Abstract:The advantages and problems of using high-proportion pellets in blast furnaces from the perspective of strategic development were analyzed, and the strategic opportunities for using high-proportion pellets in blast furnaces was clarified. According to the characteristics of domestic high-silicon iron concentration, basic researches on green pellet-making, drying and roasting of magnesia pellets with high silicon acidity and flux properties have been carried out. Furthermore, the compressive strength of pellets, high-temperature metallurgical properties, and ring formation in the production process of rotary kiln have been analyzed. The basic characteristics such as formation mechanism and the design characteristics of the basic operating parameters for pellet production were put forward, and the stable continuous production of high silica magnesia acid and flux pellets produced by the grate rotary kiln was realized. Two high-proportion pellet blast furnace production trials have been completed. Practice has proved that the production of high-proportion pellet smelting blast furnaces was stable and smooth, and all indicators were better than those of high-proportion sinter smelting blast furnaces. The operating ideas can be replicated, the smelting results can be reproduced, the operating experience can be promoted, and the environmental benefits are huge. The emissions of SO2, NOx, PM and CO2 are far superior to blast furnaces produced with a high proportion of sintered ore. It is foreseeable that the preparation of high-quality metallurgical pellets and the smelting of high-proportion blast furnace pellets will be the best measure to break the long-term steel process in China to reduce total pollutant emissions and achieve low-carbon smelting and sustainable development.
王新东, 金永龙. 高炉使用高比例球团的战略思考与球团生产的试验研究[J]. 钢铁, 2021, 56(5): 7-10.
WANG Xin-dong, JIN Yong-long. Strategy analysis and testing study of high ratio of pellet utilized in blast furnace[J]. Iron and Steel, 2021, 56(5): 7-10.
[1] 王新东. 以“绿色化、智能化、品牌化”为目标规划设计河钢唐钢新区[J]. 钢铁, 2021, 56(2): 12.(WANG Xin-dong. Planning and design of HBIS Group Tangsteel new district with goal of "Green, Intelligent and Brand"[J]. Iron and Steel, 2021, 56(2):12.) [2] ZHANG Fu-ming, CAO Chao-zhen.Progress and expectation of ironmaking technology in Shougang[C]//The 11th Korea-China Joint Symposium on Advanced Steel Technology. Korea:[s.n.], 2019:1. [3] 宝钢湛江炼铁厂. 稳定生产实践与超低排放应对[C]//2019年全国炼铁厂长座谈会. 唐山:[出版者不详],2019:48.(Iron-making plant Zhanjiang Baosteel. Practice of stable production and super low emission[C]//2019 Discussion Meeting of Directors of Domestic Iron-making Plants.Tangshan: [s.n.], 2019:48.) [4] 金永龙,何志军,王川.不同炉料结构高炉实现低碳排放的解析[J]. 钢铁, 2019,54(7):8.(JIN Yong-long,HE Zhi-jun,WANG Chuan.Analysis on low carbon emission of blast furnace with different raw materials structure[J]. Iron and Steel, 2019,54(7):8.) [5] 齐枫,李玉然,朱廷钰,等.球团及球团烟气的硫平衡对比研究[J].河北冶金,2019(s1):58.(QI Feng,LI Yu-ran,ZHU Ting-yu,et al.Comparative study of sulfur balance on pellet and pellet flue gas[J].Hebei Metallurgy,2019(s1):58.) [6] Hiroshi Nogami,Jun-ichiro Yagi,Shin-ya Kitamura,et al.Analysis on material and energy balances of ironmaking systems on blast furnace operations with metallic charging, top gas recycling and natural gas injection[J]. ISIJ International,2006,46(12):1759. [7] 沙永志,马丁·戈德斯,宋阳升.我国高炉使用高比例球团矿的技术及经济性分析[J].炼铁,2019,6(38):1.(SHA Yong-zhi,Maarten Geerdes,SONG Yang-sheng.Technical and economic analysis of blast furnace operation with high pellet ratio in china[J].Ironmaking,2019,6(38):1.) [8] Mats Bramming, Jan-Olov Wikstrom.A blast furnace view on slags[J]. Scandinavian Journal of Metallurgy, 2002,6(31):88. [9] Axelsson O, Bramming M, Karsrud K.Rebuild of ssab oxelosund blast furnace No.4 and introduction the roax-top[C]//1997 Ironmaking Conference Proceedings. Chicago: [s.n.], 1997:507. [10] Kimmo Kinnunen,Timo Paananen, Jarmo Lilja,et al.(STSI-156)Modelling and simulation of blastfurnace process for switch from sinterto pellet operation[C]//4th International Conference on Modelling and Simulation of Metallurgical Processes in Steelmaking. Düsseldorf: [s.n.], 2011:1. [11] 潘建,于鸿宾,朱德庆,等.MgO来源对磁铁精矿球团预热行为的影响[J].中南大学学报(自然科学版),2016,47(9):2914. (PAN Jian,YU Hong-bin,ZHU De-qing,et al.Effect of MgO content and sources on induration behavior of magnetite concentrate pellets[J]. Journal of Central South University(Natural Science), 2016,47(9):2914.) [12] 周明顺,沈峰满,翟立委,等.MgO添加方式对改善球团矿冶金性能的影响[J].钢铁,2012,47(4):14.(ZHOU Ming-shun,SHEN Feng-man,ZHAI Li-wei,et al. Influences of MgO adding method on improving metallurgical properties of pellet[J].Iron and Steel,2012,47(4):14.) [13] 高强健,沈峰满,郑海燕,等.MgO对铁矿球团还原冶金性能的影响[J].东北大学学报(自然科学版),2014,35(12):1742. (GAO Qiang-jian,SHEN Feng-man,ZHENG Hai-yan, et al.Investigation on effect of MgO on reduction metallurgical properties of iron ore pellet[J]. Journal of Northeastern University(Natural Science),2014,35(12):1742.) [14] 李晓兵.改善高炉球团矿还原性技术措施[J].河北冶金,2019(3):26.(LI Xiao-bing.Measures for improving reductive technology of blast furnace pellets[J].Hebei Metallurgy,2019(3):26.) [15] ZHU D,CHUN T,PAN J,et al.Influence of basicity and MgO content on metallurgical performances of Brazilian specularite pellets[J].International Journal of Mineral Processing,2013,125(3):51. [16] 刘文壮, 安志庆. 八钢高炉使用高比例球团矿冶炼实践[J]. 新疆钢铁, 2006(3): 50.(LIU Wen-zhuang, AN Zhi-qing. Practice of high ratio pellet used by BF in BaSteel[J]. Xinjiang Iron and Steel,2006(3): 50.) [17] Timo Paananen,Kimmo Kinnunen,Jarmo Lilj, et al.Experience of full scale research test with 100% pellet blast furnace operation in ruukkiauthors[C]//6th European Coke and Ironmaking Congress. Düsseldorf: [s.n.],2011:1. [18] 杨天钧. 关于新形势下炼铁工业发展的认识[C]//2020年炼铁生产技术会暨炼铁学术年会. 重庆:中国金属学会,2020:9.(YANG Tian-jun. Knowledge about the development of ironmaking industry in the new circumstances[C]//2020 Ironmaking Production and Technology Conference and Academic Annual Symposium. Chongqing:The Chinese Society for Metal,2020:9.) [19] 张文强,肖洪,高冰,等.唐钢1号高炉高比例球团矿冶炼工业试验[J].炼铁,2019,2(38):13.(ZHANG Wen-qiang,XIAO Hong,GAO Bing,et al.Commercial test of high-rate pellet smelting in Tangshan Steels No.1 BF[J].Ironmaking,2019,2(38):13.) [20] 金永龙, 何志军, 关志刚, 等. H2含量对冶炼过程影响的实践与理论分析[J].钢铁,2011,46(5):15.(JIN Yong-long, HE Zhi-jun, GUAN Zhi-gang. Practice and theorical analysis about effect of H2 content on ironmaking process[J]. Iron and Steel, 2011,46(5):15.) [21] FAN Xiao-hui, GAN Min, JIANG Tao, et al.Influence of flux additives on iron ore oxidized pellets[J]. Journal of Central South University, 2010,16(17): 732. [22] Tekkalakote Umadevi, Angalakuditi Brahmacharyulu, Ajay Kumar Roy,et al.Influence of iron ore fines feed size on microstructure, productivity and quality of iron ore sinter[J].ISIJ International, 2011,51(6):922. [23] Panigrahy S C, Verstraeten P, DIlewijns J.Influence of MgO addition on mineralogy of iron ore sinter[J]. Metallurgical Transactions B,1984,15(3):23. [24] Umadevi T, Prachethan Kumar P, Prasanna Kumar, et al.Investigation of factors affecting pellet strength instraight grate induration machine[J].Ironmaking and Steelmaking,2008,35(5):321. [25] 陆亚男,吴胜利,霍红艳,等.适合高炉低烧比炉料结构的球团矿种类优选[J].河北冶金,2020(10):6.(LU Ya-nan,WU Sheng-li,HUO Hong-yan,et al.Optimization of pellet type suitable for blast furnace burden design with low burning ratio[J].Hebei Metallurgy,2020(10):6.) [26] 邓睿,苏鸿,韩基祥,等.高球比炉料结构下镁质球团的冶金性能研究[J].烧结球团,2020,2(45):31.(DENG Rui,SU Hong,HAN Ji-xiang,et al.Study on metallurgical properties of magnesium pellet under the burden structure of high pellet ratio[J].Sintering and Pelletizing,2020,2(45):31.) [27] 张汉权,罗立群. 烧结球团理论与工艺[M]. 北京: 冶金工业出版社,2018. (ZHANG Han-quan, LUO Li-qun.Theory and Technology of Sintering and Pelleting[M]. Beijing: Metallurgical Industry Press,2018.) [28] 韩涛.高比例镁质熔剂性球团炼铁技术现状浅析[J].河南冶金,2020(8):5.(HAN Tao.Analysis on present situation of high proportion fluxed pellets ironmaking technology[J].Henan Metallurg,2020(8):5.) [29] 王新东,李建新,胡启晨.基于高炉炉料结构优化的源头减排技术及应用[J].钢铁,2019,54(12):104.(WANG Xin-dong,LI Jian-xin,HU Qi-chen.Application practice of source and process sulfur-nitrate reduction technology based on optimization of blast furnace charge structure[J].Iron and Steel,2019,54(12):104.)