Effect of nickel interlayer thickness on characteristics of 316L/EH40 composite interface
JIN He-rong1,2, ZHANG Zhao-rui3, HAN Min-feng3, YI Ya-li3, ZHAO Ding-xuan3
1. Key Laboratory of Advanced Forging and Stamping Technology and Science of Ministry of National Education, Yanshan University, Qinhuangdao 066004, Hebei, China; 2. Parallel Robot and Mechatronic System Laboratory of Hebei Province, Yanshan University, Qinhuangdao 066004, Hebei, China; 3. School of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, Hebei, China
Abstract：In order to explore the influence of interlayer thickness on the microstructure and properties of composite materials, four kinds of composite samples with different thickness of Ni interlayer (0.05, 0.10, 0.15, 0.20 mm) were set up. Hot compression test of samples with the same thickness ratio was carried out under the same conditions. The microstructure of the interface after compression was analyzed by metallographic microanalysis technology, and the diffusion of elements at the interface was analyzed by energy spectrum analysis. The mechanical properties of the interface were tested by microhardness test and the tensile properties of the material were tested by tensile test. The results show that with the increase of the thickness of the nickel interlayer, the bonding interface became smooth, and the barrier effect of diffusion of carbon, chromium and other elements became better. When the thickness reached a certain degree, the mechanical properties of plate decreased with the increase of interlayer thickness. Besides, the hardness value near the 0.05 mm Ni layer appeared obvious mutation, and the change trend of hardness value near the other three thicknesses of interlayer was almost the same. Among them, the diffusion behavior of elements could be block well by the 0.10 mm thick Ni interlayer, and the excellent tensile property(512 MPa) at the interface of materials could also be ensured.
金贺荣, 张钊瑞, 韩民峰, 宜亚丽, 赵丁选. 镍夹层厚度对316L/EH40复合界面特性影响[J]. 钢铁, 2021, 56(3): 154-163.
JIN He-rong, ZHANG Zhao-rui, HAN Min-feng, YI Ya-li, ZHAO Ding-xuan. Effect of nickel interlayer thickness on characteristics of 316L/EH40 composite interface[J]. Iron and Steel, 2021, 56(3): 154-163.
[1] 于涛, 井玉安, 张亚樵, 等. 不锈钢复合板界面组织形貌[J]. 钢铁,2018, 53(11): 63.(YU Tao, JING Yu-an, ZHANG Ya-qiao, et al. Interface morphology of stainless steel clad plate[J]. Iron and Steel,2018, 53(11): 63.) [2] 查春和, 戴燕红, 杨梅梅. 我国不锈钢复合板材的制造技术及应用[J]. 轧钢,2018, 35(6): 55.(ZHA Chun-he, DAI Yan-hong, YANG Mei-mei. Manufacturing technology and application of stainless steel composite plates in China[J]. Steel Rolling,2018, 35(6): 55. [3] ZENG X Y, WANG Y X, LI X Q, et al. Effect of inert gas-shielding on the interface and mechanical properties of Mg/Al explosive welding composite plate[J]. Journal of Manufacturing Processes, 2019, 45: 166. [4] 刘晓翠, 张转转, 吴耐, 等. 高强耐候钢加工成形性能分析及改善措施[J]. 中国冶金,2020, 30(8): 56.(LIU Xiao-cui, ZHANG Zhuan-zhuan, WU Nai, et al. Formability analysis and improvement measures of high strength weathering steel[J]. China Metallurgy,2020, 30(8): 56.) [5] 李晋. 热轧对06Cr13/Q345R爆炸复合板界面微观组织和元素扩散的影响[J]. 热加工工艺,2018, 47(17): 51.(LI Jin. The effect of hot rolling on the microstructure and element diffusion of 06Cr13/Q345R explosive composite plates[J]. Hot Processing Technology,2018, 47(17): 51.) [6] 金贺荣, 韩民峰, 段昌新. 压下率对316L/EH40复合板界面微观形貌的影响[J]. 钢铁,2019, 54(12): 62.(JIN He-rong, HAN Min-feng, DUAN Chang-xin. The effect of reduction ratio on interfacial morphology of 316L/EH40 composite plate[J]. Iron and Steel,2019, 54(12): 62.) [7] 田广民, 李选明, 赵永庆, 等. 层状金属复合材料加工技术研究现状[J]. 中国材料进展,2013, 32(11): 696.(TIAN Guang-min, LI Xuan-ming, ZHAO Yong-qing, et al. Research status of layered metal composite processing technology[J]. Progress in Materials in China, 2013, 32(11): 696.) [8] 张侠洲, 王凤会, 陈延清, 等. 焊接材料对双金属复合板焊接接头性能的影响[J]. 中国冶金, 2018, 28(7): 31.(ZHANG Xia-zhou, WANG Feng-hui, CHEN Yan-qing, et al. The effect of welding materials on the properties of bimetal composite plate welded joints[J]. China Metallurgy,2018, 28(7): 31.) [9] 刘宝龙, 张慧芳, 肖振兴, 等. 316L/Q345R热轧复合板界面组织演变及性能[J]. 钢铁,2017, 52(5): 72.(LIU Bao-long, ZHANG Hui-fang, XIAO Zhen-xing, et al. Interface evolution and properties of 316L/Q345R hot-rolled composite sheet[J]. Iron and Steel,2017, 52(5): 72.) [10] 田世伟, 江海涛, 刘继雄, 等.钛钢复合板双金属的流变行为及轧制制备[J]. 材料导报, 2019, 33(24): 414.(TIAN Shi-wei, JIANG Hai-tao, LIU Ji-xiong, et al. Rheological behavior and rolling preparation of bimetallic titanium steel composite plates[J]. Materials Guide, 2019, 33(24): 414.) [11] LI S, TANG D, WU H B, et al. Interface microstructure and properties of 304 austenite stainless steel/low carbon steel clad plate by casting and hot rolling process[J]. Advanced Materials Research,2014, 852: 178. [12] LUO Z A, WANG G L, XIE G M, et al. Interfacial microstructure and properties of a vacuum hot roll-bonded titanium-stainless steel clad plate with a niobium interlayer[J]. Acta Metallurgica Sinica (English Letters),2013, 26(6):754. [13] Varmazyar J, Khodaei M. Diffusion bonding of aluminum-magnesium using cold rolled copper interlayer[J]. Journal of Alloys and Compounds, 2019, 773: 838. [14] CHAI X Y, CHEN G, CHAI F, et al. Hot roll bonding between commercially pure titanium and high-strength low-alloy steel using Fe interlayer[J]. Journal of Iron and Steel Research, International, 2019, 26(10): 1126. [15] 金贺荣, 孔耀颉, 张一, 等. 采用铁钴镍合金夹层的316L/EH40复合板界面特征[J]. 钢铁,2020,55(10): 63.(JIN He-rong, KONG Yao-jie, ZHANG Yi, et al. Interface characteristics of 316L / EH40 composite plate with Fe, Co, Ni alloy interlayer[J]. Iron and Steel,2020, 55(10): 63.) [16] WANG S, LIU B X, ZHANG X, et al. Microstructure and interface fracture characteristics of hot-rolled stainless steel clad plates by adding different interlayers[J]. Steel Research International, 2020, 91(4): 1. [17] XIE G M, YANG D H, LUO Z A, et al. The determining role of Nb interlayer on interfacial microstructure and mechanical properties of Ti/steel clad plate by vacuum rolling cladding[J]. Materials, 2018, 11(10): 1983. [18] Elthalabawy W, Khan T.Eutectic bonding of austenitic stainless steel 316L to magnesium alloy AZ31 using copper interlayer[J]. The International Journal of Advanced Manufacturing Technology,2011, 55(1): 235. [19] 吴静怡, 孙新军, 李建, 等. 不同中间层热轧Q235/TA2复合板界面显微结构及性能[J]. 金属热处理,2018,43(1): 136.(WU Jing-yi, SUN Xin-jun, LI Jian, et al. Microstructure and properties of interface of hot rolled Q235/TA2 composite plates with different intermediate layers[J]. Metal Heat Treatment,2018, 43(1): 136.) [20] 陈泽军, 周廷, 李博新, 等. 钒中间层钛/钢复合板结合界面结构与力学性能[J]. 塑性工程学报, 2019,26(1): 188.(CHEN Ze-jun, ZHOU Ting, LI Bo-xin, et al. Interface structure and mechanical properties of the vanadium interlayer titanium/steel composite plate[J]. Journal of Plastic Engineering,2019, 26(1): 188.) [21] 谢红飙, 王德蔚, 余超, 等. 纯铁做中间材制备不锈钢/碳钢热轧复合板[J]. 钢铁, 2017, 52(12): 48.(XIE Hong-biao, WANG De-wei, YU Chao, et al. Preparation of stainless steel/carbon steel hot-rolled composite plates with pure iron as intermediate material[J].Iron and Steel, 2017, 52(12):48.)
2021, Vol. 56 