Development and application of ferrite rolling to Ti-IF steel in hot continuous rolling line
WANG Jian-gong1,ZHAO Hu2,XIA Yin-feng1,ZHOU Xun1,KANG Yong-lin3,QIU Chen-yang3
(1. Hot Rolling Department, Shougang Jingtang United Iron and Steel Co., Ltd., Tangshan 063200, Hebei, China 2. Sheet Metal Research Institute, Shougang Research Institute of Technology, Beijing 100041, China 3. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China)
Abstract:The advantages, characteristics and development of ferrite rolling in domestic and foreign iron and steel enterprises were introduced. Besides, the successful development and application of ferrite rolling to Ti-IF steel in hot continuous rolling line were introduced. Through analysis of the process system and designing the composition system based on the equipment characteristics of conventional hot rolling line, the method and processing technology for producing sheet steel product by ferrite rolling was obtained. The lubrication conditions during the Ti-IF steel ferrite rolling was improved. After improving the lubrication conditions and analyzing the {111} texture intensity before and after improvement, finally the low temperature(1 100 ℃) rolling technology was realized and the purpose of improving the yield of rolling line and energy saving is achieved. In the view of product development and creating customers, it provided technical support for ferrite rolling with high quality.
收稿日期: 2017-04-05
出版日期: 2017-09-29
引用本文:
王建功,赵 虎,夏银锋,周 旬,康永林, 邱晨阳. 常规热连轧线Ti-IF钢铁素体轧制工艺研究与应用[J]. 钢铁, 2017, 52(10): 65-71.
WANG Jian-gong,ZHAO Hu,XIA Yin-feng,ZHOU Xun,KANG Yong-lin,QIU Chen-yang. Development and application of ferrite rolling to Ti-IF steel in hot continuous rolling line. Iron and Steel, 2017, 52(10): 65-71.