| Microstructure and Properties of Low Carbon Steel Strip Produced by Ferrite Rolling Technology on FTSR Line |
| WANG Xin1,KANG Yonglin1,YU Hao1,CHEN Libin2,KONG Qingfu2 |
| 1.School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083， China;2．Tangshan Iron and Steel Group Company, Tangshan 063000, Hebei， China |
|
|
|
|
Abstract The microstructure of 3.0 mm low carbon steel strip, produced by ferrite rolling process on flexible thin slab rolling (FTSR) line at Tangshan Iron and Steel Co. was analyzed by means of optical microscope, scanning electron microscope. The tensile mechanical properties, formability and the impact toughness of the strip were tested. The results show that the technology of thin slab continuous casting and rolling is suitable for ferrite rolling process. The microstructure of 3.0 mm low carbon steel strip is mainly composed of uneven ferrite, the mean size of the grains is about 29 μm, and there is a little pearlite with very fine lamellar structure, whose space length is smaller than 100nm, distributed in grain boundaries of ferrite. The yield strength of the strip is in the range of 215～240 MPa, tensile strength is in the range of 305-335 MPa and elongation is in the range of 33%-41%, this strip has lower strength and better ductility comparing with the strip produced by austenite rolling process. The bending performance and formability and impact toughness of the strip are excellent at room temperature.
|
|
Received: 01 January 1900
|
|
|
|
| [1] |
DU Liang, HAN Xiu-li, ZHANG Quan-sheng, ZHOU Xiang, YANG Hong-da, WANG Ying. Quantitative relation between mineralogical structure and metallurgical properties of sinter of import iron ore[J]. Iron and Steel, 2020, 55(6): 38-45. |
| [2] |
SUN Chao-fan, FANG Yuan, WANG Ya-qing, LIU Wei. Influence of temper rolling reduction rate on microstructure and mechanical properties of TS290 steel[J]. Iron and Steel, 2020, 55(6): 75-79. |
| [3] |
WEI Tong-yu, ZOU De-ning, ZHANG Ying-bo, CHEN Wan-wan. Effect of aluminum on microstructure and properties of high alumina ferritic heat resistant steel[J]. Iron and Steel, 2020, 55(6): 80-83. |
| [4] |
JIANG Yue-yue, WANG Zhao-dong, DENG Xiang-tao. Effect of trace rare earth Ce on martensitic transformation behavior of ultra-high strength low alloy steel[J]. Iron and Steel, 2020, 55(6): 84-90. |
| [5] |
WU Zhi-guang, GONG Xue-ting, LI Xin, ZHAO Ji-qing, GONG Zhi-hua. Effect of heat treatment process on creep-rupture property of 20Cr1Mo1VTiB bolt steel[J]. Iron and Steel, 2020, 55(6): 101-106. |
| [6] |
SHAO Chun-juan,ZHEN Fan,ZHANG Ji-ming,QU Jin-bo,ZHANG Lei. Effect of sample thinning on DWTT property of heavy wall X80 steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 497-504. |
|
|
|
|
2006, Vol. 41 