Fatigue properties of hot-rolled medium manganese steel treated by ART-annealing
ZHOU Feng-luan1,2,3, WANG Cun-yu1, CAO Wen-quan1, DONG Han1,4
1. Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China; 2. Testing Center, NCS Testing Technology Co.,Ltd., Beijing 100081, China; 3. Department of Technology, AVIC Touchstone Testing Innovation Cooperation, Langfang 065300, Hebei, China; 4. School of Material Science and Engineering, Shanghai University, Shanghai 200444, China
Abstract:In order to study the effect of cyclic loading on the microstructure and mechanical properties of austenitic steel,the fatigue properties of manganese steel in reverse phase transformation were studied. The microstructure was characterized by SEM,EBSD,XRD,etc.,and uniaxial tensile test was used to characterized the mechanical properties before and after fatigue. The research results show that under the test condition of stress ratio R=-1,the median fatigue limit of reverse phase transformation manganese steel is 378 MPa,and the ratio of fatigue limit to tensile strength σ-1/Rm=0.48. Medium manganese steel is ultrafine grain size characteristics are conducive to hindering secondary fatigue crack growth,and the transformation behavior of metastable austenite is greatly affected by the stress amplitude. Under the stress level of the median fatigue limit,metastable austenite and uniaxial tensile properties are subject to cyclic loading has little effect.
周峰峦, 王存宇, 曹文全, 董瀚. 热轧逆相变退火中锰钢的疲劳性能[J]. 钢铁, 2020, 55(12): 87-91.
ZHOU Feng-luan, WANG Cun-yu, CAO Wen-quan, DONG Han. Fatigue properties of hot-rolled medium manganese steel treated by ART-annealing[J]. Iron and Steel, 2020, 55(12): 87-91.
[1] 王存宇,杨洁,常颖,等.先进高强度汽车钢的发展趋势与挑战[J]. 钢铁,2019,54(2):1(WANG Cun-yu,YANG Jie,CHANG Ying, et al. Development trend and challenge of advanced high strength automobile steels[J]. Iron and Steel,2019,54(2):1.) [2] 赵晓丽,张永健,惠卫军,等. 不同轧制及退火处理0.1C-5Mn中锰钢的氢脆敏感性[J]. 钢铁,2019,54(11):69. (ZHAO Xiao-li,ZHANG Yong-jian,HUI Wei-jun,et al. Hydrogen embrittlement of intercritically annealed medium-Mn steel (0.1C-5Mn) under different rolling conditions[J]. Iron and Steel,2019,54(11):69.) [3] 蒋爱娟,祝贞凤,高千林,等. 淬火制度对Q&P钢微观组织和力学性能的影响[J]. 钢铁,2019,54(10):80. (JIANG Ai-juan,ZHU Zhen-feng,GAO Qian-lin,et al. Influence of quenching process on microstructure and mechanical properties of Q&P steel[J]. Iron and Steel,2019,54(10):80.) [4] 王存宇,常颖,周峰峦,等. 高强度高塑性第三代汽车钢M3组织调控理论与技术[J]. 金属学报,2020,56(4):400 (WANG Cun-yu,CHANG Ying,ZHOU Feng-luan,et al. M3 microstructure control theory and technology of the third-generation automotive steels with high strength and high ductility[J]. Acta Metallurgica Sinica,2020,56(4):400.) [5] 邓泽,张立峰,杨文,等. Fe-22Mn-5Al-0.38C-0.55Si合金的微观组织及力学性能[J]. 中国冶金,2018,28(11):46. (DENG Ze,ZHANG Li-feng,YANG Wen,et al. Microstructure and mechanical properties of Fe-22Mn-5Al-0.38C-0.55Si alloy[J]. China Metallurgy,2018,28(11):46.) [6] 邵成伟,王俊涛,赵晓丽,等. 两相区退火处理含铝中锰钢的组织和力学性能[J]. 钢铁,2020,55(5):87. (SHAO Cheng-wei,WANG Jun-tao,ZHAO Xiao-li,et al. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel,2020,55(5):87.) [7] SHI J,SUN X J,WANG M Q,et al. Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large-fractioned metastable austenite[J]. Scripta Materialia,2010,63:815. [8] 王晓晖,康健,李振垒,等. 等温时间对低硅含铝热轧TRIP钢组织性能的影响[J]. 钢铁,2019,54(5):54. (WANG Xiao-hui,KANG Jian,LI Zhen-lei,et al. Effect of isothermal time on microstructures and mechanical properties in hot rolled TRIP steels with low Si and more Al[J]. Iron and Steel,2019,54(5):54.) [9] WANG C Y,CHANG Y,YANG J,et al. Work hardening behavior and stability of retained austenite for quenched and partitioned steels[J]. Journal of Iron and Steel Research,International,2016,23(2):130. [10] Koh-ichi Sugimoto,Tsutomu Iida,Jyunya Sakaguchi,et al. Retained austenite characteristics and tensile properties in a TRIP type bainitic sheet steel[J]. ISIJ International,2000,40(9):902. [11] N H van Dijk A M Butt,Zhao L,S Van der Zwaag,et.al. Thermal stability of retained austenite in TRIP steels studied by synchrotron X-ray diffraction during cooling[J]. Acta Materialia,2005,53(20):5439. [12] HUO C Y,GAO H L. Strain-induced martensitic transformation in fatigue crack tip zone for a high strength steel[J]. Materials Characterization,2005,55(1):12. [13] Yan B,Urban D. Characterization of fatigue and crash performance of new generation high strength steels for automotive applications[J]. Final Report of American Iron and Steel Institute,2003,4:52. [14] Abareshi M,Emadoddin E. Effect of retained austenite characteristics on fatigue behavior and tensile properties of transformation induced plasticity steel[J]. Materials and Design,2011,32(10):5099. [15] Haidemenopoulos G N,Kermanidis A T,Malliaros C. On the austenite stability on high cycle fatigue of TRIP 700 steel[J]. Materials Science and Engineering A,2013,573:7. [16] Koh-ichi Sugimoto,Junji Tsuruta,Sung-Moo Song. Fatigue strength of formable ultra high-strength TRIP-aided steels with bainitic ferrite matrix[J]. Key Engineering Materials,2007,345/346:247. [17] HU Zhi-gang,ZHU Ping,MENG Jin,et al. Experimental comparison of fatigue characterizations between TRIP and DP steel[J]. Advanceed Materials Research,2010,97-101:671. [18] Hilditch,Timothy B Timokhina,Ilana B Robertson,et al. Microstructural analysis of pre-strained TRIP steel after fatigue testing[C]//International Conference on New Developments in Advanced High-Strength Sheet Steels. Orlando:Fla,2008:295. [19] 班丽丽. 中碳Si-Mn系高强度TRIP钢高周疲劳破坏行为研究[D]. 昆明:昆明理工大学,2008. (BAN Li-li. Research on High Cycle Fatigue Failure Behavior of Medium Carbon Si-Mn High Strength TRIP Steel[D]. Kunming:Kunming University of Science and Technology,2008.) [20] 苏钰,张梅,符仁钰,等. 低碳低硅600 MPa级TRIP-SH钢的疲劳性能研究[J]. 金属热处理,2008,33(8):25. (SU Yu,ZHANG Mei,FU Ren-yu,et al. Study on fatigue properties of low carbon and low silicon 600 MPa grade TRIP-SH steel [J]. Metal Heat Treatment,2008,33(8):25.) [21] 韩伟钢,韩顺,厉勇,等. 大型客机用300M钢疲劳破坏行为[J]. 钢铁,2017,52(10):83.(HAN Wei-gang,HAN Shun,LI Yong,et al. Behavior of fatigue fracture of 300M steel for large passenger aircraft[J]. Iron and Steel,2017,52(10):83.) [22] 王存宇. 第三代汽车钢工业生产关键技术研究[R]. 太原:太原钢铁(集团)有限公司,2017. (WANG Cun-yu. Investigation on Key Technology of the Third Generation Automobile Steel[R]. Taiyuan:TISCO,2017.)