Dephosphorization influence factors in converter hot metal pretreatment
WANG Yu-mo1, TAO Lin2, GUO Hao-yu1, ZUO Da-wen1, WEI Jie1, YANG Shi-shan1
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2. Department of Materials Engineering, Henan Industrial School, Zhengzhou 450002, Henan, China
Abstract：Dephosphorization of hot metal pretreatment in the converter is nowadays playing an important role in the production of low or super low phosphorus steel grades. Based on the pretreatment dephosphorization converter practice in “duplex converter steelmaking” process in domestic iron and steel enterprises, experimental studies on dephosphorization influence factors in converter hot metal pretreatment were imitatively carried out by top addition of dephosphorization agent and immersed blowing of gaseous oxygen in SiC electric resistance furnace of molten pig iron. The effects of different hot metal temperature, initial silicon content in hot metal w(Si)i, slag basicity, oxygen supply (the ratio of gaseous oxygen and total oxygen), stirring strength, and fluorspar addition on dephosphorization efficiency are compared. The results showed that the ranking order of different factors affecting dephosphorization ratio is hot metal temperature＞w(Si)i＞oxygen supply＞slag basicity, stirring strength＞fluorspar addition,the appropriate process parameters are the hot metal temperature of 1 300 ℃, w(Si)iof 0.10%-0.26% or less than 0.30%, slag basicity of 2.9 to 3.0, oxygen supply of 50% solid oxygen or a few more, and with stronger stirring,and the dephosphorization agent is probable without fluorspar during hot metal dephosphorization pretreatment in the converter.
王雨墨, 陶林, 郭皓宇, 左大文, 韦杰, 杨世山. 转炉铁水预处理脱磷的影响因素[J]. 钢铁, 2020, 55(9): 29-37.
WANG Yu-mo, TAO Lin, GUO Hao-yu, ZUO Da-wen, WEI Jie, YANG Shi-shan. Dephosphorization influence factors in converter hot metal pretreatment[J]. Iron and Steel, 2020, 55(9): 29-37.
[1] Tsutomu Nozaki, Shuji Takeuchi, Osamu Haida, et al.Mechanism of hot metal dephosphorization by injection lime base fluxes with oxygen into bottom blown converter[J].Trans Iron Steel Inst,1983, 23(6): 513. [2] Kiminori Hajika, Matsuhide Aoki, Masaki Nitta.Quality improvement and energy saving by a newly-developed steelmaking process[C]//Steelmaking Conference Proceedings. Chicago: ISS-AIME, 1989: 325. [3] Matsuo T, Yamazaki I, Masuda S, et al.Development of new hot metal dephosphorization process in top and bottom blowing converter[C]//Steelmaking Conference Proceedings. Detroit: ISS-AIME, 1990: 115. [4] 康复,陆志新,蒋晓放,等.宝钢BRP技术的研究与开发[J].钢铁,2005,40(3):25. (KANG Fu,LU Zhi-xin,JIANG Xiao-fang,et al.Research and development of BRP technology at Baosteel[J].Iron and Steel, 2005, 40(3): 25.) [5] 刘皓铭,张进红,王硕明,等.京唐公司转炉双联冶炼工艺及技术指标[J].河北联合大学学报:自然科学版,2012,34(3):23. (LIU Hao-ming, ZHANG Jin-hong, WANG Shuo-ming, et al.Duplex melting process of converter and its analysis of technical index in Jingtang Company[J].Journal of Hebei United University:Natural Science, 2012, 34(3): 23.) [6] 栾花冰,王爽,孙振宁,等.鞍钢100 t顶吹转炉双联法脱磷工艺的研究[J].鞍钢技术,2018(1):26. (LUAN Hua-bing, WANG Shuang, SUN Zhen-ning, et al.Study on dephosphorization by duplex smelting process in 100 t top blowing converter in Ansteel[J].Angang Technology, 2018(1): 26.) [7] 万雪峰,曹东,李德刚,等.鞍钢转炉双渣深脱磷工艺研究与实践[J].钢铁,2012,47(6):32. (WAN Xue-feng, CAO Dong, LI De-gang, et al.Technical study and practice on deep dephosphorization with double slags in converter in Ansteel [J].Iron and Steel, 2012, 47(6): 32.) [8] Toshihiko Emi.Steelmaking technology for the last 100 years: Toward highly efficient mass production systems for high quality steels[J].ISIJ International, 2015, 55(1): 36. [9] 川崎正蔵,平橋英行,青木松秀,等.神戸製鉄所における転炉を中心とした精錬プロセスの改善[J].鉄と鋼,1990,76(11):1900. [10] 吉田克磨,山崎勲,戸崎泰之,等.2基の複合吹錬転炉を用いる溶銑予備処理,本吹錬による高効率精錬法の開発[J].鉄と鋼,1990,76(11):1871. [11] 宮田政樹,田村鉄平,松尾亨,等.粉CaO上吹き溶銑脱りん法の開発[J].まてりあ:日本金属学会会報,2012,51(1):16. [12] 岩崎正樹,松尾充高.製鋼技術開発の歩みと今後の展望[J].新日鉄技報,2011,391:88. [13] 小川雄司,矢野正孝,荒井雅之,等.脱りん脱炭連続処理プロセスの開発[J].まてりあ:日本金属学会会報,2014,53(3):107. [14] 潘秀兰,王艳红,梁慧智,等.国内外转炉脱磷炼钢工艺分析[J].世界钢铁,2010(1):19. (PAN Xiu-lan, WANG Yan-hong, LIANG Hui-zhi, et al.Analysis of converter dephosphorization steelmaking technology at home and abroad[J].World Iron and Steel, 2010(1): 19.) [15] 赵长亮,孙彦辉,袁天祥,等.转炉预脱磷与“全三脱”铁水少渣冶炼技术[J].钢铁,2016,51(5):28. (ZHAO Chang-liang, SUN Yan-hui, YAN Tian-xiang, et al.Dephosphorization pretreatment in LD converter and less-slag steelmaking process[J].Iron and Steel, 2016, 51(5): 28.) [16] 曾兴富,方宇荣,黄标彩,等.复吹转炉两炉双联冶炼65钢工艺研究与应用[J].炼钢,2014,30(3):5.(ZENG Xing-fu, FANG Yu-rong, HUANG Biao-cai, et al.Research and application on 65 steel smelting with duplex melting process in two converters[J].Steelmaking, 2014, 30(3): 5.)
2020, Vol. 55 