Abstract:In order to study the influence of the main process parameters on the oxide scale of hot rolled strip, the nidustry experiment was carried out on the basis of CSP production line. The results show that the thickness of the strip has an important influence on the thickness of the oxide scale,and the thickness of oxide scale is unevenly distributed along the width of the stripdue to the difference of oxygen supply. By adjusting the final rolling temperature and laminar cooling method,the thickness of oxide scale can be reduced,but the effect is not obvious. Decreasing the coiling temperature is beneficial to promote the occurrence of eutectoid reaction of FeO,increase the ratio of α-Fe+Fe3O4,and improve the adhesion of oxide scale at room temperature. The distribution of oxide scales in the width of strip is uneven,and the eutectoid reaction of FeO in the middle is more adequate.
收稿日期: 2017-06-09
出版日期: 2018-02-05
引用本文:
汪水泽,刘 洋,孙宜强,胡宽辉. CSP流程薄规格热轧带钢氧化铁皮控制技术[J]. , 2018, 53(1): 54-58.
WANG Shui-ze,LIU Yang,SUN Yi-qiang,HU Kuan-hui. Control technology of oxide scale for thin gauge hot rolled strip in CSP process. Iron and Steel, 2018, 53(1): 54-58.
R. Y. Chen , W. Y. D. Yuen. Review of the High-Temperature Oxidation of Iron and Carbon Steels in Air or Oxygen[J] , Oxidation of Metals, 2003 , 59(5), 433-468.
[1]
R. Y. Chen , W. Y. D. Yuen. Review of the High-Temperature Oxidation of Iron and Carbon Steels in Air or Oxygen[J] , Oxidation of Metals, 2003 , 59(5), 433-468.
[2]
Huibin Qi, Yuhai Qian, Wei Wang, etal. “Quartus Scale” of Hot-rolled Strip Steels and Its Formation Mechanism [J]. Baosteel Technical Research, 2007, 1(1): 42-54.
[2]
Huibin Qi, Yuhai Qian, Wei Wang, etal. “Quartus Scale” of Hot-rolled Strip Steels and Its Formation Mechanism [J]. Baosteel Technical Research, 2007, 1(1): 42-54.
[3]
F. Friedel, H. Bolt, X. Cornet, et al. Investigation of the formation, constitution and properties of scale formed during the finishing rolling, cooling and coiling of thin hot strips [R], European Commission, 2004.
[3]
F. Friedel, H. Bolt, X. Cornet, et al. Investigation of the formation, constitution and properties of scale formed during the finishing rolling, cooling and coiling of thin hot strips [R], European Commission, 2004.