钢渣中磷分离及回收的研究现状和发展趋势

doi:10.13228/j.boyuan.issn0449-749x.20200147

摘要
图/表
参考文献
相关文章 (15)

全文: PDF (2521 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要中国的钢渣产量巨大,但是钢渣的综合利用率较低,造成了严重的资源浪费和环境负担。钢渣中磷的分离与回收是实现钢渣高效资源化利用的关键所在,对开发新的磷资源和建立“无废渣”炼钢流程具有重要意义。首先分析了钢渣中磷的分布状态,总结了目前提出的从钢渣中分离和回收磷的主要方法及其技术特点,并着重介绍了利用选择性浸出从钢渣中直接提取磷酸盐产品的新技术及其研究进展,分析了选择性浸出的原理和实现钢渣循环利用的冶金工艺流程,讨论了其优缺点,最后对未来钢渣资源化利用的发展提出了建议和展望。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杜传明
	于耀辉
	袁磊
	于景坤

关键词 ：钢渣, 磷回收, 资源化利用, 浸出, 炼钢

Abstract：The productivity of steelmaking slag in China is huge,while its comprehensive utilization ratio is lower,resulting in severe resources waste and environmental burden. The separation and recovery of phosphorus from steelmaking slag is the key technology to achieve its efficient resource utilization,which is significant to the development of new phosphate resources and the establishment of a waste-free steelmaking process. Firstly,the distribution status of phosphorus in steelmaking slag was analyzed,and the major methods of phosphorus recovery from steelmaking slag proposed and their technical characteristics were summarized. A novel method of direct extraction of phosphate products from steelmaking slag by selective leaching and its research progress was introduced. The principle of selective leaching and a process of realizing the recycling of steelmaking slag was analyzed. The advantages and disadvantages of this method were discussed,and some suggestions for the future development of resource utilization of steelmaking slag were finally proposed.

Key words： steelmaking slag phosphorus recovery resource utilization leaching steelmaking

收稿日期: 2020-03-30

引用本文:

杜传明, 于耀辉, 袁磊, 于景坤. 钢渣中磷分离及回收的研究现状和发展趋势[J]. 钢铁, 2020, 55(12): 1-9. DU Chuan-ming, YU Yao-hui, YUAN Lei, YU Jing-kun. Research status and development trend of phosphorus separation and recovery from steelmaking slag[J]. Iron and Steel, 2020, 55(12): 1-9.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/10.13228/j.boyuan.issn0449-749x.20200147 或 http://www.chinamet.cn/Jweb_gt/CN/Y2020/V55/I12/1

[1] 殳黎平,吴洪义. 宁钢钢渣资源化利用的创新与实践[J]. 冶金能源,2019,38(3):46.(SHU Li-ping,WU Hong-yi. Innovation and practice of recycling utilization of steel slag in Ningbo steel[J]. Energy for Metallurgical Industry,2019,38(3):46.)
[2] 黄丽,徐杰. 浅谈钢渣热闷的现状及发展[J]. 工业加热,2016,45(4):68.(HUANG Li,XU Jie. The status and development of steel slag hot stew method[J]. Industrial Heating,2016,45(4):68.)
[3] 刘胜涛,王凯,朱利. 首秦资源类固废综合回收利用实践[J]. 中国冶金,2018,28(11):73.(LIU Sheng-tao,WANG Kai,ZHU Li. Practice on comprehensive recycling of solid waste resources in Shouqin Company[J]. China Metallurgy,2018,28(11):73.)
[4] 张作顺,徐利华,余广炜,等. 国内钢渣处理方法及资源化利用的研究进展[C]//2010年全国能源环保生产技术会议.九江:中国金属学会,2010:6.(ZHANG Zuo-shun,XU Li-hua,YU Guang-wei,et al. Development of steel slag's processing technology and utilization in China[C]//Proceedings of the 2010 National Energy Environmental Protection Production Technology Conference. Jiujiang:The Chinese Society for Metals,2010:6.)
[5] 崔虹旭,陈庆武,申莹莹,等. 转炉钢渣磷富集与应用的技术研究[J]. 中国冶金,2010,20(3):35.(CUI Hong-xu,CHEN Qing-wu,SHEN Ying-ying,et al. Technology research on phosphorus enrichment and application of converter steel slag[J]. China Metallurgy,2010,20(3):35.)
[6] 李鸿江,刘清,赵由才. 冶金过程固体废物处理与资源化[M]. 北京:冶金工业出版社,2007.(LI Hong-jiang,LIU Qing,ZHAO You-cai. Solid Waste Treatment and Recycling in Metallurgical Process[M]. Beijing:Metallurgical Industry Press,2007.)
[7] 林晨明,彭呈祥,游伟毕. 转炉钢渣代替石灰石作高炉熔剂[J]. 炼铁,1986(1):62.(LIN Chen-ming,PENG Cheng-xiang,YOU Wei-bi. Application of converter slag as blast furnace flux and replacement of limestone[J]. Ironmaking,1986(1):62.)
[8] 韩光烈,吴炳炎,肖泽勋,等. 利用平炉钢渣作铁水脱硫剂[J]. 钢铁,1989,24(10):58.(HAN Guang-lie,WU Bing-yan, XIAO Ze-xun,et al. A synthetic desulphurizer by use of open hearth tapping slag[J]. Iron and Steel,1989,24(10):58.)
[9] 张劲,陆文雄,王雪,等. 钢渣的利用及其应用研究进展[J]. 粉煤灰综合利用,2014(2):46.(ZHANG Jin,LU Wen-xiong,WANG Xue,et al. Study on comprehensive utilization of steel slag and its development trend[J]. Fly Ash Comp Rehensive Utilization,2014(2):46.)
[10] 韩凤光,邱海雨,聂慧远,等. 梅山烧结配加转炉钢渣的试验研究[J]. 烧结球团,2006(5):15.(HAN Feng-guang,QIU Hai-yu,NIE Hui-yuan,et al. Experimental study on adding converter steel slag to Meishan sintering[J]. Sintering and Pelletizing,2006(5):15.)
[11] Kazuyo M,Elizabeth W,Keisuke N,et al. Hidden phosphorus flows related with non-agriculture industrial activities:A focus on steelmaking and metal surface treatment[J]. Resources,Conservation and Recycling,2015,105:360.
[12] Du C M,Gao X,Kim S,et al. Improving the dissolution of phosphorus from 2CaO·SiO₂-3CaO·P₂O₅ solid solution in aqueous solution[C]//Proceedings of the 10th International Conference on Molten Slags,Fluxes and Salts. Seattle, Washington, USA:TMS,2016:5.
[13] 杨金星,吕宁宁,苏畅,等. 转炉钢渣中磷资源回收利用的研究进展[J]. 应用化工,2019,48(6):1440.(YANG Jin-xing,L Ning-ning,SU Chang,et al. Research progress on the recycling of phosphorus resource from converter steelmaking slag[J]. Applied Chemical Industry,2019,48(6):1440.)
[14] Fukagai S,Hamano T,Tsukihashi F. Formation reaction of phosphate compound in multi phase flux at 1 573 K[J]. ISIJ International,2007,47(1):187.
[15] 梁强,曾加庆,齐渊洪. 含磷炉渣处理技术的回顾与展望[J]. 钢铁,2015,50(1):69.(LIANG Qiang,ZENG Jia-qing,QI Yuan-hong. Retrospect and prospect of the technology of phosphatic slag treatment[J]. Iron and Steel,2015,50(1):69.)
[16] Ono H,Inagaki A,Masuz T,et al. Removal of phosphorus separation of dicalcium from LD converter slag by floating silicate during solidification[J]. Tetsu-to-Hagané,1980,66(9):1317.
[17] 李辽沙,于学峰,余亮,等. 转炉钢渣中磷元素的分布[J]. 中国冶金,2007,17(1):42.(LI Liao-sha,YU Xue-feng,YU Liang,et al. Phosphorus distribution in converter slag[J]. China Metallurgy,2007,17(1):42.)
[18] Kimihisa I,Masakazu Y,Sano N. Phosphorus distribution between solid 2CaO·SiO₂ and molten CaO-SiO₂-FeO-Fe₂O₃ slags[J]. Tetsu-to-Hagané,1982,68(2):342.
[19] Shimauchi K,Kitamura S,Shibata H. Distribution of P₂O₅ between solid dicalcium silicate and liquid phases in CaO-SiO₂-Fe₂O₃ system[J]. ISIJ International,2009,49(4):505.
[20] Yokoyama K,Kubo H,Mori K,et al. Separation and recovery of phosphorus from steelmaking slags with the aid of a strong magnetic field[J]. ISIJ International,2007,47(10):1541.
[21] Kubo H,Matsbuae-Yokoyama K,Nagasaka T. Magnetic separation of phosphorus enriched phase from multiphase dephosphorization slag[J]. ISIJ International,2010,50(1):59.
[22] LIN L,BAO Y P,WANG M,et al. Influence of SiO₂ modification on phosphorus enrichment in P bearing steelmaking slag[J]. Ironmaking and Steelmaking,2013,40(7):521.
[23] DIAO J,XIE B,WANG Y,et al. Recovery of phosphorus from dephosphorization slag produced by duplex high phosphorus hot metal refining[J]. ISIJ International,2012,52(6):955.
[24] LI C,GAO J T,WANG F Q,et al. Enriching Fe-bearing and P-bearing phases from steelmaking slag melt by super gravity[J]. Ironmaking and Steelmaking,2018,45(1):44.
[25] LI C,GAO J T,GUO Z C. Isothermal enrichment of P-concentrating phase from CaO-SiO₂-FeO-MgO-P₂O₅ melt with super gravity[J]. ISIJ International,2016,56(5):759.
[26] LI C,GAO J T,GUO Z C. Separation of phosphorus- and iron-enriched phase from CaO-SiO₂-FeO-MgO-P₂O₅ melt with super gravity[J]. Metallurgical and Materials Transactions B,2016,47(3):1516.
[27] 王玉红,郭锴,陈建峰,等. 超重力技术及其应用[J]. 金属矿山,1999(4):25.(WANG Yu-hong,GUO Kai,CHEN Jian-feng,et al. Higee technology and its application[J]. Metal Mine,1999(4):25.)
[28] Tanaka T,Hara S,Oguni R,et al. Application of capillarity of solid CaO to dephosphorization of hot metals[J]. ISIJ International,2001,41:70.
[29] Miki T,Kaneko S. Separation of FeO and P₂O₅ from steelmaking slag utilizing capillary action[J]. ISIJ International,2015,55(1):142.
[30] Li H J,Suito H,Tokuda M. Thermodynamic analysis of slag recycling using a slag regenerator[J]. ISIJ International,1995,35(9):1079.
[31] Ishikawa M. Reduction behaviors of hot metal dephosphorization slag in a slag regenerator[J]. ISIJ International,2006,46(4):530
[32] JIANG M,CUI Y,WANG D,et al. Effect of modification treatment for reduction of dephosphorization slag in hot metal bath[J]. Journal of Iron and Steel Research,International,2013,20(1):1.
[33] Morita K,Guo M,Miyazaki Y,et al. The heating characteristics of CaO-SiO₂-Fe_tO system slags under microwave irradiation[J]. ISIJ International,2001,41(7):716.
[34] Morita K,Guo M,Oka N,et al. Resurrection of the iron and phosphorus resource in steel-making slag[J]. Journal of Material Cycles and Waste Management,2002,4(2):93.
[35] 吕岩,张猛,艾立群,等. 微波处理碳热还原转炉钢渣的脱磷实验研究[J]. 炼钢,2010,26(4):70.(L Yan,ZHANG Meng,AI Li-qun,et al. Experimental research on dephosphorization of converter slag by microwave heating and carbon thermal reduction[J]. Steelmaking,2010,26(4):70.)
[36] 艾立群,张彦龙,朱祎姮. 微波碳热还原转炉钢渣脱磷研究[J]. 钢铁钒钛,2015,36(6):63.(AI Li-qun,ZHANG Yan-long,ZHU Yi-heng. Research on carbothermic reduction for dephosphorization from converter slag by microwave heating[J]. Iron Steel Vanadium Titanium,2015,36(6):63.)
[37] Marhual N P,Pradhan N,Mohanta N C,et al. Dephosphorization of LD slag by phosphorus solubilising bacteria[J]. International Biodeterioration and Biodegradation,2011,65(3):404.
[38] Sugiyama S,Shinomiya I,Kitora R,et al. Recovery and enrichment of phosphorus from the nitric acid extract of dephosphorization slag[J]. Journal of Chemical Engineering of Japan,2014,47(6):483.
[39] DIAO J,JIANG L,WANG Y H,et al. P₂O₅ solubility of dephosphorization slag in citric acid[J]. Phosphorus,Sulfur,and Silicon and the Related Elements,2015,190:387.
[40] LIN L,BAO Y P,WANG M,et al. P₂O₅ solubility behavior and resource utilization of P-bearing slag[J]. ISIJ International,2014,54(12):2746.
[41] 杨金星,笪亚玲,吕宁宁,等. 用草酸从转炉钢渣中溶解磷的试验研究[J]. 湿法冶金,2018,37(3):228.(YANG Jin-xing,DA Ya-ling,L Ning-ning,et al. Experimental study on the dissolution of phosphorus from converter steel slag by oxalic acid[J]. Hydrometallurgy of China,2018,37(3):228.)
[42] QIAO Y,DIAO J,LIU X,et al. Dephosphorization of steelmaking slag by leaching with acidic aqueous solution[J]. JOM,2016,68(9):2511.
[43] Teratoko T,Maruoka N,Shibata H,et al. Dissolution behavior of dicalcium silicate and tricalcium phosphate solid solution and other phases of steelmaking slag in an aqueous solution[J]. High Temperature Materials and Processes,2012,31:329.
[44] Numata M,Maruoka N,Kim S,et al. Fundamental experiment to extract phosphorous selectively from steelmaking slag by leaching[J]. ISIJ International,2014,54(8):1983.
[45] Du C M,Gao X,Ueda S,et al. Effects of cooling rate and acid on extracting soluble phosphorus from slag with high P₂O₅ content by selective leaching[J]. ISIJ International,2017,57(3):487.
[46] Du C M,Gao X,Ueda S,et al. Effect of Na₂O addition on phosphorus dissolution from steelmaking slag with high P₂O₅ content[J]. Journal of Sustainable Metallurgy,2017,3(4):671.
[47] Du C M,Gao X,Ueda S,et al. Effect of slag composition on the dissolution of P from steelmaking slag by selective leaching[J]. ISIJ International,2018,58(9):1659.
[48] Du C M,Gao X,Ueda S,et al. Effect of Fe²⁺/TFe ratio on the dissolution behavior of P from steelmaking slag with high P₂O₅ content[J]. Journal of Sustainable Metallurgy,2018,4(4):443.
[49] Du C M,Gao X,Ueda S,et al. Distribution of P₂O₅ and Na₂O between solid solution and liquid phase in the CaO-SiO₂-Fe₂O₃-P₂O₅-Na₂O slag system with high P₂O₅ content[J]. Metallurgical and Materials Transactions B,2018,49(1):181.
[50] DU C M,L N N,SU C,et al. Distribution of P₂O₅ between solid solution and liquid phase in dephosphorization slag of CaO-SiO₂-FeO-P₂O₅-Na₂O system[J]. Journal of Iron and Steel Research,International,2019,26(11):1162.
[51] Du C M,Gao X,Ueda S,et al. Optimum conditions for phosphorus recovery from steelmaking slag with high P₂O₅ content by selective leaching[J]. ISIJ International,2018,58(5):860.
[52] Du C M,Gao X,Ueda S,et al. Recovery of phosphorus from modified steelmaking slag with high P₂O₅ content via leaching and precipitation[J]. ISIJ International,2018,58(5):833.