Effect of two-step slag making refining on sulfur and aluminum in C82DA steel
LIU Zong-hui1, QIN Feng-ting2, REN Jian-zhong3, ZHU Miao-yong1
1. School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China; 2. Department of Metallurgical and Chemical Engineering, Jiyuan Vocational and Technical College, Jiyuan 459000, Henan, China; 3. Technology Management Department, Henan Jiyuan Iron and Steel (Group) Co., Ltd., Jiyuan 459000, Henan, China
Abstract:In order to study the effect of technology on sulfur and aluminum in C82DA steel. The process of desulfurization and aluminum control of cord steel in LF was studied. The results show that with the decrease of refining basicity, the desulfurization rate becomeslower. When basicity is about 1.6, w((FetO)+(MnO)) in slag is about 1%, basically reaching the critical value of desulfurization.When basicity is about 1.2, sulfur recovery begins with refining time. The decrease of w([Als]) in molten steel gradually decreases with the decrease of basicity. When basicity is greater than 2.2, the decrease of w([Als]) is significant. When basicity is less than 1.6, the effect on w([Als]) is no longer obvious. The LF adopts two-step slag making process, high basicity desulfurization in the early stage and low basicity aluminum reduction in the later stage. When basicity is reduced from 2.2 to about 1.2, w([S]) and w([Als]) are controlled at the lower level of 0.011% and 0.001 6% respectively.
刘宗辉, 秦凤婷, 任建忠, 朱苗勇. LF两步造渣工艺对C82DA钢中硫和铝的影响[J]. 钢铁, 2020, 55(7): 78-84.
LIU Zong-hui, QIN Feng-ting, REN Jian-zhong, ZHU Miao-yong. Effect of two-step slag making refining on sulfur and aluminum in C82DA steel[J]. Iron and Steel, 2020, 55(7): 78-84.
[1] MinamideaT,HiragaN,Shibata T. Developments in steel cord wire rods[J]. Kobe Steel Engineering Reports,2000,50(3):31. [2] 汤伟, 杨俊, 刘青, 等. 高品质弹簧钢精炼过程氧化物夹杂的控制[J]. 中国冶金, 2020, 30(5): 17. (TANG Wei, YANG Jun, LIU Qing, et al. Control of oxide inclusions in high quality spring steel during refining process[J]. China Metallurgy, 2020, 30(5): 17.) [3] 王丙兴,朱伏先,王超,等. 氧化物冶金在大线能量焊接用钢中的应用[J]. 钢铁, 2019, 54(9): 12. (WANG Bing-xing,ZHU Fu-xian,WANG Chao,et al. Application of oxide metallurgy in high heat input welding steels[J]. Iron and Steel, 2019, 54(9): 12.) [4] 李西德,邓深,杨跃标,等. SWRH82B硬线钢CaO-Al2O3-SiO2系夹杂物塑性化控制的生产实践[J]. 中国冶金, 2018, 28(2): 61.(LI Xi-de,DENG Shen,YANG Yue-biao,et al. Productive practice of plastic deformation control of CaO-Al2O3-SiO2 inclusions in SWRH82B hard wire steel[J]. China Metallurgy, 2018, 28(2): 61.) [5] UjiieY,Kimura H. Production technology for steel bars and wire rods[J].Nippon teel Technical Report,1999,80(7):1. [6] BernardG,Ribound P V,Urbain G. Oxide inclusions plasticity[C]//La Revue de Metallurgie CTT. Mai:[s.n.],1981:421. [7] 辛彩萍,岳峰,蒋晨旭,等. 顶渣对帘线钢中夹杂物塑性化的控制[J]. 中国冶金, 2015, 25(4): 33. (XIN Cai-ping,YUE Feng,JIANG Chen-xu,et al. Controlling the plastic inclusions in tire cord steel by top slag[J]. China Metallurgy, 2015, 25(4): 33.) [8] Shinsho Y,Nozaki T,Sorimachi K I,et al. Inference of secondary steelmaking on occurrence of nonmetallic inclusions in high-carbon steel for tire cord[J]. Wire Journal International,1998(9):145. [9] 薛正良, 胡会军, 于学斌,等. 帘线钢82B精炼过程中的酸溶铝控制[J]. 炼钢, 2003(2):22. (XUE Zheng-liang, HU Hui-jun, YU Xue-bin,etal.Acid soluble Al control during refining of high carbon steel for tire cord[J].Steelmaking,2003(2):22.) [10] 何肖飞, 王新华, 陈书浩, 等. 低碱度低氧化铝精炼渣对帘线钢夹杂物控制[J]. 钢铁, 2014,49(6):30. (HE Xiao-fei, WANG Xin-hua, CHEGN Shu-hao, et al. Inclusion control of tire cord steel based on refining slag of low basicity and low alumina content[J]. Iron and Steel, 2014,49(6):30.) [11] 陈书浩,王新华,何肖飞,等. 帘线钢种酸溶铝含量的变化及其对夹杂物的影响[J]. 钢铁, 2011,46(10):42.(CHEN Shu-hao, WANG Xin-hua, HE Xiao-fei, et al. Effect of acid-soluble aluminum on inclusions in tyre cord steel[J]. Iron and Steel, 2011,46(10):42.) [12] Gatellier G, Gaye H. Inclusions control in low-aluminum steel[J]. La Revue de Metallurgie-CIT,1992,89(4):361. [13] YANG H L, YE J,WU X, et al. Optimum composition of CaO-SiO2-Al2O3-MgO slag for spring steel deoxidized by Si and Mn in production[J].Metallurgical and Materials Transactions B, 2016, 47(2):1435. [14] Park J S, Park J H. Effect of slag composition on the concentration of Al2O3 in the inclusions in Si-Mn-killed steel[J]. Metallurgical and Materials Transactions B, 2014, 45(3):953. [15] REN Y, ZHANG L, FANG W, et al. Effect of slag composition on inclusions in Si-deoxidized 18Cr-8Ni stainless steels[J].Metallurgical and Materials Transactions B, 2016, 47(2): 1024. [16] 张奚东, 孙泂. LF钢包脱硫试验[J]. 上海金属, 1997, 19(3):5.(ZHANG Xi-dong, SUN Jiong. The research on desulphurization in LF[J]. Shanghai Metals, 1997, 19(3):5.) [17] 川本正辛ほか.高速连铸用パウダの特性设计[J]. 鉄鋼,1994,80(3): 219. [18] 沢村信奉,大西泰,石光国男,ほか.Ca“フテツスイソヅエクシヨソ法” による溶钢处理技术[J]. 鉄鋼,1978,64(4): 116. [19] 黄希祜. 钢铁冶金原理[M]. 3版. 北京: 冶金工业出版社,2002.(HUANG Xi-hu, Principles of Steel Metallurgy[M]. 3 rd. Beijing: Metallurgical Industry Press,2002.) [20] Rachev I P. Solubility of BaS in BaO-BaF2 slag and the influence of FeOx, SiO2, Cr2O3, BaCl2, CaO and MgO on the sulfide capacities of this system[J]. Metallurgical Transactions B, 1992, 23B (4): 175. [21] 张明博.低钛高炉渣制备LF精炼渣及其脱硫性能与实验研究[J]. 北方钒钛,2018(3):5.(ZHANG Ming-bo.Preparation of LF refining slag from low titanium blast furnace slag and its desulfurization performance and experimental study[J]. Northern Vanadium Titanium, 2018(3):5.) [22] Mapelli C, Nicodemi W. Control of inclusion in a resulphurised steel[J]. Steel Research, 2000,71(5):161. [23] 陈家祥. 钢铁冶金学[M]. 北京:冶金工业出版社,1990.(CHEN Jia-xiang.Iron and Steel Metallurgy[M]. Beijing: Metallurgical Industry Press,1990.) [24] 陈家祥. 炼钢常用图表数据手册[M]. 北京:冶金工业出版社,1998.(CHEN Jia-xiang. Data Manual of Steel Making Charts[M]. Beijing: Metallurgical Industry Press,1998.) [25] 韩少伟, 郭靖, 陈兴润,等. 低碱度渣冶炼304不锈钢脱硫热力学和工业试验[J]. 钢铁,2016,53(6):47.(HAN Shao-wei, GUO Jing, CHEN Xing-run, et al. Thermodynamics of desulfurization of 304 stainless steel with low basicity slag[J]. Iron and Steel,2016,53(6):47.)