| Application of Thermal Imaging Figure of Mould to Predicting and Controlling Longitudinal Crack of Thin Slab |
| MA Xinguang,ZHANG Yunfei,LI Junming |
| No.1 Steelmaking and Rolling Plant, Tangshan Iron and Steel Group Co., Ltd., Tangshan 063016, Hebei, China |
|
|
|
|
Abstract Based on experience of thin slab casting at Tangshan Steel,the application of thermal imaging figure of mould to predicting and controlling longitudinal crack of thin slab was analyzed. Besides,the factors affecting longitudinal cracking of thin slab were studied such as use of protecting slag, casting speed, degree of superheat, etc. And the corresponding control measures were put forward. The rate of longitudinal cracking of thin slab at Tangshan Steel was reduced largely.It was shown that making parameters of process and equipment appropriate and steady is the basic condition to reduce longitudinal cracks of thin slab. On the base of temperature uniformity displayed by thermal imaging figure of mould,the longitudinal cracking of thin slab can be predicted.Then, uniformity in heat transfer can be eliminated by changing mould taper. And, effective control of longitudinal cracking of thin slab can be realized.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
YANG Jie1,YAO Hai-ming2,WU Zhen-gang1,GAO Qian-yun2. Clogging control of submerged entry nozzle during IF steelproduction by middle-thin slab process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 20-26. |
| [2] |
GUO Junli，WEN Guanghua，FU Jiaojiao，TANG Ping，GU Shaopeng. Evaluation of carbon equivalent calculation of continue#br#
casting steel based on surface roughness[J]. Iron and Steel, 2019, 54(8): 187-193. |
| [3] |
ZHANG Jian-jun1，2， MAO Xin-ping 2， WANG Chun-feng3， ZHU Wan-jun2. Development and expection on high-efficiency producing technology of steelmaking in TSCR line[J]. Iron and Steel, 2019, 54(5): 1-8. |
| [4] |
YU Hai-tao. Practice of SK85 high carbon steel in benxi steel thin slab casting[J]. , 2019, 44(1): 5-9. |
| [5] |
ZHANG Zheng-lin， WANG Xiang-hong. Control of longitudinal surface crack of tube steel A29[J]. , 2018, 43(6): 71-73. |
| [6] |
YU Xue-cheng，LIU Feng-gang，MA Wei，NI You-jinZHU Jian-qiang，LIU Guo-liang. Development and application of chamfer mould in Shougang Qian’an Steel[J]. , 2018, 43(5): 75-79. |
|
|
|
|
2007, Vol. 42 