Study on Roll Gap of Slab Caster Based on Solidification Shrinkage |
MA Changwen1,CHEN Songlin1,ZHENG Tianran1,YANG Xiaoshan2 |
1. Shougang Research Institute of Technology, Shougang Group Corporation, Beijing 100043, China; 2. No.2 Steel Making Plant, Shougang Group Corporation, Beijing 100043, China |
|
|
Abstract In order to research the effect of roll gap reduction on reducing the centerline segregation of slab, the temperature and solidification shrinkage of a slab were calculated by numerical simulation, the distribution of the solidified shell thickness and solidification shrinkage along the metallurgical length were analyzed, then three sets of roll gap reduction were built,tested and their effects were compared. The results show that the roll gap reduction within 23 segments before the solidification end is effective to reduce the centerline segregation, and the roll gap reduction rate should be a little more than the slab solidification shrinkage.
|
Received: 01 January 1900
|
|
|
|
[1] |
MAO Jinghua,SHUAI Yong,XIE Guiqiang,WANG Yatao. Key technology of internal quality control for#br# continuous casting extrathick slab[J]. Iron and Steel, 2019, 54(8): 64-69. |
[2] |
LAN Peng,HAN Gengwei,LI Liang,WANG Pu,. Formation and control of midway crack in LDCC #br# Q235B steel slab with high casting speed[J]. Iron and Steel, 2019, 54(8): 144-153. |
[3] |
WANG Changshun,GUO Fujian,LI Guanglong,SHANG Chengjia. Influence of central segregation control on #br# low temperature toughness of steel[J]. Iron and Steel, 2019, 54(8): 202-208. |
[4] |
. Research on Central segregation control of 400mm ultra-thick slab[J]. , 2019, 44(6): 0-0. |
[5] |
XU Li-ping,WANG Hong-feng. Research and practice on corner scarring defect of continuous casting slabs[J]. , 2019, 44(1): 40-43. |
[6] |
SU Rui-xian,SU Zhi-jian. Process optimization of high carbon tool steel slab continuous casting[J]. , 2019, 44(1): 18-21. |
|
|
|
|