Research on Mechanism of Poor Adhesion of Coated Layer in HDG |
Wu Kang-Mian |
|
|
Abstract Normal Fe-Al inhibition layer has been clearly observed under SEM through inclined specimen grinding. Research results show that there are different causes for poor coated layer adhesion in actual production, but abnormal coated lay structure can be found out in every case of poor adhesion. When the ratio of air to fuel gas is unsuitably low in NOF section, carbon enrichment on strip surface will occurs which makes poor coated layer adhesion. When the ratio is unsuitably high, thick oxidation film on strip surface makes it difficult to be deoxidized by reduction section. Poor deoxidized surface results in bad adhesion. In this case, many ZnO particles exist in the coated layer near steel substrate. Delaminated Zn layer causes bad adhesion with ZnO phase found in the delaminated place.
|
Received: 24 September 2009
|
|
|
|
[1] |
YU Hui-xiang, PAN Ming, YANG De-xin. Behavior of inclusions in ultra-low carbon IF steel during deoxidation and alloying process[J]. Iron and Steel, 2020, 55(6): 46-53. |
[2] |
QIN Da-wei, LIU Hong-min, ZHANG Dong, WANG Jun-sheng. Prediction models of coating mass per unit area for hot-dip galvanized strip based on artificial neural network[J]. Iron and Steel, 2020, 55(5): 68-72. |
[3] |
JIANG Da-jun. Influence of fuel structure on sintering character and comprehensive effect[J]. Iron and Steel, 2020, 55(2): 31-41. |
[4] |
LI Bai-song, CHEN Wen-zhi, YAO Shu-fang, ZHAO Yu-lin. Source and formation mechanism of inclusions in FeSiB amorphous ribbon[J]. Iron and Steel, 2020, 55(1): 27-33. |
[5] |
ZHANG Shu-hui,ZHOU Xiao-jia,LAN Chen-chen,QIE Ya-na,LV Qing. Future prospect and effects of harmful elements on coke gasification reaction[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(9): 771-778. |
[6] |
YANG Geng-wei,LU Jia-wei,SUN Hui,FANG Zi-wei,ZHOU Yi-liao,YAO Nan. Microstructure, mechanical properties and phase transformation behavior of TiV microalloyed highstrength hotstrip steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2019, 31(8): 726-732. |
|
|
|
|