Abstract：The high temperature carbothermic reduction test of domestic stainless steel slag was conducted， reducing valuable metals. The effects of carbon equivalent， basicity， reaction temperature and thermal insulation time on the reduction ratio of Fe and Cr were studied. Results show that the reduction ratio of Fe and Cr improved with the increase of carbon equivalent and reaction temperature and the reduction of basicity. The highest reduction ratio of Fe and Cr reached at 93.92% and 72.76%， respectively. The reduction ratio was low when the carbon equivalent was less， and with the increase of carbon equivalent， the reduction ratio of Cr raised sharply as the reduction ratio of Fe became stable. The reduction of Fe and Cr became less steep when the basicity ranged from 1.4 to 1.2. When the holding time was over 60 min， there was no significant effect on increasing the reduction ratio of Fe and Cr.
收稿日期: 2016-06-28
出版日期: 2017-03-10
引用本文:
漆启松，徐安军， ，贺东风，潘江涛，. 碳热还原法回收不锈钢尾渣中铁和铬的试验[J]. 钢铁, 2017, 52(3): 82-87.
QI Qi-song，，XU An-jun，，HE Dong-feng，，PAN Jiang-tao，. Carbothermic reduction for recycling of iron and chromium from stainless steel slag. Iron and Steel, 2017, 52(3): 82-87.
Noboru YOSHIKAWA.Microwave carbo-thermal reduction for recycling of cr from cr-containing steel making wastes[J].ISIJ International, 2008, 48(5):690-695
[10]
Noboru YOSHIKAWA.Microwave carbo-thermal reduction for recycling of cr from cr-containing steel making wastes[J].ISIJ International, 2008, 48(5):690-695
[11]
D Park，S R Lim，H W Lee.Mechanism and kinetics of cr(VI) reduction by waste slag generated from iron making industry[J][J].Hydrometallurgy, 2008, 1(93):72-75
[11]
D Park，S R Lim，H W Lee.Mechanism and kinetics of cr(VI) reduction by waste slag generated from iron making industry[J][J].Hydrometallurgy, 2008, 1(93):72-75
[12]
Sheen Y N，Wang H Y，Sun T H.A study of engineering properties of cement mortar with stainless steel oxidizing slag and reducing slag resource materials[J].Construction and Building Materials, 2013, 1(40):239-245
[12]
Sheen Y N，Wang H Y，Sun T H.A study of engineering properties of cement mortar with stainless steel oxidizing slag and reducing slag resource materials[J].Construction and Building Materials, 2013, 1(40):239-245
2017, Vol. 52 