Effect of Al and Ti Treatment on Microstructure of CoarseGrain HAZ in HSLA Steel |
CHAI Feng1,2,YANG Caifu2,ZHANG Yongquan2,SU Hang2,XU Zhou1 |
1. Shanghai Jiaotong University, Shanghai 200030, China;2. Central Iron and Steel Research Institute, Beijing 100081, China |
|
|
Abstract The Effect of Al and Ti treatment on coarsegrain HAZ microstructure in HSLA steel was investigated. The results showed that the inclusions in Al treated steel are mainly aluminum oxides and titanium nitrides. Aluminum oxide and Titanium nitride could not promote the formation of acicular ferrite. Microstructure of coarsegrain HAZ of Al treated steels consists of heavy ferrite in grain boundaries and ferrite side plate. The inclusions in Ti treated steel are Al,Ti,Mg,Ca composite oxides with size in the range of 0.53 μm and titanium nitride. Ti composite oxide could promote the formation of acicular ferrite and microstructure of coarsegrain HAZ of Ti treated steel consists of ferrit in grain boundaries, ferrite side plate and large amount of intragranular acicular ferrite.The size of ferrite in grain boundaries is increased and the amount of ferrite side plate is decreased with the increase of soaking time at the peak temperature. The amount of ferrite in grain boundaries and the size of acicular ferrite is increased with the increase of cooling rate during phase formation.
|
Received: 01 January 1900
|
|
|
|
[1] |
SUN Li-gen, LEI Ming, ZHANG Xin, LIU Yun-song, ZHU Li-guang. In-situ research on microstructure refining effect of Mg treatment for shipbuilding steel at high temperature[J]. Iron and Steel, 2020, 55(5): 94-102. |
[2] |
ZHU Li-guang, ZHENG Shi-wei, ZHANG Qing-jun, CAO Sheng-li. Influence of oxide metallurgy and pulsed magnetic field parameters on steel microstructure[J]. Iron and Steel, 2020, 55(3): 74-79. |
[3] |
ZHOU Ren-yuan, ZHU Li-hui, LI Shi-xian, ZHAI Guo-li. Improvement of reheat-cracking susceptibility and microstructure of T23 steel[J]. Iron and Steel, 2020, 55(3): 80-86. |
[4] |
DOU Wei-xue,WANG He-song,KANG Jian,LI Zhen-lei,YUAN Guo. Effect of cooling rate on microstructure of low-carbon steel produced by strip casting[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 748-753. |
[5] |
ZHANG Cai-wei,QU Tian-peng,WANG De-yong,TIAN Jun,HOU Dong. Effect and mechanism research of MgTi treatment on solidification structure of ferritic stainless steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(7): 660-666. |
[6] |
LOU Hao-nan,WANG Bing-xing,WANG Zhao-dong. Microstructure and properties of Ti-Mg oxide metallurgy steel under TMCP process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(12): 1039-1045. |
|
|
|
|