Study on FluorineBearing Iron Concentrate Pellets Added With Dolomite |
XU Bin,XIONG Lin,YANG Yongbin,JIANG Tao,LI Qian,WANG Jiechao |
College of Resources Processing and Bioengineering, Central South University, Changsha 410083, Hunan, China |
|
|
Abstract The effect of MgO on the properties of fluorinebearing iron concentrate pellets was investigated. The results showed that the properties of greenball did not change evidently with the increasing of the content of MgO. When the content of MgO was increased from 0.83% to 2.0%, the compression strength of roasted pellets was increased evidently from 3555 to 5050 N per pellet. However, CO2 from dolomite decomposition increased porosity of pellets, reducing the compression strength of preheated pellets. The compression strength of roasted pellets and preheated pellets were improved by prolonging the preheating time. Most of the MgO existed in iron phase which made magnetic iron ore and magnesia crystal lattice stable at high roasting temperature, these minerals were interconnected, tightened by cementation and mutual eroded with calcium ferrite and Fe2O3, all of them could improve the compression strength of roasted pellets.
|
Received: 01 January 1900
|
|
|
|
[1] |
CHEN Shao-guo,WU Sheng-li,ZHANG Guo-liang,ZHU Juan,FAN Jia-xin, SU Bo. Blending Structure of Iron Ore for Dolomite Substitute Serpentine in Sintering Process[J]. Iron and Steel, 2014, 49(5): 24-29. |
[2] |
LIU Qing-cai, ZHANG Yang-bin,LAN Yuan-pei,CHEN Qian-xiang,AO Wan-zhong,ZHANG Dong-sheng. Effect of Lightly Fired Dolomite on Metallurgical Properties of Sinter[J]. Iron and Steel, 2013, 48(3): 15-18. |
[3] |
FAN Jian-jun,YANG Li-yuan,CAI Mei-xia,ZHAO Guo-dong,XI Yu-ming,ZHANG Wen-ping. Effect of Damp Milling on Improvement of Preheating and Roasting Properties for Magnesia Pellets[J]. Iron and Steel, 2012, 47(11): 21-26. |
[4] |
LIU Cheng-wei1,OUYANG Dai-gang2,LIU Qing-cai1,WEI Min1,HU Gang3,LU Zhen3. Technological Test on Injection of Light-Burned Dolomite Powder During Material Mixing of Sintering Process[J]. Iron and Steel, 2011, 46(8): 12-16. |
[5] |
JIN Mingfang;LI Guangsen;CHU Mansheng;SHEN Fengman. Diffusion Between MgO and Hematite During Sintering[J]. Iron and Steel, 2008, 43(3): 10-0. |
[6] |
LI Qian;HUANG Zhucheng;JIANG Tao;YANG Yongbin;LI Guanghui. Effect of Dolomite and Serpentine on Sinter Quality and Microstructure[J]. Iron and Steel, 2006, 41(12): 10-0. |
|
|
|
|