Effect of Overaging Temperature in Continuous Annealing on Microstructure and Properties of HeatTreated DP Steel |
HAN Huiquan,HUO Gang,LIU Yanchun,WANG Guodong |
State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China |
|
|
Abstract With bright continuous annealing simulator, the microstructure and properties of 0.08C1.7Mn0.03Si steel treated with different overaging temperature and the phase transformation during continuous annealing process were studied. The results show that second phase was mostly of granular bainite and martensite in the specimen overaged at 450 ℃, mostly lath bainite and martensite in the specimen overaged at 350 ℃ and mostly martensite or MA island in the specimen overaged at 250 ℃; Tensile strength was increased and yield strength decreased, obviously, but n, and Erichsen value changed only a little with reduction of overaging temperature, thus, adjusting constituent ratio of second phase perhaps is an effective way for promoting plasticity of the steel due to the fact that elongation of the steel overaged at 350 ℃ was increased.
|
Received: 01 January 1900
|
|
|
|
[1] |
CAO Jing-hua1,PAN Hong-bo2,3,ZHANG Jing1,ZHANG Teng-fei2,LI Xu-dong2,LIU Wei-ming2,3. Continuous cooling transformation of NbTi microcarbon deep drawing dualphase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(4): 322-328. |
[2] |
CAI Zhen, LIANG Wen, WANG Shui-ze, LIU Yong-qian. Discussion about practice and process of ferrite rolling in Ti-IF steel[J]. PHYSICS EXAMINATION AND TESTING, 2020, 38(3): 7-. |
[3] |
SHI Jun-liang1,LI Shen-bao2,ZHENG Wei-wei2. Effect of bainite characteristics on room temperature mechanical properties of fine ferrite/bainite dual phase steel[J]. JOURNAL OF IRON AND STEEL RESEARCH , 2020, 32(2): 166-174. |
[4] |
. Development of SAE8620 gear steel hot rolled wire coil[J]. , 2019, 44(3): 0-0. |
[5] |
LI Song-fen. Fatigue crack growth behavior of DP780 dual phase steel subjected to single tensile overload[J]. Iron and Steel, 2019, 54(3): 82-86. |
[6] |
KANG Yong-lin, TIAN Peng, ZHU Guo-ming. Progress and trend on hot wide strip endless rolling technology[J]. Iron and Steel, 2019, 54(3): 1-8. |
|
|
|
|