Strengthening Mechanism of HotRolled Low Carbon Steel Produced by CSP |
SU Shihuai1,HE Yizhu2,ZHU Tao1,LIU Xuewei2,WENG Yuqing3 |
1. Maanshan Iron and Steel Co., Ltd., Maanshan 243000, Anhui, China;2. School of Metallurgy and Materials, Anhui University of Technology, Maanshan 243002, Anhui, China;3. The Chinese Society for Metals, Beijing 100711 |
|
|
Abstract The effect of microstructure, precipitation of second phase on strength of SPHC produced by CSP (compact strip production) were investigated. The yield strength of SPHC produced both by CSP and by traditional technology were compared. The results show that the calculated yield strength of SPHC produced by CSP is 42 MPa lower than measured, but the measured and calculated yield strength of SPHC produced by traditional technology are the same. The TEM observation shows that there are three kinds of particles which sizes are nanoscale, submicronscale, and microscale in the steel produced by CSP. Precipitating strengthening contributes 40 MPa to the yield strength of SPHC produced by CSP.
|
Received: 01 January 1900
|
|
|
|
[1] |
CAO Yan-guang, LI Zhao-dong, DING Can-can, ZHANG Jin-wen, YONG Qi-long, GAO Jian-bing. Effect of niobium addition on hardenability of high-speed railway axle steel[J]. Iron and Steel, 2020, 55(6): 107-112. |
[2] |
HE Ya-yuan,LI Li-wei,YIN Yun-yang,DENG Zhao-jun. Evolution of microstructure and properties of thickness section of wearresistant steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(6): 512-518. |
[3] |
LI Lan-xin1,WANG Min1,JUAN Rong-fei1,BAO Yan-ping1,YANG Jin2. Distribution characteristics of oxides and sulfide inclusions in key areas of gear steel forgings[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(5): 370-376. |
[4] |
ZENG Ze-yun, LI Chang-rong, LI Zhi-ying, LIU Zhan-lin,LI Zheng-song, ZHAI Yong-qiang. Thermodynamic analysis of titanium precipitation in HRB500E seismic steel[J]. Iron and Steel, 2020, 55(5): 45-51. |
[5] |
ZHOU Cong-rui, CHEN Xiao-long, ZHOU Ming-ke,FAN Lei, MEI Peng, BAO Si-qian. Cause analysis of surface blackening of SPHC hot rolled strip after pickling[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 41-. |
[6] |
ZHOU Ren-yuan, ZHU Li-hui, LI Shi-xian, ZHAI Guo-li. Improvement of reheat-cracking susceptibility and microstructure of T23 steel[J]. Iron and Steel, 2020, 55(3): 80-86. |
|
|
|
|