35CrNiMoV钢铸坯断裂原因分析

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (0 KB) HTML (0 KB)
Export: BibTeX | EndNote (RIS)

Abstract The cracking of 35CrNiMoV continuously cast slab was studied. Results show that the main reason is caused by improper cooling after casting. Some solutions, such as change the chemical composition and slow cooling under cover were given, and proved effective in practice.

Key words： continuously cast slab cracking internal stress slow cooling

Received: 01 January 1900

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FU Yongtao
	QIU Changsheng
	LIU Wuqun
	SHI Jie

Cite this article:

FU Yongtao,QIU Changsheng,LIU Wuqun等. Analysis of Cracking of 35CrNiMoV Continuous Casting Slab[J]. Iron and Steel, 2006, 41(9): 0-78.

URL:

http://www.chinamet.cn/Jweb_gt/EN/ OR http://www.chinamet.cn/Jweb_gt/EN/Y2006/V41/I9/0

[1]	CHEN Ya-jun1,KUANG Shuang2,ZHAO Zheng-zhi3. Study status of hydrogen induced delayed fracture of advanced high strength automotive steel[J]. JOURNAL OF IRON AND STEEL RESEARCH　, 2020, 32(4): 265-272.
[2]	. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0.
[3]	LIU Long，LI Nan，LUO Zhi-qiang. Analysis of cracking in tracks for a type of armored vehicle[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 22-.
[4]	GUO Yan-fei，CHEN Han，SUN Ke-qiang，LI Ju-qiang. Fracture analysis of 0Cr17Ni7Al spring wire winding spring[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 28-.
[5]	LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22.
[6]	YANG Yan-hui，BAI Yun，FAN Hai-dong， TANG Xiao-bing. Comparison of KIC test standards for metallic materials at home and abroad[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(1): 14-.