Abstract By the observation of microstructures and the analysis of SEM(scanning electron microscope) and EDS(energy dispersive x-ray spectrometry), the hot rolled plate peeling defects of pipeline steel are studied. It shows that the surface microcrack is found in continuous casting slab, and the elements of O, Si, Al, Ca, Cu are enriched around the crack. The main reason for hot rolled plate surface peeling is the slsb surface microcrack which is caused by oxide inclusions and copper content overproof. Finally, the influence mechanism of nonmetal oxide and low melting point metal on slab surface microcrack is discussed, and the preventive measures are presented correspondingly.
|
Received: 13 July 2009
|
|
|
|
[1] |
AI Ke-nan, ZHANG Pan-pan, ZHAO Meng-hao, LI Cheng-liang, ZHANG Zhi-ming, FU Jian-xun. Analysis of formation mechanism of surface crack of 1215 free-cutting steel during drawing[J]. Iron and Steel, 2020, 55(2): 88-94. |
[2] |
LIN Peng,ZHANG Hong-cai,LIU Ying,XU Zheng-zhou. Cause analysis of surface crack defects of gear steel 20CrNiMo rolled product[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(2): 40-. |
[3] |
CHANG Jinbao,YANG Wen,ZHANG Lifeng,REN Ying. Characteristics and formation mechanism of #br# sulfide in the slab of pipeline steel[J]. Iron and Steel, 2019, 54(8): 154-160. |
[4] |
MENG Yao-qing,ZHAO Hao-qian,TENG Yan-feng,KONG Wei-tao,ZHENG Yong-rui. Influence of calcium treatment on oxide inclusions in Sikilled spring steel 55SiCr[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(6): 538-546. |
[5] |
TANG Cun-jiang,SHANG Cheng-jia,XIA Dian-xiu,ZHOU Yun,CHEN Yun-bo. Characterization parameters for strain hardening behavior of ferrite/bainite multiphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(6): 553-562. |
[6] |
SHEN Bin-bin. Discussion about the thermoplasticity of vanadium microalloyed steel[J]. PHYSICS EXAMINATION AND TESTING, 2019, 37(5): 9-11. |
|
|
|
|