Effect of heating rate on coating microstructure of galvanized hot-formed steel
LI Xue-tao1,2,3，ZHANG Jie1，JIANG She-ming1，ZHANG Qi-fu1， XU De-chao2,3，TENG Hua-xiang2,3
（1. National Engineering Laboratory of Advanced Coating Technology for Metals， Central Iron and Steel Research Institute，Beijing 100081， China 2. Research Institute of Technology， Shougang Group Co.， Ltd.， Beijing 100043， China 3. Beijing Key Laboratory of Green Recyclable Process for Iron and Steel Production Technology，Beijing 100043， China）
Abstract：The morphology and microstructure of zinc coating of the galvanized hot-formed steel，before and after hot treatment at different heating rate，were studied by scanning electron microscopy （SEM） with energy dispersive spectrometer system （EDS） and glow discharge optical emission spectroscopy （GDOES）. The results showed that the coating mainly consisted of Γ phase and α-Fe（Zn），with the heating rate reduced，the content of α-Fe（Zn） phase in the coating gradually increased，the content of Γ phase in the coating gradually reduced. When the heat rate was at 5-15 ℃/s，the coating was almost entirely α-Fe（Zn）. With heating rate reduced mass percent of Fe and thickness of alloyed coating increased and the distribution of Fe and Zn was more uniformity. When samples heated to 900 ℃ with 5-15 ℃/s heating rate，the generation of Liquid-Metal-Induced-Embrittlement（LMIE） cracks during hot stamping could be effectively reduced.
收稿日期: 2018-03-19
出版日期: 2018-11-20
引用本文:
李学涛 ，，张 杰，江社明，张启富，徐德超，滕华湘，. 加热速率对镀锌热成形钢镀层组织的影响[J]. , 2018, 53(11): 80-84.
LI Xue-tao，，，ZHANG Jie，JIANG She-ming，ZHANG Qi-fu， XU De-chao，，TENG Hua-xiang，. Effect of heating rate on coating microstructure of galvanized hot-formed steel. Iron and Steel, 2018, 53(11): 80-84.
Fan D W, Bruno C. Cooman D.. State-of-the-Knowledge on Coating Systems for Hot Stamped Parts[J]. Steel Research Int. 2012, 83( 5):412-433
[4]
Fan D W, Bruno C. Cooman D.. State-of-the-Knowledge on Coating Systems for Hot Stamped Parts[J]. Steel Research Int. 2012, 83( 5):412-433
[5]
Steinhoff K, Barbakedze N, Schupfer M, et al., Press Hardening-Form Galvanized UHSS to Body-in-White application[C]. Galvatech11, Genava, 2011
[5]
Steinhoff K, Barbakedze N, Schupfer M, et al., Press Hardening-Form Galvanized UHSS to Body-in-White application[C]. Galvatech11, Genava, 2011
[6]
C. W. Lee, D. W. Fan, et al. Galvanized Coating Evolution during Hot Stamping [A]. 8th International conference on zinc and zinc alloy coated steel sheet. Genova, Italy, 2011, 327-334.
[6]
C. W. Lee, D. W. Fan, et al. Galvanized Coating Evolution during Hot Stamping [A]. 8th International conference on zinc and zinc alloy coated steel sheet. Genova, Italy, 2011, 327-334.
[7]
Lee C W, Fan D W, Sohn I R, et al., Liquid-Metal-Induced Embrittlement of Zn-coated Hot Stamping Steel. Metallurgical and Materials Transactions A [J]. 2012,43(13):5122-5127
[7]
Lee C W, Fan D W, Sohn I R, et al., Liquid-Metal-Induced Embrittlement of Zn-coated Hot Stamping Steel. Metallurgical and Materials Transactions A [J]. 2012,43(13):5122-5127
[8]
Drillet P, Grigorieva R, Leuillier G, et al. Study of cracks propagation inside the steel on press hardened steel zinc based coatings[J]. La Metallurgia Italiana, 2013, 104(1):3-8.
[8]
Drillet P, Grigorieva R, Leuillier G, et al. Study of cracks propagation inside the steel on press hardened steel zinc based coatings[J]. La Metallurgia Italiana, 2013, 104(1):3-8.
[9]
Lee R S, Lin Y K, Chien T W. Experimental and theoretical studies on formability of 22MnB5 at elevated temperature by Gleeble simulator[J]. Procedia Engineering, 2014, 81: 1682-1688.
[9]
Lee R S, Lin Y K, Chien T W. Experimental and theoretical studies on formability of 22MnB5 at elevated temperature by Gleeble simulator[J]. Procedia Engineering, 2014, 81: 1682-1688.
2018, Vol. 53 