B2O3-Na2O系调渣剂对钒钛铁水脱硫渣性能的影响

doi:10.13228/j.boyuan.issn0449-749x.20210078

摘要
图/表
参考文献
相关文章 (7)

全文: PDF (2829 KB) HTML (1 KB)
输出: BibTeX | EndNote (RIS)

摘要为解决含钒钛铁水脱硫扒渣过程中炉渣黏稠、铁损大及后续回硫多等问题,运用FactSage热力学软件,结合高温试验,探究了B₂O₃+Na₂O系调渣剂对钒钛铁水脱硫渣回硫、熔点及黏度的影响。结果表明,随着B₂O₃和Na₂O加入,铁水脱硫渣熔点及黏度显著降低;调渣剂中添加CaO有助于抑制回硫。并提出了改善铁水脱硫渣性能的调渣剂配方(质量分数),即CaO 45%～55%、SiO₂ 10%～15%、Al₂O₃ 5%～8%、B₂O₃ 15%～20%、Na₂O 5%～10%。调渣剂添加量为脱硫渣渣量的5%～10%时,能有效降低脱硫渣熔点和黏度,减少回硫。

	服务

	把本文推荐给朋友
	加入我的书架
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杨必文
	王海北
	郑朝振
	陈亮
	胡一航

关键词 ：钒钛铁水, 脱硫渣, 回硫, 渣态性能, 调渣剂

Abstract：In order to solve the problems of thick of slag, large of iron loss, and much of resulfurization in the slagging-off process after pre-desulfurization of hot metal containing vanadium and titanium, the effect of B₂O₃-Na₂O slag modifier on resulfurization, melting point, and viscosity of the desulfurization slag was investigated by using FactSage thermodynamic software and combing with high-temperature experiments. The results showed that the melting point and viscosity of the desulfurization slag decreased significantly with the addition of B₂O₃ and Na₂O. And the addition of CaO to the slag modifier helped to reduce resulfurization. The formula of slag modifier (45%-55% of CaO, 10%-12% of SiO₂, 5%-8% of Al₂O₃, 15%-20% of B₂O₃, and 5%-10% of Na₂O) to improve the performance of desulfurization slag was presented. It effectively reduced the melting point and viscosity of desulfurization slag and decreased the resulfurization, when the added amount of the slag modifier was 5%-10% of the desulfurization slag.

Key words： hot metal containing vanadium and titanium desulfurization slag resulfurization performance of slag slag modifier

收稿日期: 2021-02-05

引用本文:

杨必文, 王海北, 郑朝振, 陈亮, 胡一航. B₂O₃-Na₂O系调渣剂对钒钛铁水脱硫渣性能的影响[J]. 钢铁, 2021, 56(10): 91-98. YANG Bi-wen, WANG Hai-bei, ZHENG Chao-zhen, CHEN Liang, HU Yi-hang. Effect of B₂O₃-Na₂O slag modifier on desulfurization slag performance of hot metal containing vanadium and titanium[J]. Iron and Steel, 2021, 56(10): 91-98.

链接本文:

http://www.chinamet.cn/Jweb_gt/CN/10.13228/j.boyuan.issn0449-749x.20210078 或 http://www.chinamet.cn/Jweb_gt/CN/Y2021/V56/I10/91

[1] Vuolio T, Visuri V V, Paananen T, et al. Identification of rate, extent, and mechanisms of hot metal resulfurization with CaO-SiO₂-Na₂O slag systems[J]. Metallurgical and Materials Transactions B, 2019, 50(4): 1791.
[2] 吴发达, 包燕平, 刘建华. 转炉冶炼低硫钢回硫的控制[J]. 炼钢, 2007, 23(3): 24.(WU Fa-da, BAO Yan-ping, LIU Jian-hua. Control on resulphurization in production of low sulphur steel in BOF[J]. Steelmaking, 2007, 23(3): 24.)
[3] 刘国平, 徐小伟, 毛鸣, 等. 马钢300 t转炉炼钢系统钢中硫的控制研究与实践[J]. 钢铁, 2011, 46(9): 29.(LIU Guo-ping, XU Xiao-wei, MAO Ming, et al. Practice and research on sulfur control of 300 t BOF steelmaking process in Masteel[J]. Iron and Steel, 2011, 46(9): 29.)
[4] 孙亮, 朱良, 赵晓东. 3种铁水脱硫工艺的应用实践[J]. 中国冶金, 2018, 28(3): 50.(SUN Liang, ZHU Liang, ZHAO Xiao-dong. Application practice of three kinds of hot metal desulphurization process[J]. China Metallurgy, 2018, 28(3): 50.)
[5] XU J, HUANG F, WANG X, et al. Resulfurization behavior of pipeline steel in a converter steelmaking process[J]. Metallurgical Research and Technology, 2015, 112(5): 504.
[6] Susaki K, Maeda M, Sano N. Influence of additives on sulfide capacity of CaO-CaF₂-SiO₂ slags[J]. Metallurgical Transactions B, 1990, 21(6): 1081.
[7] Cho M K, Cheng J, Park J H, et al. Hot metal desulfurization by CaO-SiO₂-CaF₂-Na₂O slag saturated with MgO[J]. ISIJ International, 2010, 50(2): 215.
[8] Magnelöv M, Dahlberg A C, Gustavsson L, et al. Iron losses during desulphurisation of hot metal utilising co-injection of Mg and CaC₂ combined with nepheline syenite[J]. Ironmaking and Steelmaking, 2015, 42(7): 525.
[9] 梁新腾, 曾建华, 李扬洲, 等. 含钒钛铁水的脱硫渣改性剂和脱硫方法: 中国, 201410469708.1[P]. 2014-09-16.(LIANG Xin-teng, ZENG Jian-hua, LI Yang-zhou, et al. Desulfurization Slag Modifier and Desulfurization Method for Hot Metal Containing Vanadium and Titanium: China, 201410469708.1[P]. 2014-09-16.)
[10] 蒋龙奎, 戈文荪, 陈永, 等. 一种降低含钒钛铁水脱硫扒渣铁损的方法: 中国, 201310632828.4[P]. 2013-11-27.(JIANG Long-kui, GE Wen-sun, CHEN Yong, et al. A Method to Reduce Iron Loss in Slagging-off Process after Desulfurization of Hot Metal Containing Vanadium and Titanium: China, 201310632828.4[P]. 2013-11-27.)
[11] Wu L, Ek M, Song M, et al. The effect of solid particles on liquid viscosity[J]. Steel Research International, 2011, 82(4): 388.
[12] 雷家柳, 赵栋楠, 朱航宇, 等. 基于IMCT理论的CaO-SiO₂-MgO-Al₂O₃-Na₂O渣系的脱硫热力学模型[J]. 钢铁, 2019, 54(3): 35. (LEI Jia-liu, ZHAO Dong-nan, ZHU Hang-yu, et al. A thermodynamic model of desulfurization for CaO-SiO₂-MgO-Al₂O₃-Na₂O slag based on IMCT theory[J]. Iron and Steel, 2019, 54(3): 35.)
[13] 封波, 徐昊, 高卫, 等. LF精炼渣低氟化研究进展[J]. 中国冶金, 2014, 24(6): 1. (FENG Bo, XU Hao, GAO Wei, et al. Research progress on LF refining slag with low-fluorite[J]. China Metallurgy, 2014, 24(6): 1.)
[14] 林银河, 符娅玲, 罗林根, 等. 高钛型高炉渣中B₂O₃替代CaF₂的作用机理[J]. 钢铁, 2019, 54(2): 26. (LIN Yin-he, FU Ya-ling, LUO Lin-gen, et al. Effect on B₂O₃ replacing CaF₂ of high Ti-bearing blast furnace slag[J]. Iron and Steel, 2019, 54(2): 26.)
[15] Toop G W, Somis C S. Some new ionic concepts of silicate slags[J]. Canadian Metallurgical Quarterly, 1962, 1(2):129.
[16] Maxl E, Hiebler H, Presslinger H, et al. Microanalytical investigations of oxidizing slags with special consideration of phosphorus- and sulphur-containing phases[J]. ISIJ International, 1993, 33(1): 88.
[17] Ono H, Nakajima K, Maruo R, et al. Formation conditions of Mg₂TiO₄ and MgAl₂O₄ in Ti-Mg-Al complex deoxidation of molten iron[J]. ISIJ International, 2009, 49(7): 957.
[18] Jung E J, Wook W, Sohn I, et al. A study on the interfacial tension between solid iron and CaO-SiO₂-MO system[J]. Journal of Materials Science, 2010, 45(8): 2023.
[19] ZENG L, WANG Y, FAN L, et al. Experimental study and thermodynamic optimization of the FeO-V₂O₃ system[J]. Journal of Iron and Steel Research, International, 2014, 21(10): 910.
[20] Tsujino R, Nakashima J, Hirai M, et al. Behavior of desulfurization in ladle steel refining with powder injection at reduced pressures[J]. ISIJ International, 1989, 29(1): 92.
[21] 魏寿昆. 炉渣氧化铁含量对脱硫的作用[J]. 金属学报, 1964, 7(2): 157.(WEI Shou-kun. The effect of the iron oxide content in molten slags upon desulphurization[J]. Acta Metall Since, 1964, 7(2): 157.)