Prediction and influencing factors of scraper force for sink roll system of hot dip galvanizing unit
WANG Xiao-jian1,3, QIAN Sheng1,2, CUI Meng-yu1, BAI Zhen-hua1,4
1. National Cold Rolling Strip Equipment and Process Engineering Technology Research Center, Yanshan University, Qinhuangdao 066004, Hebei, China; 2. College of Mechanical and Electrical Engineering, Huangshan University, Huangshan 245041, Anhui, China; 3. Meigang Technology Center, Baosteel Co., Ltd., Central Research Institute, Nanjing 210039, Jiangsu, China; 4. State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004, Hebei, China
Abstract：The sink roll in hot galvanizing units blown not clean on the surface of zinc slag leads to the strip surface defects, which seriously affect strip product quality grades. The characteristics of equipment and process of hot galvanizing unit were combined in this paper. Firstly, the force of sink rollers scraper mechanism was analyzed and the model of scraper force was established on the basis of steady state condition. Considering the influence of gap fluctuation between axle sleeve and bearing bush, the residual zinc residue deposited on the roll surface and the blade wear on the blade force in the actual working conditions of sink roll system, the scraper force model was modified to calculate the scraper force under unsteady conditions. Then the influence mechanism of scraper angle, journal eccentricity, blade wear and residual zinc residue on scraper force was analyzed. The calculation process of scraper force was developed according to the scraper force modification model, and the model was applied to actual production. Three typical specifications of strip steel were selected to predict the scraper force. The relative error between the predicted value and the measured value was less than 15%, and met the precision requirement of the unit. Finally, the influence of strip production parameters (strip tension, strip speed, surface galvanization) on the predicted value of scraper force was analyzed by taking strip A as an example. The results show that the scraper force increases with the increase of scraper angle in a small range (9°-12°), and the scraper force increases nonlinearly with the journal eccentricity increasing. The increase of blade wear will reduce the slag removal ability of scraper. The increase of residual zinc residue on the roller surface leads to the increase of scraper force, which is easy to cause the phenomenon of roller system sticking or slipping. The scraper force increases linearly with strip tension and decreases linearly with strip speed, but the influence of surface galvanization on scraper force is relatively small.
王孝建, 钱胜, 崔梦雨, 白振华. 热镀锌机组沉没辊系刮刀力预报及影响因素[J]. 钢铁, 2022, 57(6): 82-90.
WANG Xiao-jian, QIAN Sheng, CUI Meng-yu, BAI Zhen-hua. Prediction and influencing factors of scraper force for sink roll system of hot dip galvanizing unit[J]. Iron and Steel, 2022, 57(6): 82-90.
[1] 魏宝民,何召龙,王孝建,等. 材料成分对热镀锌钢板性能及表面质量的影响[J].中国冶金,2020,30(10):71.(WEI Bao-min, HE Zhao-long, WANG Xiao-jian, et al. Effect of material composition on properties and surface quality of hot dip galvanized steel sheet[J].China Metallurgy,2020,30(10):71.) [2] 王畅,于洋,李研,等.高强镀锌板表面发麻缺陷产生机理[J].中国冶金,2020,6(29):21.(WANG Chang, YU Yang, LI Yan, et al. Formation mechanism of pitting defect on surface of high strength galvanized sheet[J].China Metallurgy,2020,6(29):21.) [3] 王滕,柴立涛,李伟刚.镀铝板用耐高温型无铬钝化结合机理及性能[J].中国冶金, 2019, 12(29):45.(WANG Teng, CAI Li-tao, LI Wei-gang. Bonding mechanism and technological properties of high temperature resistant chromium-free passivation coating for aluminized sheet[J].China Metallurgy, 2019, 12(29):45.) [4] 赵占彪,王强狄,彦军,等. 热镀锌基板表面缺陷遗传性影响分析及相应措施[J]. 轧钢, 2019, 36(6), 90.(ZHAO Zhan-biao, WANG Qiang-di, YAN Jun, et al. Analysis of genetic effects of surface defects in hot dip galvanized substrate and corresponding measures[J].Steel Rolling, 2019, 36(6):90.) [5] 董子亮,段晓溪,张学范,等. 炉鼻子氮气露点对带钢表面质量的影响及控制[J]. 轧钢,2021,38(2),90.(DONG Zi-liang, DUAN Xiao-xi, ZHANG Xue-fan, et al. Influence and control of nitrogen dew point on strip surface quality in furnace nose[J].Steel Rolling, 2021,38(2),90.) [6] 秦大伟,刘宏民,张栋,等.带钢热镀锌镀层单位面积质量神经网络预测模型[J].钢铁,2020,55(5),68.(QIN Da-wei, LIU Hong-min, ZHANG Dong, et al. Prediction models of coating mass per unit area for hot-dip galvanized strip based on artificial neural network[J]. Iron and Steel,2020,55(5),68.) [7] 孙永旭,钱胜,白振华. 热镀铝锌连退过程中带钢横向拉窄量预报及其影响因素[J]. 轧钢, 2021,38(1): 41.(SUN Yong-xu, QIAN Sheng, BAI Zhen-hua. Investigation on prediction of transverse narrowing of strip and its influence factors in continuous annealing process of galvalume unit[J].Steel Rolling,2021,38(1):41.) [8] 钱胜,顾清,李学通,等. 镀锌机组带钢C翘缺陷综合治理技术的开发[J].钢铁,2021,56(11):160. (QIAN Sheng, GU Qing, LI Xue-tong, et al. Development of comprehensive treatment technology for strip C-shaped warp defect in galvanizing unit[J].Iron and Steel,2021,56(11):160.) [9] 岳崇锋,江社明,王银军,等. 热镀铝锌硅镀层凸点缺陷组织分析及生产工艺优化[J].腐蚀与防护,2015,36(3):306.(YUE Chong-feng, JIANG She-ming, WANG Yin-jun, et al. Analysis of bump defect of hot-dipped galvalume and process optimization in production[J]. Corrosion and Protection,2015,36(3):306.) [10] 李超,王滕,孙镕强,等. 热浸镀铝硅钢板表面点状缺陷分析及改进[J].金属热处理,2021,46(3):213.(LI Chao, WANG Teng, SUN Rong-qiang, et al. Analysis and improvement of point defects on surface of hot dip aluminum-silicon plated steel sheet[J]. Heat Treatment of Metals,2021,46(3):213.) [11] 金鑫焱,钱洪卫,林传华. 沉没辊沟槽印缺陷在合金化过程中的演变[J].宝钢技术,2017(6):21.(JIN Xin-yan, QIAN Hong-wei, LIN Chuan-hua. Investigation on the transformation of sink roll groove mark defect in the galvannealing process[J].Baosteel Technology,2017(6):21.) [12] 段晓溪,马幸江,鲁洋泽,等. 热镀锌带钢表面色差缺陷形成机理及改进措施[J].物理测试,2020,38(6):37.(DUAN Xiao-xi, MA Xing-jiang, LU Yang-ze, et al. Formation mechanism and improvement measures of color difference defect on surface of hot-dip galvanized strip steel[J]. Physics Examination and Testing, 2020,38(6):37.) [13] 王银军,李远鹏,江社明,等. 热浸镀铝锌熔池锌渣形成的研究进展[J].材料保护,2020,53(10):85.(WANG Yin-jun, LI Yuan-peng, JIANG She-ming, et al. Research progress of the formation mechanism of zinc slag in hot dip galvanizing Al-Zn molten bath[J]. Materials Protection,2020,53(10):85.) [14] 徐勇. 镀锌机组改造为镀铝锌机组工艺装备自主集成[J].轧钢,2021,38(1):55.(XU Yong. Process and equipment independent integration of reforming GI line to GL line[J].Steel Rolling,2021,38(1):55.) [15] 钱胜,张文军,林威,等.热镀锌连退过程C翘机理及其预报模型[J]. 钢铁2021,56(9),88.(QIAN Sheng, ZHANG Wen-jun, LIN Wei, et al. Formation mechanism and prediction model for C-shaped warp defects of strip in continuous annealing process of galvalume unit[J].Iron and Steel,2021,56(9),88.)
2022, Vol. 57 