Study of Microstructure and StretchFlangeFormability of Low Carbon FB Steel With Niobium |
SHANG Yan1,DING Hua1,2,WANG Weiwei1,3,ZHANG Jiansu4,DU Linxiu2 |
1. School of Material and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China; 2. The State Key Lab of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China; 3. Metallurgical Technology Institute of China Iron and Steel Research Institute Group, Beijing 100081, China; 4. Technology Center, Baosteel Group Co., Ltd., Shanghai 201900, China)Abstract: TMCP(ThermoMechanical Controlled Process |
|
|
Abstract TMCP(ThermoMechanical Controlled Process) tests were carried out, and the microstructure and stretchflangeformability of low carbon FB steels microalloyed with niobium were analyzed. The results show the strength of the tested steels was increased and hole expanding ratio was decreased with the decrease of final rolling temperature or coiling temperature. With the increase of Nb, the combination of tensile strength and stretchflangeformability was improved. When the final rolling temperature was 860 ℃, the intermediate temperature was 710 ℃ during cooling and the coiling temperature was 450 ℃, a good combination of strength and formability of tested steel with 0.02% Nb was obtained of which the ferrite grains size was 6.3 μm, tensile strength was about 570 MPa and hole expanding ratio was around 91%.
|
Received: 01 January 1900
|
|
|
|
[1] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
[2] |
TIAN Yan1,2,ZHAO Ming-chun2. Segregation of Nb and its formation mechanism of high strength casing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 335-343. |
[3] |
TIAN Yan1,2,ZHAO Ming-chun2. Segregation of Nb and its formation mechanism of high strength casing steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 344-350. |
[4] |
FENG Lu-lu1,2,3,WU Kai-ming1,LI Ping-ping2,CHEN Shu-min2,LU Xiu-yu4,QIAO Wen-wei3. Effect of Nb on microstructure transformation in reheating process of 2000MPa bridge cable steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(1): 60-65. |
[5] |
WANG Bingxing,ZHU Fuxian,WANG Chao,LOU Haonan,. Application of oxide metallurgy in high heat input welding steels[J]. Iron and Steel, 2019, 54(9): 12-21. |
[6] |
WANG Chengyong, MEN Dongpo, CHEN Peng, LI Ziwen. Nonlinear prediction model for caking index based on coal petrology[J]. Iron and Steel, 2019, 54(9): 22-26. |
|
|
|
|