Fatigue Fracture Engineering Materials Structures,2001(24):781-790.
[6]
Shiozawa K, Lu L, Ishihara S. S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon chromium bearing steel [J]. Fatigue Fracture Engineering Materials Structures,2001(24):781-790.
[7]
Shiozawa K, Hasegawa T, Kashiwagi Y. Veiy high cycle fatigue properties of bearing steel under axial loading condition[J]. International Journal of Fatigue, 2009,31:880-888.
[7]
Shiozawa K, Hasegawa T, Kashiwagi Y. Veiy high cycle fatigue properties of bearing steel under axial loading condition[J]. International Journal of Fatigue, 2009,31:880-888.
L. T. L U, Zhang J W, Shiozawa K. Influence of inclusion size on S‐N curve characteristics of high-strength steels in the giga-cycle fatigue regime[J]. Fatigue & Fracture of Engineering Materials & Structures, 2009, 32(32):647-655.
[9]
L. T. L U, Zhang J W, Shiozawa K. Influence of inclusion size on S‐N curve characteristics of high-strength steels in the giga-cycle fatigue regime[J]. Fatigue & Fracture of Engineering Materials & Structures, 2009, 32(32):647-655.
Wang Q Y, Berard J Y, Rathery S, et al. High-cycle fatigue crack initiation and propagation behavior of high-strength spring steel wires[J]. Fatigue & Fracture of Engineering Materials & Structures, 1999, 22(8): 673-677.
[12]
Wang Q Y, Berard J Y, Rathery S, et al. High-cycle fatigue crack initiation and propagation behavior of high-strength spring steel wires[J]. Fatigue & Fracture of Engineering Materials & Structures, 1999, 22(8): 673-677.
[13]
Marines-Garcia I, Paris P C, Tada H, et al. Fatigue crack growth from small to long cracks in VHCF with surface initiations[J]. International Journal of Fatigue, 2007, 29(9): 2072-2078.
[13]
Marines-Garcia I, Paris P C, Tada H, et al. Fatigue crack growth from small to long cracks in VHCF with surface initiations[J]. International Journal of Fatigue, 2007, 29(9): 2072-2078.
[14]
Bathias. There is no infinite fatigue life in metallic materials[J]. Fatigue & Fracture of Engineering Materials & Structures, 1999, 22(7):559–565.
[14]
Bathias. There is no infinite fatigue life in metallic materials[J]. Fatigue & Fracture of Engineering Materials & Structures, 1999, 22(7):559–565.
[15]
Yao J, Qu X H, He X B, et al. Effect of inclusion size on the high cycle fatigue strength and failure mode of a high V alloyed powder metallurgy tool steel[J]. International Journal of Minerals Metallurgy & Materials, 2012, 19(7):608-614.
[15]
Yao J, Qu X H, He X B, et al. Effect of inclusion size on the high cycle fatigue strength and failure mode of a high V alloyed powder metallurgy tool steel[J]. International Journal of Minerals Metallurgy & Materials, 2012, 19(7):608-614.
[16]
Zhao H M, Hui W J, Nie Y H, et al. Effect of Inclusion Size on High-Cycle Fatigue Behavior of High Strength Spring Steel[J]. Iron & Steel, 2008,43(5):66-70.
[16]
Zhao H M, Hui W J, Nie Y H, et al. Effect of Inclusion Size on High-Cycle Fatigue Behavior of High Strength Spring Steel[J]. Iron & Steel, 2008,43(5):66-70.
[17]
Chao, He. Very high cycle fatigue behavior of bridge steel welded joint[J]. 力学快报(英文版), 2012, 2(03):36-40.
[18]
刘龙隆. 25Cr2Ni2MoV钢焊接接头的超高周疲劳行为研究[D]. 华东理工大学, 2014.
[17]
Chao, He. Very high cycle fatigue behavior of bridge steel welded joint[J]. 力学快报(英文版), 2012, 2(03):36-40.
[19]
Xu X X, Yu Y, Cui W L, et al. Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure[J]. 矿物冶金与材料学报:英文版, 2009, 16(3):285-292.
[18]
刘龙隆. 25Cr2Ni2MoV钢焊接接头的超高周疲劳行为研究[D]. 华东理工大学, 2014.
[19]
Xu X X, Yu Y, Cui W L, et al. Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure[J]. 矿物冶金与材料学报:英文版, 2009, 16(3):285-292.
[20]
Murakami Y, YokoyamaN N, Nagata J. Mechanism of fatigue failure in ultra-long life regime [J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):735-746.
[20]
Murakami Y, YokoyamaN N, Nagata J. Mechanism of fatigue failure in ultra-long life regime [J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):735-746.
[21]
Sakai T, Sato Y, Oguma N. Characteristic S-N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue[J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):765-773.
[21]
Sakai T, Sato Y, Oguma N. Characteristic S-N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue[J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):765-773.
[22]
Paris P C, Erdogan F. A critical analysis of crack propagation laws[J]. Journal of Fluids Engineering, 1963, 85(4): 528-533.
[22]
Paris P C, Erdogan F. A critical analysis of crack propagation laws[J]. Journal of Fluids Engineering, 1963, 85(4): 528-533.
[23]
Tanaka K, Akiniwa Y. Fatigue crack propagation behaviour derived from S-N data in very high cycle regime[J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):775–784.
[23]
Tanaka K, Akiniwa Y. Fatigue crack propagation behaviour derived from S-N data in very high cycle regime[J]. Fatigue & Fracture of Engineering Materials & Structures, 2002, 25(8-9):775–784.
[24]
Li W, Sakai T, Li Q, et al. Reliability evaluation on very high cycle fatigue property of GCr15 bearing steel[J]. International Journal of Fatigue, 2010, 32(7):1096-1107.
[24]
Li W, Sakai T, Li Q, et al. Reliability evaluation on very high cycle fatigue property of GCr15 bearing steel[J]. International Journal of Fatigue, 2010, 32(7):1096-1107.
[25]
Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape[J]. Engineering Fracture Mechanics, 1985, 22(1):101-114.
[25]
Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape[J]. Engineering Fracture Mechanics, 1985, 22(1):101-114.
[26]
倪金刚.超声疲劳试验技术的应用[J].航空动力学报,1995,10(3):245-248.
[26]
倪金刚.超声疲劳试验技术的应用[J].航空动力学报,1995,10(3):245-248.
[27]
Roth L D, Willertz L E, Leax T R. On the fatigue of copper up to ultrasonic frequencies[J]. Ultrasonic Fatigue, 1981: 265-282.
[27]
Roth L D, Willertz L E, Leax T R. On the fatigue of copper up to ultrasonic frequencies[J]. Ultrasonic Fatigue, 1981: 265-282.
[28]
kikukawa M., K. Oji and K. Ogura, Trans JSME, 32(1966): 36-370.
[28]
kikukawa M., K. Oji and K. Ogura, Trans JSME, 32(1966): 36-370.
[29]
Kikukawa M., K.Oji and K.Ogura,Trans JSME,32(1966):875-879.
[29]
Kikukawa M., K.Oji and K.Ogura,Trans JSME,32(1966):875-879.
Nakajima M, Tokaji K, Itoga H, et al. Morphology of step-wise S–N curves depending on work-hardened layer and humidity in a high-strength steel[J]. Fatigue & Fracture of Engineering Materials & Structures, 2003, 26(12):1113–1118.
[33]
Nakajima M, Tokaji K, Itoga H, et al. Morphology of step-wise S–N curves depending on work-hardened layer and humidity in a high-strength steel[J]. Fatigue & Fracture of Engineering Materials & Structures, 2003, 26(12):1113–1118.