Abstract:In order to analyze the fiberization mechanism of melting slag and its influencing factors. The fiberization process of molten BF slag was studied experimentally through centrifugal method. Combining the experimental results, factors influenceing the length and the diameter of blast furnace slag fibers were investigated, and the influence of such parameters as roll diameter, roll speed and outlet slag temperature on the centrifugal spinning process and the obtained fibers were also analyzed. Under the experimental conditions, the optimum tapping temperature was 1450 ℃, the four rollers speed of the four-roller centrifuge were 3 840,4 620,5 220 and 5 820 r/min respectively. The results show that the We number and the Oh number of the molten slag must reach 4.223×106-4.28××106 and 3.81×10-2-4.56×10-2 respectively to produce a fibrosis decomposition. The two parameters reflect the relationship among the factors that affect the fibrosis of the slag and finally the expression of fiber diameter and fiber length in the test condition are determined.
Liu J X, Yu Q B, Duan W J, et al.Experimental investigation on ligament formation for molten slag[J].Applied Thermal Engineering, 2014, 73(1):888-893
[3]
Liu J X, Yu Q B, Duan W J, et al.Experimental investigation on ligament formation for molten slag[J].Applied Thermal Engineering, 2014, 73(1):888-893
[4]
Liu Jun-xiang, Yu Qing-bo, Li Peng, et al.Cold experiments on ligament formation for blast furnace slag granulation[J].Applied Thermal Engineering, 2012, 40(-):351-357
[4]
Liu Jun-xiang, Yu Qing-bo, Li Peng, et al.Cold experiments on ligament formation for blast furnace slag granulation[J].Applied Thermal Engineering, 2012, 40(-):351-357
[5]
Liu J X, Yu Q B, Guo Q.Experimental investigation of liquid disintegration by rotary cups[J].Chemical Engineering Science, 2012, 73(19):44-50
[5]
Liu J X, Yu Q B, Guo Q.Experimental investigation of liquid disintegration by rotary cups[J].Chemical Engineering Science, 2012, 73(19):44-50
[6]
irok Brane, Bizjan Benjamin, Orbani? Alen, et al.Mineral wool melt fiberization on a spinner wheel[J].Chemical Engineering Research and Design, 2014, 92(1):80-90
[6]
irok Brane, Bizjan Benjamin, Orbani? Alen, et al.Mineral wool melt fiberization on a spinner wheel[J].Chemical Engineering Research and Design, 2014, 92(1):80-90
[7]
Eisenklam P. On ligament formation from spinning discs and cups[J].Chemistry Engineering Science, 1964, 19(-):693-694
[7]
Eisenklam P. On ligament formation from spinning discs and cups[J].Chemistry Engineering Science, 1964, 19(-):693-694
Benjamin Bizjan, Brane ?irok, Marko Ho?evar, et al.Ligament-type liquid disintegration by a spinning wheel[J].Chemical Engineering Science, 2014, 116(-):172-182
[9]
Benjamin Bizjan, Brane ?irok, Marko Ho?evar, et al.Ligament-type liquid disintegration by a spinning wheel[J].Chemical Engineering Science, 2014, 116(-):172-182
[10]
Bizjan B, ?irok B, Ho?evar M, et al.Liquid ligament formation dynamics on a spinning wheel[J].Chemical Engineering Science, 2014, 119(-):187-198
[10]
Bizjan B, ?irok B, Ho?evar M, et al.Liquid ligament formation dynamics on a spinning wheel[J].Chemical Engineering Science, 2014, 119(-):187-198
[11]
周传典.高炉炼铁生产技术手册[M]. 北京: 冶金工业出版社, 2002: 126.
[11]
周传典.高炉炼铁生产技术手册[M]. 北京: 冶金工业出版社, 2002: 126.
[12]
Zhang G H, Kuo-Chih C.Model for Evaluating Density of Molten Slag With Optical Basicity[J].钢铁研究学报英文版, 2010, 17(4):1-4
[12]
Zhang G H, Kuo-Chih C.Model for Evaluating Density of Molten Slag With Optical Basicity[J].钢铁研究学报英文版, 2010, 17(4):1-4