Comprehensive optimization setting of emulsion flowrate and concentration for double cold reduction mill
CUI Ya-ya1,LI Bo-yang1,BAI Zhen-hua1,2,CUI Xi-ying1,LI Xiao-feng1,XU Ji-shuan1
(1. National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University,Qinhuangdao 066004, Hebei, China 2. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China)
Abstract:In light of the problems that researches on the lubrication and oil consumption of direct application system were very few in the double cold reduction mill,the emulsion flow and concentration were set separately,and therefore the lubricity and oil consumption could not be fulfilled simultaneously, the emulsion flowrate and concentration comprehensive optimization technology for direct application system of double cold reduction mill was developed with oil consumption fixed mode and lubricity assured mode based on the equipment and technological characteristics of the direct application system of the double cold reduction mill,which considers the steel grade and specifications. The corresponding software of emulsion flowrate and concentration comprehensive optimization technology was compiled and applied to the production practice of a 1 220 double cold reduction mill,which achieves good results,with further popularization and application value.
Azushima A, Inagaki S. Measurement and Analysis of Inlet Oil Film Thickness in Cold Sheet Rolling with Oil-in-Water Emulsion[J]. Tribology Transactions, 2009, 52(4):427-434.
[1]
Azushima A, Inagaki S. Measurement and Analysis of Inlet Oil Film Thickness in Cold Sheet Rolling with Oil-in-Water Emulsion[J]. Tribology Transactions, 2009, 52(4):427-434.
[2]
Kimura Y, Fujita N, Matsubara Y, et al. High-speed rolling by hybrid-lubrication system in tandem cold rolling mills[J]. Journal of Materials Processing Tech, 2015, 216:357-368.
[2]
Kimura Y, Fujita N, Matsubara Y, et al. High-speed rolling by hybrid-lubrication system in tandem cold rolling mills[J]. Journal of Materials Processing Tech, 2015, 216:357-368.
[3]
Fujita N, Kimura Y, Kobayashi K, et al. Estimation model of plate-out oil film in high-speed tandem cold rolling[J]. Journal of Materials Processing Tech, 2015, 219:295-302.
[3]
Fujita N, Kimura Y, Kobayashi K, et al. Estimation model of plate-out oil film in high-speed tandem cold rolling[J]. Journal of Materials Processing Tech, 2015, 219:295-302.
BAI Zhen-hua, WANG Song-yao, CUI Ya-ya, et al. Study on Optimization Technology of Relationship Graph between Flow Rate of Emulsion and Rolling Speed in Cold Rolling Process[J]. Iron and Steel, 2017,52(07):58-63.
[4]
BAI Zhen-hua, WANG Song-yao, CUI Ya-ya, et al. Study on Optimization Technology of Relationship Graph between Flow Rate of Emulsion and Rolling Speed in Cold Rolling Process[J]. Iron and Steel, 2017,52(07):58-63.
BAI Zhen-hua, HOU Bin, SONG He-chuan, et al. Research on Comprehensive Optimization Setting Technology of Emulsion Flow in Cold Rolling Process[J]. Iron and Steel, 2017 , 52(3) :58-63.
[5]
BAI Zhen-hua, HOU Bin, SONG He-chuan, et al. Research on Comprehensive Optimization Setting Technology of Emulsion Flow in Cold Rolling Process[J]. Iron and Steel, 2017 , 52(3) :58-63.
BAI Zhen-hua, SI Hong-xin, ZHOU Qing-tian, et al. Comprehensive Optimized Technology of Processing Lubrication System In Double Cold Reduction[J]. Iron and Steel, 2011,46(06):60-62+73.
[6]
BAI Zhen-hua, SI Hong-xin, ZHOU Qing-tian, et al. Comprehensive Optimized Technology of Processing Lubrication System In Double Cold Reduction[J]. Iron and Steel, 2011,46(06):60-62+73.
[7]
Sun J, Yi M, Sun Q, et al. Experimental Investigation of the Relationship Between Lubricants' Tribological Properties and Their Lubricating Performances in Cold Rolling[J]. Journal of Electroanalytical Chemistry, 2014, 136(3):381-389.
[7]
Sun J, Yi M, Sun Q, et al. Experimental Investigation of the Relationship Between Lubricants' Tribological Properties and Their Lubricating Performances in Cold Rolling[J]. Journal of Electroanalytical Chemistry, 2014, 136(3):381-389.
LI Chang-sheng, LI You-yuan, YU Tao, et al. Experimental Research on Rolling- Lubricating Process on 4-igh Reversing Cold Rolling Mill[J]. Journal of Northeastern University (Natural Science), 2010,31(8):1117-1120.
[8]
LI Chang-sheng, LI You-yuan, YU Tao, et al. Experimental Research on Rolling- Lubricating Process on 4-igh Reversing Cold Rolling Mill[J]. Journal of Northeastern University (Natural Science), 2010,31(8):1117-1120.
BAI Zhen-hua, ZHOU Qing-tian, DOU Ai-min, et al. Study on Mechanism Model of Friction Coefficient in High-Speed Tandem Cold Rolling Process [J]. Iron and Steel, 2007,42(05):47-50.
[9]
BAI Zhen-hua, ZHOU Qing-tian, DOU Ai-min, et al. Study on Mechanism Model of Friction Coefficient in High-Speed Tandem Cold Rolling Process [J]. Iron and Steel, 2007,42(05):47-50.
[10]
曹鸿德. 塑性变形力学基础与轧制原理[M].北京∶机械工业出版社, 1979:211-245.
[10]
曹鸿德. 塑性变形力学基础与轧制原理[M].北京∶机械工业出版社, 1979:211-245.
[10]
CAO Hong-de. Fundamentals of plastic deformation mechanics and rolling theory[M]. Beijing: China Machine Press,1979:211-245.
[10]
CAO Hong-de. Fundamentals of plastic deformation mechanics and rolling theory[M]. Beijing: China Machine Press,1979:211-245.