Genetic Analysis of Surface Cracks in H Beam |
LIU Jianhua1,BAO Yanping1,SUN Wei2,HUANG Sheqing2,ZHOU Jie1,2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China;2. Technical Center, Maanshan Iron and Steel Co., Ltd., Maanshan 243011, Anhui, China |
|
|
Abstract H beam is produced from beam blank at Masteel. Owing to the special shape, uneven distribution of lateral surface temperature, complicate distribution of strain and stress, high quality molten steel and high level continuous casting operation are required for continuous casting of beam blanks. The reasons of surface cracking are: in production, SS400 molten steel is not refined, C content of some heats locates in the range of peritectic reaction, S and P contents are high, Mn/S is low; and T[O] and content of macroinclusions are high; thickness of the shell is uneven and up stream of the liquid steel is weak in the mold by use of submerged nozzles with straight outlets and at low casting speed, which makes heat supply to molten steel insufficient and full melt of mould powder; the surface temperature of the web is in the brittleness range due to high cooling intensity in the secondary cooling zone.
|
Received: 01 January 1900
|
|
|
|
[1] |
chishirong chishirongchishirong. [J]. , 2020, 45(3): 0-0. |
[2] |
. Analysis and control of slag inclusion defect of low carbon steel slab[J]. , 2020, 45(2): 0-0. |
[3] |
Gan-Shui ZHOU. Diagnosis of instability during trial production of the billet continuous casting in a steel factory in Vietnam[J]. , 2020, 45(2): 0-0. |
[4] |
LAN Peng, TIE Zhan-peng, ZHANG Wei, MIAO Hong-sheng, YAN Qing-zhong, ZHANG Jia-quan. Research progress on spot segregation defects in continuously cast semi-products[J]. Iron and Steel, 2020, 55(2): 11-22. |
[5] |
AI Ke-nan, ZHANG Pan-pan, ZHAO Meng-hao, LI Cheng-liang, ZHANG Zhi-ming, FU Jian-xun. Analysis of formation mechanism of surface crack of 1215 free-cutting steel during drawing[J]. Iron and Steel, 2020, 55(2): 88-94. |
[6] |
ZHANG Si-yuan1,2,LONG Mu-jun1,2,AI Song-yuan1,2,TAN Kai1,2,CHEN Deng-fu1,2,HUANG Yun-wei1,2. Oxidation behavior of continuous casting slabs and its effect on temperature during cooling process[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 129-134. |
|
|
|
|