Mixed crystal of austenite grain size in track pins 1E1158M steel
WANG Huan1, HU Jia-li1, ZHANG Chao-lei1, LI Jian2, MIAO Hong-sheng3
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2. School of Mechanical Engineering, Qinghai University, Xining 810016, Qinghai, China; 3. Qinghai Special Steel Engineering Technology Research Center, Xining Special Steel Co., Ltd., Xining 810005, Qinghai, China
Abstract:The mixed crystal of austenite grain size in track pins 1E1158M steel was investigated at different finishing temperatures,then the grain size and it's microstructure were adopted to study the effect of different finishing temperatures by thermal simulation test,quantitative analysis of microstructure and intercept method. The results show that the abnormal grain growth temperature of hot-rolled and normal-fired microstructures is both 850 ℃,and the finishing rolling temperature has an effect on mixed crystal degree. When the finish rolling temperature is 850 ℃,the austenite grains are partially recrystallized at the end of rolling,and the degree of mixed crystals is serious. As the finishing temperature increases,the inhomogeneity of the intrinsic grain size decreases and the recommended finishing temperature is 1 000 ℃.
[1] 邓安华. 金属材料简明辞典[M]. 北京:冶金工业出版社,1992. (DENG An-hua. Concise Dictionary of Metallic Materials[M]. Beijing:Metallurgical Industry Press,1992.) [2] 关小军,凤佩华. 终轧温度对ELC-BH板组织和性能的影响[J]. 工程科学学报,1995,17(3):249. (GUAN Xiao-jun,FENG Pei-hua. Effects of hot rolling finishing temperature on the microstructure and properties of ELC-BH sheet[J]. Chinese Journal of Engineering,1995,17(3):249.) [3] YANG H L,XU G,WANG L,et al. A study of growth of austenite grains in a steel microalloyed with Ti and Nb[J]. Metal Science and Heat Treatment. 2017,59(1/2):8. [4] Lin Chi-kang,Su Yen-hao,Hwang Weng-sing,et al. On pinning effect of austenite grain growth in Mg-containing low-carbon steel[J]. Materials Science and Technology,2018,34(5):596. [5] 汪杨鑫,赵秀明,毛向阳,等. SCr420H钢奥氏体晶粒长大动力学[J]. 钢铁,2018,53(7):86.(WANG Yang-xin,ZHAO Xiu-ming,MAO Xiang-yang,et al. Kinetics of austenite grain growth in SCr420H steel[J]. Iron and Steel,2018,53(7):86.) [6] 莫伟灵. 热加工工艺对奥氏体本质晶粒度的影响[J]. 特殊钢,1980(2):96.(MO Wei-ling. Effect of thermal processing on the austenite grain size[J].Special Steel,1980(2):96.) [7] 吴志方,况嘉伦,石俊,等. CSP工艺生产热轧钢板显微组织混晶的产生和消除[J]. 热加工工艺,2013,42(11):105. (WU Zhi-fang,KUANG Jia-lun,SHI Jun,et al. Producing and eliminating of mixed grain microstructure of hot rolled strip in CSP process[J]. Hot Working Technology,2013,42(11):105.) [8] 董芳. 锻造及预备热处理工艺对18Cr2 Ni4 WA锻件本质晶粒度的影响[J]. 金属加工:热加工,2017(11):61. (DONG Fang. Effect of forging and preliminary heat treatment on the inherent grain size of 18Cr2 Ni4 WA forgings[J]. MW Metal Forming,2017(11):61.) [9] 陈斌,白丽杨,张宇光,等. 卷取温度对IF钢组织性能影响规律[J]. 中国冶金,2019,29(8):34. (CHEN Bin,BAI Li-yang,ZHANG Yu-guang,et al. Effects of coiling temperature on microstructure and properties of IF steel[J]. China Metallurgy,2019,29(8):34.) [10] 蔡仲卫. 履带销轴用1E1158M钢的生产实践[J]. 河北冶金,2012(6):39. (CAI Zhong-wei. Production practice of 1E1158M steel for pin shaft of caterpillar[J]. Hebei Metallurgy,2012(6):39.) [11] 徐尚呈,周立新,张志成,等. 热处理工艺对SAE4320钢奥氏体晶粒度的影响[J]. 金属热处理,2014,39(11):111.(XU Shang-cheng,ZHOU Li-xin,ZHANG Zhi-cheng,et al. Effect of heat treatment on austenite grain size of SAE4320 steel[J]. Heat Treatment of Metals,2014,39(11):111.) [12] 毛卫民,赵新兵. 金属的再结晶与晶粒长大[M]. 北京:冶金工业出版社,1994. (MAO Wei-min,ZHAO Xin-bing. Metal Recrystallization and Grain Growth[M]. Beijing:Metallurgical Industry Press,1994.) [13] 常铁军,马茂元. 钢的混晶程度评价方法探讨[J]. 理化检验:物理分册,1989(1):41. (CHANG Tie-jun,MA Mao-yuan. Discussion on evaluation method of mixed crystal degree of steel[J]. Physical Testing and Chemical Analysis Part A:Physical Testing,1989(1):41.) [14] Pous-Romero H,Lonardelli I,Cogswell D,et al. Austenite grain growth in a nuclear pressure vessel steel[J]. Materials Science and Engineering,2013(567):72. [15] 徐厚训,栗牧怀. 对结构钢(40CrNiMoA)奥氏体本质晶粒度影响因素的探讨[J]. 材料工程,1983(2):16. (XU Hou-xun,LI Mu-huai. Discussion on the factors affecting the austenite grain size of structural steel(40CrNiMoA)[J]. Journal of Materials Engineering,1983(2):16.) [16] 赵勇桃,刘宗昌,王玉峰. 34CrNi3MoV钢的混晶及消除措施[J]. 金属热处理,2007,32(5):75. (ZHAO Yong-tao,LIU Zong-chang,WANG Yu-feng. Mixed grain and elimination measure of 34CrNi3MoV steel[J]. Heat Treatment of Metals,2007,32(5):75.)